Effect of different dental composite resins on the polymerization process

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Y-TZP ceramic processing from coprecipitated powders: A comparative study with three commercial dental ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Assessment of the effectiveness of light-emitting diode and diode laser hybrid light sources to intensify dental bleaching treatment

Objective. To evaluate the effectiveness of the color change of hybrid light-emitting diode (LED) and low-intensity infrared diode laser devices for activating dental bleaching and to verify the occurrence of a color regression with time. Material and methods. A total of 180 specimens obtained from human premolars were immersed in a coffee solution for 15 days for darkening and then divided into eight experimental groups (n = 20 in each) as follows: G1, bleaching without light; G2, bleaching with halogen light; G3, bleaching with a blue LED (1000 mW/470 nm) and a laser device (120 mW/795 nm) simultaneously; G4, bleaching with an LED emitting blue light (1000 mW/470 nm); G5, bleaching with a blue LED (800 mW/470 nm) and a laser device (500 mW/830 nm) simultaneously; G6, bleaching with a blue LED device (800 mW); G7, bleaching with a green LED (600 mW/530 nm) and a laser device (120 mW/795 nm) simultaneously; and G8, bleaching with a green LED (600 mW). Three measurements were performed (at baseline and 14 days and 12 months after bleaching) using a Vita Easyshade spectrophotometer. The data were submitted to two-way ANOVA and a Tukey test. Results. All groups showed significantly higher Delta E values than Group G1, with the exception of Group G8. Variations in the Delta E values at 14 days were significant when compared with those obtained at baseline and after 12 months. Conclusions. Light activation of the bleaching gel provided faster and more intense bleaching than use of the bleaching gel without light activation. Combinations of low-intensity diode lasers are ineffective as a bleaching gel activator. Color regression was observed after 12 months of storage.

A study of the microstructural characteristics of dental amalgams

Metallographic studies by scanning electron microscopy and energy dispersive spectroscopy carried out for two types of dental amalgam showing a porous multiphase material. Surface analysis shows that the structure of the Dispersalloy amalgam consists of gamma-Ag3Sn, gamma(1)-Ag2Hg3, eta'-Cu6Sn5, epsilon-Cu3Sn and eutectic Ag-Cu phases. while Velvalloy amalgam consists mainly of gamma, gamma(1) and gamma(2)-Sn7-8Hg phases. The latter phase presents an uniform distribution often associated with voids.

Histomorphological response of dogs' dental pulp capped with white mineral trioxide aggregate

Foi objetivo deste trabalho estudar a reação do tecido pulpar ao capeamento com agregado de trióxido mineral (MTA) branco. Para isto, foram utilizados 15 dentes de cães, onde após o preparo de cavidades na região cervical da face vestibular e exposição pulpar, estas foram capeadas com MTA branco. Os animais foram sacrificados após 60 dias do término dos procedimentos clínicos e os dentes processados em laboratório para obtenção de cortes histológicos. Foi observada formação de ponte de tecido duro em todas as polpas. em alguns casos, não havia dentina tubular mas somente uma estrutura de aspecto morfológico peculiar, selando a cavidade de exposição pulpar. Apenas dois casos apresentaram inflamação pulpar. Conclui-se que o MTA branco possui as características necessárias de um material para capeamento pulpar.

Characterization of ceramic powders used in the inCeram systems to fixed dental Prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Fibrin adhesive implant in wound healing repair of dental sockets with topical application of epsilon aminocaproic acid: Histological analysis

The aim of the study was to evaluate wound healing repair of dental sockets after topical application of 5% epsilon-aminocaproic acid (EACA) and the use of fibrin adhesive implant in rats under anticoagulant therapy with warfarin. Sixty Albinus wistar rats were used, divided into three groups of 20. In Group I, the animals were given 0.1 mL/100 mg of 0.9% saline solution per day, beginning 6 days before dental extraction and continuing throughout the experimental period. In Group II, the animals received 0.03 mL of sodium warfarin daily, beginning 6 days before the surgery and continuing until the day of sacrifice; after tooth extractions, the sockets were filled with fibrin adhesive material. In Group III the animals were treated as in Group II, and after extractions, the sockets were irrigated with 5 mL of 5% EACA and filled with the same fibrin adhesive material. All groups presented biological phases of wound healing repair, the differences being evident only in the chronology. The results obtained in Group III were very similar to those of Group I in the last period of wound repair, whereas Group II presented a late chronology compared to the other groups. © 2005 Wiley Periodicals, Inc.

A comparative study of the corrosion of high copper dental amalgams

Metallographic studies carried out for Tytin-Plus and Dispersalloy amalgams show a porous multiphase material, whose surface phases are: gamma-(Ag3Sn), gamma(1)-(Ag2Hg3), eta'-(Cu6Sn5) and epsilon-(Cu3Sn). Additionally, Dispersalloy is present in the Ag-Cu eutectic. The application of surface analysis by SEM reveal a heterogeneous distribution of the above mentioned phases. Microstructures consisting of colonies or clusters were not observed. The corrosion testing of these materials was done in 0.9% NaCl aerated solution at 25 degrees C using potentiodynamic polarization curves and ac impedance measurements. The corrosion process in these multiphase systems can be interpreted as the sum of more than one electrodissolution process and the posterior formation of corrosion films. on each electrode, the corrosion film is formed by different mechanisms. (C) 1998 Elsevier B.V. B.V. All rights reserved.

Effect of root canal filling material and level of surgical injury on periodontal healing in dogs

Some divergencies in the literature about periodontal healing after surgical injury stimulated the development of this experiment. The root canals of dogs' teeth were negotiated and filled by the lateral condensation technique with two kinds of sealers: Sealapex and zinc oxide-eugenol cement. In the second session, the bone tissue was exposed and one cavity was made at the apical third of the root and another at the border between the coronal and middle thirds, both penetrating into the root canal. Six months later the animals were sacrificed and the specimens prepared for histopathologic analysis. The results showed that the kind of filling material and the level of the periodontal wound exposing the root canal can influence the healing process (P<0.01).

Mineral trioxide aggregate as a root canal filling material in reimplanted teeth. Microscopic analysis in monkeys

This study analyzed mineral trioxide aggregate (MTA) as a root canal filling material for the immediate reimplantation of monkey teeth. Four adult capuchin monkeys Cebus apella were used, which had their maxillary and mandibular lateral incisors on both sides extracted and reimplanted after 15 min. During the extra-alveolar period, the teeth were kept in saline solution and after reimplantation retention was performed with a stainless steel wire and composite resin for 14 days. After 7 days, the reimplanted teeth were submitted to endodontic treatment with biomechanics up to file n. 30 and irrigation with a saturated solution of calcium hydroxide [Ca(OH)(2)], and then divided into two study groups: group I - root canal filled with a Ca(OH)(2) paste, and group II - root canal filled with MTA. Radiographic follow up was performed at 30, 60 and 90 days postoperatively, and after 180 days the animals were killed and specimens were processed for histomorphological analysis. The results revealed that most specimens of both groups presented organized periodontal ligament with no inflammation. The resorptions observed were surface resorptions and were repaired by cementum. Both MTA and Ca(OH)(2) were good root canal filling materials for immediately reimplanted teeth, providing good repair and also allowing biological sealing of some lateral canals. There was no significant difference between the study groups (alpha = 29.60%).

Preparation of new glass systems by the polymeric precursor method for dental applications

Glass ionomer cements (GICs) are largely employed in Dentistry for several applications, such as luting cements for the attachment of crowns, bridges, and orthodontic brackets as well as restorative materials. The development of new glass systems is very important in Dentistry to improve of the mechanical properties and chemical stability. The aim of this study is the preparation of two glass systems containing niobium in their compositions for use as GICs. Glass systems based on the composition SiO2,Al2O3-Nb2O5-CaO were prepared by chemical route at 700degreesC. The XRD and DTA results confirmed that the prepared materials are glasses. The structures of the obtained glasses were compared to commercial material using FTIR, Al-27 and Si-29 MAS-NMR. The analysis of FTIR and MAS-NMR spectra indicated that the systems developed and commercial material are formed by SiO4 and AlO4 linked tetrahedra. These structures are essential to get the set time control and to have cements. These results encourage further applications of the experimental glasses in the formation of GICs. (C) 2004 Elsevier B.V. All rights reserved.