TENSILE PROPERTIES OF BLENDS OF POLY(ETHER SULFONE) WITH A POLY(ETHER IMIDE)

Blends of poly(ether sulphone) (PES) with a poly(ether imide) (PEI) in various proportions were prepared by the coprecipitation method. Mechanical properties and morphology of the blends were studied using tensile tests and scanning electron microscopy (SEM). The tensile moduli exhibit positive deviations from simple additivity. Marked positive deviations were also observed for ultimate strength. These results suggest that the PEI/PES blends are mechanically compatible. SEM study revealed that the blends are not homogeneous and the polymers are immiscible on the segmental level. However, the dispersions of the blends are rather fine. The interfaces between the two phases are excellently bonded; PEI and PES appear to interact well.

MISCIBILITY OF POLY(N-VINYL-2-PYRROLIDONE) WITH POLY(ETHER SULFONE) AND 2 PHENOLPHTHALEIN-BASED POLYMERS

Blends of poly(N-vinyl-2-pyrrolidone) (PVP) with poly(ether sulphone) and two phenolphthalein-based polymers, viz. phenolphthalein poly(ether ether sulphone) and phenolphthalein poly(ether ether ketone) were prepared by casting from a common solvent and studied by differential scanning calorimetry. It was found that all the PVP blends are miscible and show a single, composition-dependent glass transition temperature (T(g)). The T(g)-composition dependence has been analysed by the use of the Gordon-Taylor equation. The values of the k parameter in the Gordon-Taylor equation obtained are all not high for the three pairs, in accordance with the fact that there is no strongly specific interaction between PVP and any of the other polymers.

TENSILE PROPERTIES OF BLENDS OF PHENOLPHTHALEIN POLY(ETHER ETHER KETONE) WITH A POLY(ETHER IMIDE)

Blends of phenolphthalein poly(ether ether ketone) (PEK-C) with a poly(ether imide) (PEI) in various proportions were prepared by the coprecipitation method. Mechanical properties and morphology of the blends were studied using tensile tests and scanning electron microscopy (SEM). It was found that the tensile moduli exhibit positive deviations from simple additivity. Marked positive deviations were also observed for ultimate strength. These results suggest that the PEI/PEK-C blends are mechanically compatible. SEM study shows no evidence of phase separation, supporting the idea that the blends are compatible.

PHASE-SEPARATION IN ANHYDRIDE-CURED EPOXY-RESIN CONTAINING PHENOLPHTHALEIN POLY(ETHER ETHER KETONE)

Dynamic mechanical analysis and scanning electron microscopy were used to study phase separation of three blends of anhydride-cure bisphenol-A-type epoxy resin with phenolphthalein poly(ether ether ketone). Phase separation was observed for all the blends. The overall compatibility and the resulting morphology of the cured blends are dependent on the choice of cure agent. The phenomena have been discussed from the points of view of both thermodynamics and kinetics. The effects of the choice of hardener on phase separation are considered to be primarily due to differences between the chemical natures of the hardeners.

MISCIBILITY OF POLY(N-VINYL-2-PYRROLIDONE) WITH A COPOLYAMIDE

Blends of poly(N-vinyl-2-pyrrolidone) (PVP) with a copolyamide (CoPA) randomly composed of 1:1:1 (wt) nylon 6, nylon 66 and nylon 610 structural units were prepared by casting from a common solvent. They were found to be miscible and show a single, composition-dependent glass transition temperature (T(g)). The addition of PVP to CoPA significantly lowers the crystallinity owing to an increasing T(g) of the system. The observed miscibility is proposed to be the result of specific interactions between the proton acceptor groups of PVP and the amide groups of CoPA.

MISCIBILITY OF POLY(EPICHLOROHYDRIN) WITH POLY(VINYL ACETATE) AND POLY(STYRENE-CO-ACRYLONITRILE)

The phase behaviours of poly(vinyl acetate) (PVAc) and poly(styrene-co-acrylonitrile)s (SAN) with poly(epichlorohydrin) (PECH) were examined using differential scanning calorimetry and an optical method using a hot plate. The PECH/PVAc blends showed LCST behaviour. The observed miscibility is thought to be a result of hydrogen-bonding interactions between the alpha-hydrogen atoms of PECH and the carbonyl groups of PVAc. Two SAN copolymers with an acrylonitrile (AN) content of 18 wt% (SAN18) and 25 wt% (SAN25), respectively, were also found to exhibit miscibility with PECH. No phase separation occurred by heating up to about 280-degrees-C, and the individual blend has a single, composition-dependent glass transition temperature. The formation of miscible PECH/SAN blends can be considered as a result of the intramolecular repulsion between styrene and AN units in SAN.

THE MISCIBILITY AND MORPHOLOGY OF EPOXY-RESIN POLY(ETHYLENE OXIDE) BLENDS

Poly(ethylene oxide) (PEO) was found to be miscible with uncured epoxy resin, diglycidyl ether of bisphenol A (DGEBA), as shown by the existence of a single glass transition temperature (T(g)) in each blend. However, PEO with M(n) = 20 000 was judged to be immiscible with the highly amine-crosslinked epoxy resin (ER). The miscibility and morphology of the ER/PEO blends was remarkably affected by crosslinking. It was observed that phase separation in the ER/PEO blends occurred as the crosslinking progressed. This is considered to be due to the dramatic change in the chemical and physical nature of ER during the crosslinking.

BLENDS OF PHENOLPHTHALEIN POLY(ETHER ETHER KETONE) WITH PHENOXY AND EPOXY-RESIN

The properties of miscible phenolphthalein poly(ether ether ketone)/phenoxy (PEK-C/phenoxy) blends have been measured by dynamic mechanical analysis and tensile testing. The blends were found to have single glass transition temperatures (T(g)) that vary continuously with composition. The tensile moduli exhibit positive deviations from simple additivity. Marked positive deviations were also observed for tensile strength. The tensile strengths of the 90/10 and 75/25 PEK-C/phenoxy blends are higher than those of both the pure components. Embrittlement, or transition from the brittle to the ductile mode of failure, occurs in the composition range of 50-25 wt% PEK-C. These observations suggest that mixing on the segmental level has occurred and that there is enough interaction between the components to decrease its internal mobility significantly. PEK-C was also found to be miscible with the epoxy monomer, diglycidyl ether of bisphenol A (DGEBA), as shown by the existence of a single glass transition temperature (T(g)) within the whole composition range. Miscibility between PEK-C and DGEBA could be considered to be due mainly to entropy. However, PEK-C was judged to be immiscible with the diaminodiphenylmethane-curved epoxy resin (DDM-cured ER). It was observed that the PEK-C/ER blends have two T(g), which remain invariant with composition and are almost the same as those of the pure components, respectively. Scanning electron microscopy showed that the PEK-C/ER blends have a two-phase structure. The different miscibility with PEK-C between DGEBA and the DDM-cured ER is considered to be due to the dramatic change in the chemical and physical nature of ER after curing.

COMPATIBILIZING EFFECT OF POLY(ETHYLENE OXIDE)-B-POLYSTYRENE-B-POLY(ETHYLENE OXIDE) IN PHENOLPHTHALEIN POLY(ETHER ETHER KETONE) POLY(2,6-DIMETHYL-1,4-PHENYLENE OXIDE) BLENDS

The morphology and mechanical behaviour of phenolphthalein poly(ether ether ketone) (PEK-C)/poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) blends has been investigated. A poly(ethylene oxide)-b-polystyrene-b-poly(ethylene oxide) (PEO-PS-PEO) triblock copolymer was used as compatibilizer. It was found that PEO-PS-PEO has a compatibilizing effect on the PEK-C/PPO blends. The addition of PEO-PS-PEO to the blends greatly improves phase dispersion and interfacial interfacial adhesion and also enhances the ultimate tensile strength and Young's modulus at compositions ranging from 30 to 70% PEK-C. However, all the values of the ultimate tensile strength within the whole composition range are lower than those expected by simple additivity, probably owing to the poor mechanical properties of PEO-PS-PEO copolymer.