卤化铅调整Tm^3＋／Yb^3＋共掺碲酸盐玻璃上转换发光研究

研究了卤化铅调整Tm^3+／Yb^3+共掺碲酸盐玻璃的热稳定性能、Raman光谱和上转换发光光谱，分析了Tm^3+／Yb^3+共掺氧卤碲酸盐玻璃的上转换发光机理．结果发现：混合卤化铅调整Tm^3+／Yb^3+共掺碲酸盐玻璃具有好的热稳定性能、低的声子能量、强的上转换蓝光．这表明混合卤化铅调整Tm^3+／Yb^3+共掺碲酸盐玻璃是一种上转换蓝光激光器的潜在基质材料．

频率上转换掺稀土氧氟纳米微晶玻璃的研究进展

本文综述了近年来用于上转换发光的掺稀土离子氧氟微晶玻璃的研究概况，系统阐述了氧氟微晶玻璃中的上转换发光特性及其机理，提出了值得进一步研究的工作并对掺稀土离子氧氟微晶玻璃未来的前景做出了展望。

CE3+对ER3+/Yb3+共掺TeO2-WO3-ZnO玻璃发光性能的影响

Ce3+ ions were introduced into the Er3+/Yb3+ -codoped TeO2-WO3-ZnO glasses, and the effect of Ce3+ on the emission properties at 1.5 mu m band and the upconversion luminescence of Er3+ in the glasses was investigated. With the increasing of Ce3+ concentration, the emission intensity of Er3+ at 1.5 mu m band increases firstly, and then decreases. The optimal doping concentration of Ce3+ is about 2.07 x 10(20)/cm(3). As for the Er3+ emission at 1.5-mu m band, the fluorescence lifetime decreases a little from 3.4ms to 3.0ms, while the full width at half maximum (FWHM) hardly changes with the increase of Cc 3+ concentration. Due to the effective cross relaxation between Ce3+ and Er3+ : Er3+ (I-4(11/2)) + Ce3+ (F-2(5/2)) -> Er3+ (I-4(13/2)) + Ce3+ (F-2(7/2)), the upconversion emission intensity of Er3+ is reduced greatly. But when Ce3+ -doping concentration is too high, the other cross relaxation between Ce3+ and Er3+ : Er3+ (4I(13/2)) + Ce3+ (F-2(5/2)) -> Er3+ (I-4(15/2)) + Ce3+ (F-2(7/2)) happens, which depopulates the I-4(13/2) level of Er3+ and results in the decrease of the emission intensity and fluorescence lifetime of Er3+ at 1.5 mu m band.

掺铒氟（卤）磷碲酸盐玻璃的上转换发光性能研究

研究了掺铒氟（卤）磷碲酸盐玻璃的吸收光谱和上转换荧光光谱，探讨了Er^2＋在氟（卤）磷碲酸盐玻璃中的上转换发光机理．在975nm激光二极管抽运下产生强烈的上转换红光及绿光。且红光的发光强度要远远大于绿光．以PbCl2取代PbF2后，红光的发光强度下降，而绿光却没有明显变化；以ZnCl2取代ZnF2达5mol％时，红光和绿光的发光强度均明显增大．

Spectroscopic properties and Judd-Ofelt theory analysis of Dy3+ doped oxyfluoride silicate glass

Dy3+ doped oxyfluoride silicate glass was prepared and its optical absorption, 1.3 mu m emission, and upconversion luminescence properties were studied. Furthermore, the Judd-Ofelt [Phys. Rev. 127, 750 (1962); J. Chem. Phys. 37, 511 (1962)] intensity parameters, oscillator strengths, spontaneous transition probability, fluorescence branching ratio and radiative lifetime were calculated by Judd-Ofelt theory, while stimulated emission cross section of H-6(9/2)+F-6(11/2)-> H-6(15/2) transition was calculated by McCumber theory [Phys. Rev. A. 134, 299 (1964)]. According to the obtained Judd-Ofelt intensity parameters Omega(2)=2.69x10(-20) cm(2), Omega(4)=1.64x10(-20) cm(2), and Omega(6)=1.64x10(-20) cm(2), the radiative lifetime was calculated to be 810 mu s for 1.3 mu m emission, whose full width at half maximum and sigma(e) were 115 nm and 2.21x10(-20)cm(2), respectively. In addition, near infrared to visible upconversion luminescence was observed and evaluated. The results suggest that Dy3+ doped oxyfluoride silicate glass can be used as potential host material for developing broadband optical amplifiers and laser applications.

Spectroscopic properties of Er3+/Yb3+ codoped fluorophosphate glasses

Er3+/Yb3+ cocloped fluorophosphate glasses were prepared and their thermal stabilities, Raman spectra, absorption spectra, and fluorescence spectra were measured. It is found that proper content of NaF or PbF2 is helpful for the increase of stability against crystallization. The variation of AI(PO3)3 or NaF content in the composition affects not the maximum phonon energy but the phonon density. The introduction of PbF2 decreases the phonon energy slightly. Intense green and red upconversion luminescence was observed for the fluorophosphate glass with low phosphate content. A glass matrix for upconversion luminescence requiring neither expensive raw material nor special atmospheric conditioned preparation is provided. Infrared luminescence around 1530 nm was researched. Fluorophosphate glasses with bandwidth properties and stimulated-emission cross sections better than tellurite, germanate and silicate glasses are obtained. Through the introduction of NaF, the bandwidth properties are decreased. Through the introduction of PbF2 the gain properties are increased. On the whole, it is difficult to obtain a material with the best gain properties and bandwidth properties simultaneously. There should be a compromise between them according to the demand. (C) 2006 Elsevier B.V. All rights reserved.

Structural investigation on TeO2-BiCl3 glassy system

Glass systems of composition xBiCl(3)-(1-x)TeO2 (x=0.2, 0.4, 0.5 and 0.6, respectively) have been investigated by means of DSC, infrared absorption spectroscopy and Raman spectroscopy in order to obtain information about the transformation of structure, thermal and optical properties in the formation of the glass network. The results confirm that the addition of BiCl3 network former increases the glass forming ability and the optical transmission range. And also from Raman results a structural evolution was observed where the number of structural units described as [TeO3] trigonal pyramids, [TeO3+1] polyhedra and ionic behavior bonds (NBO) increases at the expense of the [TeO4] trigonal bipyramids. Bi3+ ions exist in network structure as [BiO6] or [BiCl6] octahedral coordination. As upconversion luminescence glass host, this glassy system is desired for optical properties but the thermal stability will still be improved. (c) 2005 Elsevier B.V. All rights reserved.

Tm3+/Er3+/Yb3+-codoped oxyhalide tellurite glasses as materials for three-dimensional display

Blue, green and red emissions through frequency upconversion and energy transfer processes in Tm3+/Er3+/Yb3+-codoped oxyhalide tellurite glass under 980 nm excitation are investigated. The intense blue (476 nm), green (530 and 545 nm) and red (656 nm) emissions are simultaneously observed at room temperature. The blue (476 nm) emission was originated from the (1)G(4)->H-3(6) transition of Tm3+. The green (530 and 545 nm), and red (656 nm) upconversion luminescences were identified from the H-2(11/2)->I-4(15/2), S-4(3/2)->I-4(15/2), and F-4(9/2)->I-4(15/2) transitions of Er3+, respectively. The energy transfer processes and possible upconversion mechanisms are evaluated. (C) 2005 Elsevier B.V. All rights reserved.

Effect of chloride ions' introduction on structural, thermal stability, and spectroscopic properties in Yb3+Er3+-codoped germanate-bismuth-lead glasses

Yb3+Er3+-codoped chloride-modified germanate-bismuth-lead glasses have been synthesized by the conventional melting and quenching method. Structural and thermal stability properties have been obtained on the basis of the Raman spectra and differential thermal analysis, which indicate that the PbCl2 addition has an important influence on the phonon density of states, maximum phonon energy, and thermal stability of host glasses. The Judd-Ofelt intensity parameters and quantum efficiencies were calculated on the basis of the Judd-Ofelt theory and lifetime measurements. For the 1.53 mu m emission band, the full widths at the half-maximum increase and peak wavelengths are blueshifted with increasing PbCl2 content. Moreover, the effect of the PbCl2 addition on the phonon density of states, OH- content, and upconversion luminescence has been discussed and evaluated. Our results reveal that, with increasing PbCl2 content, the decrease of phonon density and OH- content contributes more to the enhanced upconversion emissions than that of maximum phonon energy. (c) 2005 Optical Society of America

Transparent colloid containing upconverting nanocrystals: An alternative medium for three-dimensional volumetric display

We report an alternative medium of transparent upconverting colloid containing lanthanide ion doped NaYF4 nanocrystals for three-dimensional (3D) volumetric display. The colloids exhibit tunable upconversion luminescence with a wide spectrum of colors by adjusting the doping concentrations of the nanocrystals and the compositions of the colloids. Our preliminary experimental result indicates that an upconverting colloid-based 3D volumetric display using a convergent, near infrared laser beam to induce a localized luminescent spot near the focus is technically feasible. Therefore arbitrary 3D objects can be created inside the upconverting colloid by use of computer controlled 3D scanning systems. (C) 2008 Optical Society of America

红外飞秒激光诱导Ce^3＋掺杂闪烁晶体的上转换发光研究

本文研究了红外飞秒激光照射下Ce^3＋ 掺杂的YAP和LSO两种闪烁晶体的上转换发光现象.实验发现在飞秒激光泵浦下,这两种晶体的荧光均来自于Ce^3＋离子的5d-4f跃迁.荧光强度与泵浦光功率之间的依赖关系揭示了Ce^3＋：YAP和Ce^3＋：LSO晶体的上转换过程皆由三光子吸收过程所主导.分析表明,Ce^3＋：YAP和Ce^3＋：LSO晶体中的三光子吸收是三光子同时吸收.

Fabrication, patterning, and optical properties of nanocrystalline YVO4 : A (A = Eu3+, Dy3+, Sm3+, Er3+) phosphor films via sol-gel soft lithography

Nanocrystalline YVO4:A (A = Eu3+, Dy3+, Sm3+, Er3+) phosphor films and their patterning were fabricated by a Pechini sol-gel process combined with soft lithography. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric and differential thermal analysis (TG-DTA), atomic force microscopy (AFM) and optical microscopy, UV/vis transmission and absorption spectra, photoluminescence (PL) spectra, and lifetimes were used to characterize the resulting films. The results of XRD indicated that the films began to crystallize at 400 degreesC and the crystallinity increased with the increase of annealing temperatures. Transparent nonpatterned phosphor films were uniform and crack-free, which mainly consisted of grains with an average size of 90 nm. Patterned gel and crystalline phosphor film bands with different widths (5-60 mum) were obtained. Significant shrinkage and a few defects were observed in the patterned films during the heat treatment process. The doped rare earth ions (A) showed their characteristic emission in crystalline YVO4 phosphor films because of an efficient energy transfer from vanadate groups to them. The Sm3+ and Er3+ ions also showed upconversion luminescence in a YVO4 film host. Both the lifetimes and PL intensity of the rare earth ions increased with increasing annealing temperature from 400 to 800 degreesC, and the optimum concentration for Eu3+ was determined to be 7 mol % and those for Dy3+, Sm3-, and Er3+ were 2 Mol % of Y3- in YVO4 films, respectively.

Sol-Gel Erbium-Doped Silica-Hafnia Planar and Channel Waveguides

Erbium activated SiO2 -HfO2 planar waveguides, doped with Er3+ concentrations ranging from 0.01 to 4 mol%, were prepared by sol-gel method. The films were deposited on v-SiO2 and silica-on-silicon substrates using dip-coating technique. The waveguides show high densification degree, effective intermingling of the two film components, and uniform surface morphology. The waveguide deposited on silica-on-silicon substrates shows one single propagation mode at 1.5μm, with a confinement coefficient of 0.81 and an attenuation coefficient of 0.8 dB/cm at 632.8nm. Emission in the C-telecommunication band was observed at room temperature for all the samples upon continuouswave excitation at 980 nm or 514.5 nm. The shape of the emission band corresponding to the 4I13/2 → 4I15/2 transition is found to be almost independent both on erbium content and excitation wavelength, with a FWHM between 44 and 48 nm. The 4I13/2 level decay curves presented a single-exponential profile, with a lifetime ranging between 1.1 - 6.6 ms, depending on the erbium concentration. Infrared to visible upconversion luminescence upon continuous-wave excitation at 980 nm was observed for all the samples. Channel waveguide in rib configuration was obtained by etching the active film in order to have a well confined mode at 1.5 μm.

Origin of the high upconversion green luminescence efficiency in -NaYF4:2% Er3+,20% Yb3+

Site-selective spectroscopy in hexagonal beta-NaYF4:Er3+,Yb3+ has revealed different environments for Er3+ ions (multisite formation). The low-temperature S-4(3/2) -> (I15/2Er3+)-I-4 green emission depends on the excitation wavelength associated with the F-4(7/2) Er3+ level. We have studied the effect of hydrostatic pressure on the green, red, and blue Er3+ emission upon NIR excitation at similar to 980 nm, in order to establish the role played by energy resonance conditions and the multiple Er3+ sites due to the disordered structure for the upconversion (UC) process (energy tuning). The variation of photoluminescence spectra and lifetimes as a function of pressure and temperature reveals that the origin of the high green UC efficiency of the beta-NaYF4:Er3+,Yb3+ compound is mainly due to the multisite distribution, and the low phonon energy of the host lattice.