An electron spectroscopic study of the adsorption of nitrogen on a Ni/TiO2 catalyst prepared in situ in the spectrometer: evidence for dissociative adsorption in the strong-metal-support-interaction (SMSI) state

Nitrogen is dissociatively adsorbed on an annealed Ni/TiO2 surface just as on a Ti–Ni alloy surface while it is molecularly adsorbed on a Ni/Al2O3 surface.

Amorphous Mesoporous Iron Aluminophosphate Catalyst for the Synthesis of 1,5-Benzodiazepines

A simple and versatile method for the synthesis of 1,5-benzodiazepines from o-phenylenediamine and ketones in the presence of solvents and under solvent-free conditions that used an amorphous mesoporous iron aluminophosphate as catalyst was developed. High yields with excellent selectivity were obtained with a wide variety of ketones under mild reaction conditions. The catalyst had the advantages of ease of preparation, ease of handling, simple recovery, reusability, non toxicity, and being inexpensive.

A simplified kinetic model for oxidative dehydrogenation of ethylbenzene over Pd-NaBr/Al2O3 catalyst

The oxidative dehydrogenation of ethylbenzene is gaining considerable importance in recent years as a promising alternative for styrene production. This vapour phase reaction has been studied over Pd-NaBr/Al2O3 catalyst in the temperature range 623-793 K in a fixed bed reactor. Kinetic analysis of this reaction has been done using a recursion procedure developed in this work from first principles. The advantage of this method is the absence of any restriction on the conversion level as it uses an integrated rate equation. The rate of styrene formation was found to follow a linear relationship with concentration of ethylbenzene and shows a Langmuir type dependence on the concentration of oxygen.

Ce0.98Pd0.02O2-delta: Recyclable, ligand free palladium(II) catalyst for Heck reaction

Palladium substituted in cerium dioxide in the form of a solid solution, Ce-0.98 Pd-0.02 O-1.98 is a new heterogeneous catalyst which exhibits high activity and 100% trans-selectivity for the Heck reactions of aryl bromides including heteroaryls with olefins. The catalytic reactions work without any ligand. Nano-crystalline Ce-0.98 Pd-0.02 O-1.98 is prepared by solution combustion method and Pd is in +2 state. The catalyst can be separated, recovered and reused without significant loss in activity.

Design and development of a self-supported polymer electrolyte fuel cell system with anodic dead-end operation

Design and operational details for a self-supported polymer electrolyte fuel cell (PEFC) system with anodic dead-end fuel supply and internally humidified cathodic oxidant flow are described. During the PEFC operation, nitrogen and water back diffuse across the Nafion membrane from the cathode to the anode and accumulate in the anode flow channels affecting stack performance. The accumulated inert species are flushed from the stack by purging the fuel cell stack with a timer-activated purge valve to address the aforesaid problem. To minimize the system complexity, stack is designed in such a way that all the inert species accumulate in only one cell called the purge cell. A pulsed purge sequence comprises opening the valve for purge duration followed by purge-valve closing for the hold period and repeating the sequence in cycles. Since self-humidification is inadequate to keep the membrane wet, the anodic dead-end-operated PEFC stack with composite membrane comprising perflourosulphonic acid (Nafion) and silica is employed for keeping the membrane humidified even while operating the stack with dry hydrogen and internally humidified air.

Methanation of CO2 over Ru?SiO2 catalyst

Using Ru - SiO2 catalyst, the kinetics of methanation of carbon dioxide has been studied. In the temperature range of 320-460-degrees-C a simple power law model is found to predict experimental results with a good agreement over the range of variables studied.

New uniform solid catalyst for the low-temperature oxidation of carbon monoxide: A triple-layered rare earth perovskite containing Co and Cu ions

Oxygen reactivity and catalytic activity of the cobalt-containing layered defect perovskites, YBa2Cu2CoO7+delta and LaBa2Cu2CoO7+delta, in comparison with LaBa2Cu3O7-delta have been investigated employing temperature-programmed desorption (TPD) and temperature-programmed surface reactions (TPSR) in the stoichiometric and catalytic mode using carbon monoxide as a probe molecule. TPD studies showed evidence for the presence of two distinct labile oxygen species, one at (0 0 1/2) sites and the other at (0 1/2 0) sites in LaBa2Cu2CoO7+delta against a single labile species at (0 1/2 0) in the case of two other oxides. The activation energies for the catalytic oxidation of carbon monoxide by oxygen over LaBa2Cu3O7-delta, YBa2Cu2CoO7+delta, and LaBa2Cu2CoO7+delta have been estimated to be 24.2, 15.9, and 13.6 kcal/mol, respectively. The reactivity and catalytic activity of the oxide systems have been interpreted in terms of the structural changes brought about by substituents, guided by a directing effect of the larger rare earth cation. TPSR profiles, structural analysis, and infrared spectroscopic investigations suggest that the oxygen present at (0 0 1/2) sites in the case of LaBa2Cu2CoO7+delta is accessible to catalytic oxidation of CO through a Mars-Van Krevelen pathway. Catalytic conversion of CO to CO2 over LaBa2Cu2CoO7+delta occurs at 200 degrees C. The enhanced reactivity is explained in terms of changes brought about in the coordination polyhedra around transition metals, enhanced basal plane oxygen diffusivity, and redox potentials of the different transition metal cations.

Enhancing the mesoporosity of pillared clay catalyst - a study of pillar aggregates and deactivation in alkylation reaction

A sample of montmorillonite was pillared with aluminium polyoxycations in presence of different amounts of tween-80, a nonionic surfactant, ranging from 0.01 to 0.20 mmol/meq of clay. The amount of aluminium sorbed was found to vary with the amount of surfactant added during pillaring. Vapour phase catalytic activity of the samples for alkylation of toluene with methanol in a fixed bed down flow reactor showed that the rate of deactivation, in general, increased with decrease in the pillar density. The samples treated with 0.06 to 0.08 mmol/meq of surfactant showed the lowest deactivation and also an enhancement in the mesopores which did not change on calcining to 540°C. Suppression of deactivation is attributed to the distribution of pillars by the surfactant in such a way as to decrease the coke formation.

Probing the structural changes in the phase transitions of a Bi2MoO6 catalyst: the nature of the intermediate-temperature phase

The nature of the phase transitions of Bi2MoO6 has been investigated by the combined use of X-ray diffraction and Xray absorption spectroscopy. The distorted MoO6 octahedra in the low-temperature form are shown to undergo further distortion in the intermediate-temperature form before transforming to MoO4 tetrahedra in the high-temperature phase. (C) 1995 Academic Press, Inc.

Graphitic Carbon as Durable Cathode-Catalyst Support for PEFCs

Long-term deterioration in the performance of PEFCs is attributed largely to reduction in active area of the platinum catalyst at cathode, usually caused by carbon-support corrosion. It is found that the use of graphitic carbon as cathode-catalyst support enhances its long-term stability in relation to non-graphitic carbon. This is because graphitic-carbon-supported- Pt (Pt/GrC) cathodes exhibit higher resistance to carbon corrosion in-relation to non-graphitic-carbon-supported- Pt (Pt/Non-GrC) cathodes in PEFCs during accelerated stress test (AST) as evidenced by chronoamperometry and carbon dioxide studies. The corresponding change in electrochemical surface area (ESA), cell performance and charge-transfer resistance are monitored through cyclic voltammetry (CV), cell polarisation and impedance measurements, respectively. The degradation in performance of PEFC with Pt/GrC cathode is found to be around 10% after 70 h of AST as against 77% for Pt/Non-GrC cathode. It is noteworthy that Pt/GrC cathodes can withstand even up to 100 h of AST with nominal effect on their performance. Xray diffraction (XRD), Raman spectroscopy, transmission electron microscopy and cross-sectional field-emission scanning electron microscopy (FE-SEM) studies before and after AST suggest lesser deformation in catalyst layer and catalyst particles for Pt/GrC cathodes in relation to Pt/Non-GrC cathodes, reflecting that graphitic carbon-support resists carbon corrosion and helps mitigating aggregation of Pt-particles.

Studies on Cu/CeO2: A new NO reduction catalyst

Fine particle and large surface area Cu/CeO2 catalysts of crystallite sizes in the range of 100-200 Angstrom synthesized by the solution combustion method have been investigated for NO reduction. Five percent Cu/CeO2 catalyst shows nearly 100% conversion of NO by NH3 below 300 degrees C, whereas pure ceria and Zr, Y, and Ca doped ceria show 85-95% NO conversion above 600 degrees C. Similarly NO reduction by CO has been observed over 5% Cu/CeO2 with nearly 100% conversion below 300 degrees C. Hydrocarbon (n-butane) oxidation by NO to CO2, N-2, and H2O has also been demonstrated over this catalyst below 350 degrees C making Cu/CeO2 a new NO reduction catalyst in the low temperature window of 150-350 degrees C. Kinetics of NO reduction over 5% Cu/CeO2 have also been investigated. The rate constants are in the range of 1.4 x 10(4) to 2.3 x 10(4) cm(3) g(-1) s(-1) between 170 and 300 degrees C. Cu/CeO2 catalysts are characterized by X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, and electron paramagnetic resonance spectroscopy where Cu2+ ions are shown to be dispersed on the CeO2 surface. (C) 1999 Academic Press.

Characterization and catalytic properties of combustion synthesized Au/CeO2 catalyst

Ceria-supported Au catalyst has been synthesized by the solution combustion method for the first time and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). Au is dispersed as Au as well as Au3+ states on CeO2 surface of 20-30 nm crystallites. On heating the as-prepared 1% Au/CeO2 in air, the concentration of Au3- ions on CeO2 increases at the expense of Au. Catalytic activities for CO and hydrocarbon oxidation and NO reduction over the as-prepared and the heat-treated 1% Au/CeO2 have been carried out using a temperature-programmed reaction technique in a packed bed tubular reactor. The results are compared with nano-sized Au metal particles dispersed on alpha-Al2O3 substrate prepared by the same method. All the reactions over heat-treated Au/CeO2 occur at lower temperature in comparison with the as-prepared Au/CeO2 and Au/Al2O3. The rate of NO + CO reaction over as-prepared and heat-treated 1% Au/CeO2 are 28.3 and 54.0 mumol g(-1) s(-1) at 250 and 300 degreesC respeceively. Activation energy (E,) values are 106 and 90 kJ mol(-1) for CO + O-2 reaction respectively over as-prepared and heat-treated 1% Au/CeO2 respectively.