The response of porous Al2O3 probed to nanoindentation

The response of porous Al2O3 to nanoindentation was investigated at microscopic scales (nm-mu m) and under ultra-low loads from 5 to 90 mN with special attention paid to the dependence of the load-depth behaviour to sample porosity. It was found that the load-depth curves manifest local responses typical of the various porous structures investigated. This is particularly clear for the residual deformation after load removal. Similarly, the limited mean pressure of the sample containing small grains and interconnected pores is consistent with its porous structure. By comparison, the samples with larger grain size and various porous structures exhibit higher pressures and smaller residual deformations that can be attributed to the mechanical response of the solid phase. (C) 2007 Elsevier B.V. All rights reserved.

Formation of dendritic nanostructures in Pyrex glass anodically bonded to silicon coated with an aluminum thin film

Anodic bonding with thin films of metal or alloy as an intermediate layer, finds increasing applications in micro/nanoelectromechanical systems. At the bonding temperature of 350 degrees C, voltage of 400 V, and 30 min duration, the anodic bonding is completed between Pyrex glass and crystalline silicon coated with an aluminum thin film with a thickness comprised between 50 and 230 nm. Sodium-depleted layers and dendritic nanostructures were observed in Pyrex 7740 glass adjacent to the bonding interface. The sodium depletion width does not increase remarkably with the thickness of aluminum film. The dendritic nanostructures result from aluminum diffusion into the Pyrex glass. This experimental research is expected to enhance the understanding of how the depletion layer and dendritic nanostructures affect the quality of anodic bonding. (C) 2007 Elsevier B.V. All rights reserved.

Development of a universal stress sensor for graphene and carbon fibres

Carbon fibres are a significant volume fraction of modern structural airframes. Embedded into polymer matrices, they provide significant strength and stiffness gains by unit weight compared with competing structural materials. Here we use the Raman G peak to assess the response of carbon fibres to the application of strain, with reference to the response of graphene itself. Our data highlight the predominance of the in-plane graphene properties in all graphitic structures examined. A universal master plot relating the G peak strain sensitivity to tensile modulus of all types of carbon fibres, as well as graphene, is presented. We derive a universal value of - average - phonon shift rate with axial stress of around -5ω0 -1 (cm -1 Mpa-1), where ω0 is the G peak position at zero stress for both graphene and carbon fibre with annular morphology. The use of this for stress measurements in a variety of applications is discussed. © 2011 Macmillan Publishers Limited. All rights reserved.

Wear resistance of reaction sintered alumina/mullite composites

Alumina and alumina/mullite composites with mullite content of 0.96-8.72 vol.% were subjected to an abrasive wear test under loads of 0.1-2.0 N with a ball-on-disc apparatus. The wear rate and area fraction of pullout f(po) on the worn surfaces were measured. The wear resistances of the alumina/mullite composites were better by a factor of 1-2 than that of pure alumina. The main wear mechanism of alumina is fracture wear, and for alumina/mullite composites, fracture wear and plastic wear mechanisms work together. The influence of mechanical properties on wear resistance was estimated by Evans' method. It was found that the wear rate depends on f(po), and the primary reason for the better wear resistance of alumina/mullite composites is the reduction off, induced by fracture mode transition. (c) 2007 Elsevier B.V. All rights reserved.

Mechanical alloying of Fe-Mn and Fe-Mn-Si

The ball milling of Fe-24Mn and Fe-24Mn-6Si mixed powders has been performed by the high energy ball milling technique. By employing X-ray diffraction and Mossbauer measurements, the composition evolution during the milling process has been investigated. The results indicate the formation of paramagnetic Fe-Mn or Fe-Mn-Si alloys with a metastable fee phase as final products, which imply that the Fe and Mn proceed a co-diffusion mechanism through the surface of fragmented powders. The thermal stability and composition evolution of the as-milled alloys were discussed comparing with the bulk alloy. (C) 1999 Published by Elsevier Science S.A. All rights reserved.

A modified criterion for shear band formation in bulk metallic glass under complex stress states

A new criterion for shear band formation in metallic glasses is proposed based on the shear plane criterion proposed by Packard and Schuh [1]. This modified shear plane (MSP) criterion suggests that a shear band is not initiated randomly throughout the entire material under stress but is initiated at the physical boundaries or defects and at locations where the highest normal stress modified maximum shear stress occurs. Moreover, the same as in the shear plan criterion, the shear stress all over the shear band should exceed the shear yield strength of the material. For a complete shear band to form, both requirements need to be fulfilled. The shear yield strength of the material is represented by the shear stress of the point at which the shear band stops. The new criterion agrees very well with experimental results in both the determination of the shear yield strength and the shear band path. (C) 2010 Elsevier B.V. All rights reserved.

Indentation of power law creep solids by self-similar indenters

For creep solids obeying the power law under tension proposed by Tabor, namely sigma = b(epsilon) over dot(m), it has been established through dimensional analysis that for self-similar indenters the load F versus indentation depth h can be expressed as F(t) = bh(2)(t)[(h) over dot(t)/h(t)](m)Pi(alpha) where the dimensionless factor Pi(alpha) depends on material parameters such as m and the indenter geometry. In this article, we show that by generalizing the Tabor power law to the general three dimensional case on the basis of isotropy, this factor can be calculated so that indentation test can be used to determine the material parameters b and m appearing in the original power law. Hence indentation test can replace tension test. This could be a distinct advantage for materials that come in the form of thin films, coatings or otherwise available only in small amounts. To facilitate application values of this constant are given in tabulated form for a range of material parameters. (C) 2010 Elsevier B.V. All rights reserved.

一种低活化铁素体/ 马氏体钢的高能重离子辐照效应研究

Low-activation Ferritic/Martensitic steels are a kind of important structural materials candidate to the application in advanced nuclear energy systems.Possible degradation of properties and even failure in the condition of high-temperature and high helium production due to energetic neutron irradiation in a fusion reactor is a major concern with the application of this kind of materials.In the present work microstructural evolution in a 9Cr Ferritic/Martensitic steel(T92B) irradiated with 122 MeV 20Ne ions...中文摘要：低活化的铁素体/马氏体钢是先进核能装置(如聚变堆)的重要候选结构材料。在聚变堆实际工作环境下,由于高温和高氦产生率引起的材料失效是这类材料面临的一个重要问题。本项研究以兰州重离子加速器(HIRFL)提供的中能惰性气体离子束(20Ne,122 MeV)作为模拟辐照条件,借助透射电子显微镜,研究了一种低活化的9Cr铁素体/马氏体钢(T92B)组织结构的变化和辐照肿胀。实验结果表明,高温下当材料中晶格原子的撞出损伤和惰性气体原子沉积浓度超过一定限值时,材料内部形成高浓度的空洞,并且空洞肿胀率显著依赖于辐照温度和剂量;在马氏体板条界面及其它晶界处空洞趋于优先形成,并且在晶界交汇处呈加速生长。基于氦泡的形核生长与空洞肿胀的经典模型探讨了在不同辐照条件(He离子、Ne离子、Fe/He离子双束、快中子、Ni离子)下铁素体/马氏体钢中肿胀率数据的关联。

Effects of cerium on the microstructure and mechanical properties of Mg–20Zn–8Al alloy

Mg-20Zn-8Al-xCe(x=0-2 wt.%) alloys were prepared by metal mould casting method, the effects of Ce on the microstructure and mechanical properties of the alloys were investigated. The results showed that the dendrite as well as gram size were refined by the addition of Ce, and the best refinement was obtained in 1.39% Ce containing alloy.