Effect of H2S on stress corrosion cracking and hydrogen permeation behaviour of X56 grade steel in atmospheric environment

Susceptibility to stress corrosion cracking of X56 steel and its relationship with hydrogen permeation behaviour in atmospheric environment containing H2S was investigated by hydrogen permeation tests at a slow strain rate. The results show that: the fracture strain decreases with the decrease of strain rate under the same experimental conditions; the fracture strain also decreases with the increase of H2S concentration under the same strain rate, and the increased concentration of H2S has no significant effect on the hydrogen permeation in the first wet, etc. dry cycle, however has lead to increased hydrogen permeation in the later cycles. The SEM images of the fractured surfaces show clear evidences of enhanced stress corrosion cracking susceptibility by H2S.

Hydrogen entry into steel during atmospheric corrosion process

Hydrogen entry and permeation into iron were measured by an electrochemical method during atmospheric corrosion reaction. The hydrogen permeation was enhanced on passive films because the hydrogen adsorption increased by the hydrogen evolution mechanism which is different from that on a bear iron surface. The permeation rate during a wet and dry corrosion cycle showed a maximum in the drying process depending upon the surface pH and the corrosion potential. The pollutant such as Na2SO3 which decreases the pH and the corrosion potential causes an increase in the permeation rate. The mechanism of the change in the permeation rate during the wet and dry cycles is explained by the polarization diagram of the electrode covered by thin water layer. (c) 2005 Elsevier Ltd. All rights reserved.

Corrosion failure of marine steel in sea-mud containing sulfate reducing bacteria

The corrosion failure behavior of marine steel is affected by stress, which exists in offshore structures at sea-mud region. The sulfate reducing bacteria (SRB) in the sea-mud made the steel more sensitive to stress corrosion cracking (SCC) and weaken the corrosion fatigue endurance. In this paper, a kind of natural sea-mud containing SRB was collected. Both SCC tests by slow strain rate technique and corrosion fatigue tests were performed on a kind of selected steel in sea-mud with and without SRB at corrosion and cathodic potentials. After this, the electrochemical response of static and cyclic stress of the specimen with and without cracks in sea-mud was analyzed in order to explain the failure mechanism. Hydrogen permeation tests were also performed in the sea-mud at corrosion and cathodic potentials. It is concluded that the effect of SRB on environment sensitive fracture maybe explained as the consequences of the acceleration of SRB on corrosion rate and hydrogen entry into the metal.

Effects of anaerobe in sea bottom sediment on the corrosion of carbon steel

The in-situ study of steel corrosion in sea bottom sediment (SBS) was carried out by Transplanting Burying Plate method (TBP method). It was found that the corrosion rate of steel in the sea bottom sediment with sulfate reducing bacteria (SRB) could be as high as ten times of that in sea bottom sediment without SRB. The experiments in simulated sea bottom sediments with different SRB contents by artificial culturing showed that the electrochemical behavior of steel in the sea bottom sediment with SRB was different from that without SRB. SRB altered the polarization behavior of steel significantly. The environment was acidified due to the activity of SRB and the corrosion of steel was accelerated. The corrosion of carbon steel in sea bottom sediment is anaerobic corrosion, and the main factor is anaerobe. There are SRB commonly in SBS, and the amount of SRB decreases along with the depth of sediment. Because of the asymmetry and variation of sea bottom sediment, the most dangerous corrosion breakage of steel in SBS is local corrosion caused by SRB. So the main countermeasure of corrosion protection of sea bottom steel facilities should be controlling of the corrosion caused by anaerobe.

The synergy between deformation and anodic dissolution of an austenitic stainless steel in acidic chloride solution

In corrosion medium, metals can deform under tensile stress and form a new active surface with the anodic dissolution of the metals being accelerated. At the same time, the anodic dissolution may accelerate the deformation of the metals. The synergy can lead to crack nucleation and development and shorten the service life of the component. Austenitic stainless steel in acidic chloride solution was in active dissolution condition when stress corrosion cracking (SCC) occurred. It is reasonable to assume that the anodic dissolution play an important role, so it's necessary to study the synergy between anodic dissolution and deformation of austenitic stainless steels. The synergy between deformation and anodic dissolution of AISI 321 austenitic stainless steel in an acidic chloride solution was studied in this paper. The corrosion rate of the steel increased remarkably due to the deformation-accelerated anodic and cathodic processes. The creep rate was increased while the yield strength was reduced by anodic dissolution. The analysis by thermal activation theory of deformation showed a linear relationship between the logarithm of creep rate and the logarithm of anodic cur-rent. Besides, the reciprocal of yield strength was also linearly dependent on the logarithm of anodic current. The theoretical deductions were in good agreement with experimental results.

Corrosion of mild steel in different granularity seabed sediment saturated with seawater

In order to investigate the corrosion of pipeline materials in Seabed Sediment (SBS) environment, weight-loss and electrochemical measurements in saturated sand and mud cells with seawater were performed for a simulation. The used electrochemical measurements included linear polarization resistance (LPR) and potentiodynamic scanning measurement. It was showed that the corrosion rate of mild steel in the present condition was lower than the corrosion rate of other marine environment corrosion zones of it; that the granularity of SBS could affect the corrosion behavior greatly; that with increasing grain size of SBS, the corrosion rate increased. Integrated over the results of the weight loss and polarization curves, the oxygen diffusion (oxygen as a depolarizant agent) mechanism was proposed and discussed.

Hydrogen permeation and corrosion behaviour of high strength steel 35CrMo under cyclic wet-dry conditions

Hydrogen permeation behaviours of high strength steel 35CrMo under different cyclic wet-dry conditions have been investigated by using Devanathan-Stachurski's technique. Four electrolytes were used: distilled water, seawater, seawater containing 1500 ppm H2S and seawater containing 0.03 mol L-1 SO2. The corrosion weight loss of 35CrMo in the wet-dry cycles was measured simultaneously. The experimental results show that hydrogen can be detected at the surface opposite to the corroding side of the specimen during wet-dry cycles and the permeation current density during a wet-dry cycle showed a maximum during the drying process. The hydrogen permeation was obviously promoted by Cl- ions, H2S and SO2. The hydrogen permeation in the real marine atmosphere has also been investigated. There is a clear correlation between the amount of hydrogen permeated and the corrosion weight losses. Results show the importance of hydrogen permeation that merits further investigation.

Investigation of AISI 1040 steel corrosion H(2)S solution containing chloride ions by digital image processing coupled with in electrochemical techniques

This paper presents a study of AISI 1040 steel corrosion in aqueous electrolyte of acetic acid buffer containing 3.1 and 31 x 10(-3) mol dm(-3) of Na(2)S in both the presence and absence of 3.5 wt.% NaCl. This investigation of steel corrosion was carried out using potential polarization, and open-circuit and in situ optical microscopy. The morphological analysis and classification of types of surface corrosion damage by digital image processing reveals grain boundary corrosion and shows a non-uniform sulfide film growth, which occurs preferentially over pearlitic grains through successive formation and dissolution of the film. (C) 2011 Elsevier Ltd. All rights reserved.

Comparative electrochemical study of 5832-9 stainless steel at different media of biological interest

The electrochemical behavior of ISO 5832-9 stainless steel at 37 degrees C in 0.9% NaCl, Ringer Lactate and minimum essential medium (MEM) has been studied, using linear voltammetry, and surface analysis by SEM and EDS. Mechanical and toxicity tests were made. ISO 5832-9 is passivated at corrosion potential (E) and it does not present pitting corrosion on the media studied from to 50 in V above the transpassivation potential (Ei). SEM and EDS analysis have shown that the sample previously immersed in MEM presents a diffirent behavior at 50 in V above El: the manganese oxide inclusions are absent in the surface. E. values and passivation current density values j(pass) changed according to the following. E(corr, RL) < E(corr,NaCl) < E(corr, MEM) and J (MEM) << j(RL) congruent to j(NaCl) The stainless steel was characterized as non toxic in the cytotoxicity assay

Study of electrochemical behavior of azoles for AISI 430 stainless steel in H(2)SO(4) 1 mol L(-1)

Corrosion is an undesirable process that occurs in metallic materials. Studied was the effect of inhibiting Benzotriazole (BTAH), Benzimidazole (BZM) and Indole in different concentrations-for the stainless steel (SS) AISI 430 in H(2)SO(4) mol The techniques employed this research were: anodic potenciostatic polarisation, electrochemical impedance spectroscopy, optical microscopy and scanning electron microscopy The curves of anodic polarisation showed that BTAH, BZM and Indol act as corrosion inhibitors for 430 SS, at concentrations of 1x10(-3) and 5x10(-4) mol L(-1) but do not inhibit corrosion for concentrations equal to or less than 1x10(-4) mol L(-1). The in-crease of the efficiency in relation to the inhibitory substances studied followed this order: Indol

The corrosion of austenitic 304 stainless steel in biodiesel

Fuel distribution uses 304 stainless steel containers for the storage of biofuels, however there are few reports in the literature about the corrosive aspects this. steel in biodiesel. The objective of this research is to study the corrosive behavior of 304 austenitic stainless steel in the presence of biodiesel, unwashed and washed, with aqueous solutions of citric, oxalic, acetic and ascorbic acids 0,01 mol L(-1), and compare with results obtained for the copper (ASTM D130). The employedtechniques were: atomic absorption spectrometry (AAS) and optical microscopy (OM). The results of EA A showed a low rate of corrosion for the stainless steel, the alloys elements studied were Cr, Ni and Fe, the highest rate was observed for the chrome, 1.78 ppm / day in biodiesel with or without washing. The OM of the 304 steel, when compared with that of copper has a low corrosion rate in the 304 steel/biodiesel system. Not with standing, this demonstrates that not only the 304 steel, but also the copper corrodes in biodiesel

Electrochemical behavior of the cistein and diphosfonate for stainless steel in media of HCl 1 mol L(-1)

Amino acids and self assembled monolayers (SAM`s) have been studied as to their inhibiting action on the corrosion of metallic materials. The objective of work is to study the electrochemical behavior of the cisteincisteine, the diphosfonate and the mixture of both in inhibiting the action of corrosion on stainless steel 304 in HCl 1 molL(-1). As the following techniques were used: open circuit potential (OCP), potenciostatic anodic polarization (A P), chronoamperomeny (CA), electrochemical impedance spectroscopy (EIS) and optical microscopy (OM). The results of CA showed that cisteine has a double effect, catalytic and inhibiting, in function of the immersion time of the metallic part in the electrolytic solution. AP curves have shown lesser current density for the system containing cisteine diphosfonate suggesting an inhibiting synergic action. These results have been confirmed by EIS and OM.

Effect of grain size on deformation twinning behaviour of high MN steel

The effect of grain size on the mechanical properties and deformation twinning behaviour in high manganese steel was investigated. In order to generate different grain sizes, the samples were subjected to hot rolling, cold rolling and annealing. Room temperature tensile testing of the steel with different grain sizes (5-50 µm) indicated the occurrence of twinning induced plasticity (TWIP) in all the samples. Also, changes in work-hardening behaviour accompanied changes in the grain size. The results are discussed in terms of the enhanced sensitivity of twinning to the grain size.

Deformation behaviour of ultrafine grained steel produced by cold rolling of martensite

An ultrafine grained Nb microalloyed steel was produced by cold rolling of martensite followed by annealing heat treatments at different times to study its effect on the microstructure and mechanical behaviour of the ultrafine grained steel. High strength was achieved by this thermomechanical processing due to the formation of cell and subgrain dislocation substructure; however annealing reduced both strength and elongation.

Microstructure and mechanical properties of nitrided and chromized short steel fiber reinforced aluminum based P/M composites

The present investigation is on the microstructure evolution and hardness of powder metallurgically processed Al- 0.5 wt.%Mg base 10 wt.% short steel fiber reinforced composites. The 0.38 wt.% C short steel fibers of average diameter 50µm and 500-800µm length were nitrided and chromized in a fluid bed furnace. Nitriding was carried out at 525°C for 90, 30 and 5 min durations. Chromizing was performed at 950°C for 53 and 7 min durations, using thermal reactive deposition (TRD) and diffusion technique. The treated fibers and resulting reaction interfaces were characterized using metallographic, microhardness and XRD techniques.