Transient and d.c. analysis of the operation mechanism of light-emitting electrochemical cells

Light-emitting electrochemical cells (LECs) made of electroluminescent polymers were studied by d.c. and transient current-voltage and luminance-voltage measurements to elucidate the operation mechanisms of this kind of device. The time and external voltage necessary to form electrical double layers (EDLs) at the electrode interfaces could be determined from the results. In the low-and intermediate-voltage ranges (below 1.1 V), the ionic transport and the electronic diffusion dominate the current, being the device operation better described by an electrodynamic model. For higher voltages, electrochemical doping occurs, giving rise to the formation of a p-i-n junction, according to an electrochemical doping model. Copyright (C) EPLA, 2012

Intense green-yellow electroluminescence from Tb+-implanted silicon-rich silicon nitride/oxide light emitting devices

High optical power density of 0.5 mW/cm2, external quantum efficiency of 0.1%, and population inversion of 7% are reported from Tb+-implanted silicon-rich silicon nitride/oxide light emitting devices. Electrical and electroluminescence mechanisms in these devices were investigated. The excitation cross section for the 543 nm Tb3+ emission was estimated under electrical pumping, resulting in a value of 8.2 × 10−14 cm2, which is one order of magnitude larger than one reported for Tb3+:SiO2 light emitting devices. These results demonstrate the potentiality of Tb+-implanted silicon nitride material for the development of integrated light sources compatible with Si technology.

Phenomenological model for the interpretation of impedance/admittance spectroscopy results in polymer light-emitting electrochemical cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Metalosupramoléculas discretas e Metal Organic Frameworks (MOFs) baseados em íons lantanídeos: design, síntese, caracterização e propriedades

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Polymer Light Emitting Diode Using PFT-Poly(9,9 `-n-dihexil-2,7-fluorenodiilvinylene-alt-2,5thiophene)

The development of new electroluminescence polymers for specific colour tuning in Polymer Light Emitting Devices (PLEDs) is currently one of the most important fields for organic electronics. This work reports a synthesis of a new electroluminescent polymer and the concomitant test as PLED emissive layer. The polymer, synthesised from fluorene, is poly(9,9`-n-dihexil-2,7-fluorenodiilvinylene-alt-2,5thiophene) or PFT The luminescence shows large bands with maxima around 480 nm in absorption and 560 nm in emission. The device was made in a three layer structure, with PEDOT:PSS as hole transport layer, PFT as emissive layer and butyl-PBD as electron transport layer. The electroluminescence spectrum shows a strong band peaked at 540 nm. For an applied voltage of 12 Volt, the brightness at normal angle of viewing is near 10 cd/m(2) and the luminous efficiency is of 0.01 lm/W. A discussion about carrier transport and the electroluminescence properties is made.

Electroluminescence and electric current response spectroscopy applied to the characterization of polymer light-emitting electrochemical cells

Frequency-dependent electroluminescence and electric current response spectroscopy were applied to polymeric light-emitting electrochemical cells in order to obtain information about the operation mechanism regimes of such devices. Three clearly distinct frequency regimes could be identified: a dielectric regime at high frequencies; an ionic transport regime, characterized by ionic drift and electronic diffusion; and an electrolytic regime, characterized by electronic injection from the electrodes and electrochemical doping of the conjugated polymer. From the analysis of the results, it was possible to evaluate parameters like the diffusion speed of electronic charge carriers in the active layer and the voltage drop necessary for operation. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4752438]

Conjugated semiconducting organic materials for electronic applications

Since conjugated polymers, i.e. polymers with spatially extended pi-bonding system have offered unique physical properties, unobtainable for conventional polymers, significant research efforts directed to better understanding of their chemistry, physics and engineering have been undertaken in the past two and half decades. In this thesis we discuss the synthesis, characterisation and investigation of conjugated semiconducting organic materials for electronic applications. Owing to the versatile properties of metal-organic hybrid materials, there is significant promise that these materials can find use in optical or electronic devices in the future. In addressing this issue, the synthesis of bisthiazol-2-yl-amine (BTA) based polymers is attempted and their metallation is investigated. The focus of this work has been to examine whether the introduction of coordinating metal ions onto the polymer backbone can enhance the conductivity of the material. These studies can provide a basis for understanding the photophysical properties of metal-organic polymers based on BTA. In their neutral (undoped) form conjugated polymers are semiconductors and can be used as active components of plastics electronics such as polymer light-emitting diodes, polymer lasers, photovoltaic cells, field-effect transistors, etc. Toward this goal, it is an objective of the study to synthesize and characterize new classes of luminescent polymeric materials based on anthracene and phenanthrene moieties. A series of materials based on polyphenylenes and poly(phenyleneethynylene)s with 9,10-anthrylene subunits are not only presented but the synthesis and characterization of step-ladder and ladder poly(p-phenylene-alt-anthrylene)s containing 9,10-anthrylene building groups within the main chain are also explored. In a separate work, a series of soluble poly-2,7- and 3,6-phenanthrylenes are synthesized. This can enable us to do a systematic investigation into the optical and electronic properties of PPP-like versus PPV-like. Besides, the self-organization of 3,6-linked macrocyclic triphenanthrylene has been investigated by 2D wide-angle X-ray scattering experiments performed on extruded filaments in solution and in the bulk. Additionally, from the concept that donor-acceptor materials can induce efficient electron transfer, the covalent incorporation of perylene tetracarboxydiimide (PDI) into one block of a poly(2,7-carbazole) (PCz)-based diblock copolymer and 2,5-pyrrole based on push-pull type material are achieved respectively.

Extended donor and acceptor molecules for organic electronics

Die Untersuchung von halbleitenden Materialien auf der Basis von organischen Molekülen stellt ein Gebiet der angewandten Forschung an der Schwelle zur industriellen Nutzung dar. Geringes Gewicht und hohe mechanische Flexibilität ermöglichen völlig neue Produkte, die mit anorganischen Halbleitern nicht zu realisieren sind. Die Herstellung von Bauteilen wie Transistoren, Solarzellen oder Leuchtdioden aus organischen Materialien ist ein komplexes Gebiet, das einer Vielzahl von unterschiedlichen Optimierungen bedarf, um eine konkurrenzfähige Leistung zu erreichen. Die synthetische organische Chemie bietet vielfältige Möglichkeiten, mit maßgeschneiderten Lösungen zum Optimierungsprozess beizutragen. Zum einen können neue aktive Materialien hergestellt werden mit besserer Leistung und leichterer Verarbeitbarkeit. Zum anderen sind Substanzen zugänglich, die z.B. bei der Ladungsträgerinjektion hilfreich sein können.rnIn dieser Arbeit wurde an beiden dieser Fronten gearbeitet. Dabei lag die Entwicklungsstrategie darin, ausgedehnte π-konjugierte Moleküle herzustellen, die entweder besonders elektronenarme Akzeptoren oder elektronenreiche Donoren darstellen. Die genaue Kontrolle der elektronischen Niveaus stellt einen wichtigen Bestandteil dar, um niedrige elektrische Kontaktbarrieren zu Metallen zu erreichen und ausreichend stabile Materialien zu erreichen.rnDer erste Fokus der Arbeiten lag in der Funktionalisierung von Coronen. Dieser PAH stellt einen guten Kompromiss bezüglich seiner Größe dar: Er ist groß genug, um Diffusion in andere Schichten von Bauteilen zu vermeiden, aber nicht zu groß, um Verarbeitung durch Vakuumsublimation zu ermöglichen. Bislang sind praktisch keine Coronen-Derivate in der Literatur beschrieben, weshalb eine neue Synthese entwickelt werden musste, die die Einführung starker Donor- und Akzeptorfunktionalitäten erlaubt. Die photochemische Cyclodehydrierung von substituierten [2.2.2]paracyclophan-trienen stellte sich als hervorragende Möglichkeit heraus, dies zu bewerkstelligen. Es wurde eine Reihe von methoxy-substitutierten Coronenen mit unterschiedlicher Symmetrie hergestellt. Mittels optischer Spektroskopie konnte gezeigt werden, dass Methoxygruppen wenig Einfluss auf die elektronischen Eigenschaften von Coronen haben. Unter Spaltung der Methylether und anschließender Oxidation allerdings sind Coronenketone zugänglich, welche bis zu drei α-Diketongruppen besitzen. Diese Moleküle sind enorm starke Akzeptoren, was durch Cyclovoltammetrie und Vergleich zu anderen Akzeptoren eindrucksvoll gezeigt werden konnte. Die Sublimation dieses Akzeptors auf die Oberfläche von Metallen zeigt einen dramatischen Einfluss auf die Austrittsarbeit dieses Metalls, was zur Herstellung eines ohmschen Kontakts zu organischen Halbleitern von außerordentlichem Nutzen ist. rnDen zweiten Teil der Arbeit bilden Benzodithiophen enthaltende Polymere, die für den Einsatz als aktive Komponente in elektronischen Bauteilen entwickelt wurden. Nach systematischer Strukturoptimierung wurde ein Polymer enthalten, welches in einem Feldeffekt-Transistor auf Standard-Silizium-Substraten Ladungsträger-Mobilitäten über 0,1 cm2/Vs erreicht mit großer Reproduzierbarkeit und ausgezeichneter Transistor-Charakteristik. Es konnte gezeigt werden, dass die durch die Monomergeometrie erzeugte Kurvung des Polymers zu einem optimalen Kompromiss aus Löslichkeit und effektiver Packung darstellt. Auf für industrielle Anwendungen besonders interessanten polymer-basierten Substraten wurde eine noch erheblich bessere Leistung gezeigt. Auf einem PET-Substrat wurden Feldeffekt-Mobilitäten von 0,5 cm2/Vs gemessen mit überzeugenden Reproduzierbarkeit und Stabilität.rnDamit konnte in der Arbeit ein bedeutender Beitrag zur Weiterentwicklung von Materialien für den Einsatz in elektronischen Bauteilen geleistet werden. Die Substanzen versprechen noch erhebliches Potenzial nach intensiver Optimierung und wurden deshalb zum Patent angemeldet.rn

Triphenylene-based polymers for organic electronics

An efficient synthesis has been developed toward a novel series of conjugated blue emitting polymers containing triphenylene as repeating unit for polymer light emitting diodes (PLEDs). Soluble triphenylene-based co- and homo-polymers have been synthesized by the palladium-catalyzed Suzuki-Miyaura and the nickel-catalysed Yamamoto polycondensation reactions, respectively. The photophysical properties as well as the application of the polymers in PLED devices are presented here.rnIn addition a simple GNR fabrication method that allows for the production of atomically precise GNRs of different topologies and widths is introduced. This bottom-up approach consists in the surface-assisted coupling of suitably designed molecular triphenylene precursors into linear polyphenylenes and their subsequent cyclodehydrogenation and results in GNRs whose topology, width and edge periphery are defined by the precursor monomers. Various types of atomically precise GNRs thus eventually become available for experimental investigation and exploitation of their many predicted and technologically highly interesting properties. Furthermore, it is anticipated that this bottom-up approach of GNR fabrication will allow the engineering of chemical and electronic properties and the yet elusive realization of theoretically predicted structures such as intraribbon quantum dots, superlattice structures, or magnetic devices based on specific GNR edge states.rn

Morphology Change of C60 Islands on Organic Crystals Observed by Atomic Force Microscopy

Organic-organic heterojunctions are nowadays highly regarded materials for light-emitting diodes, field-effect transistors, and photovoltaic cells with the prospect of designing low-cost, flexible, and efficient electronic devices.1-3 However, the key parameter of optimized heterojunctions relies on the choice of the molecular compounds as well as on the morphology of the organic-organic interface,4 which thus requires fundamental studies. In this work, we investigated the deposition of C60 molecules at room temperature on an organic layer compound, the salt bis(benzylammonium)bis(oxalato)cupurate(II), by means of noncontact atomic force microscopy. Three-dimensional molecular islands of C60 having either triangular or hexagonal shapes are formed on the substrate following a "Volmer-Weber" type of growth. We demonstrate the dynamical reshaping of those C60 nanostructures under the local action of the AFM tip at room temperature. The dissipated energy is about 75 meV and can be interpreted as the activation energy required for this migration process.

Modeling of optical detection of spin-polarized carrier injection into light-emitting devices

We investigate the emission of multimodal polarized light from light emitting devices due to spin-aligned carrier injection. The results are derived through operator Langevin equations, which include thermal and carrier-injection fluctuations, as well as nonradiative recombination and electronic g-factor temperature dependence. We study the dynamics of the optoelectronic processes and show how the temperature-dependent g factor and magnetic field affect the degree of polarization of the emitted light. In addition, at high temperatures, thermal fluctuation reduces the efficiency of the optoelectronic detection method for measuring the degree of spin polarization of carrier injection into nonmagnetic semicondutors.

Site controlled red-yellow-green light emitting InGaN quantum discs on nano-tipped GaN rods

We report a method of growing site controlled InGaN multiple quantum discs (QDs) at uniform wafer scale on coalescence free ultra-high density (>80%) nanorod templates by metal organic chemical vapour deposition (MOCVD). The dislocation and coalescence free nature of the GaN space filling nanorod arrays eliminates the well-known emission problems seen in InGaN based visible light sources that these types of crystallographic defects cause. Correlative scanning transmission electron microscopy (STEM), energy-dispersive X-ray (EDX) mapping and cathodoluminescence (CL) hyperspectral imaging illustrates the controlled site selection of the red, yellow and green (RYG) emission at these nano tips. This article reveals that the nanorod tips' broad emission in the RYG visible range is in fact achieved by manipulating the InGaN QD's confinement dimensions, rather than significantly increasing the In%. This article details the easily controlled method of manipulating the QDs dimensions producing high crystal quality InGaN without complicated growth conditions needed for strain relaxation and alloy compositional changes seen for bulk planar GaN templates.

Viability of fibroblasts cultured under nutritional stress irradiated with red laser, infrared laser, and red light-emitting diode

Phototherapy is noninvasive, painless and has no known side effect. However, for its incorporation into clinical practice, more well-designed studies are necessary to define optimal parameters for its application. The viability of fibroblasts cultured under nutritional stress irradiated with either a red laser, an infrared laser, or a red light-emitting diode (LED) was analyzed. Irradiation parameters were: red laser (660 nm, 40 mW, 1 W/cm(2)), infrared laser (780 nm, 40 mW, 1 W/cm(2)), and red LED (637 +/- 15 nm, 40 mW, 1 W/cm(2)). All applications were punctual and performed with a spot with 0.4 mm(2) of diameter for 4 or 8 s. The Kruskal-Wallis test and analysis of variance of the general linear model (p <= 0.05) were used for statistical analysis. After 72 h, phototherapy with low-intensity laser and LED showed no toxicity at the cellular level. It even stimulated methylthiazol tetrazolium assay (MTT) conversion and neutral red uptake of fibroblasts cultured under nutritional stress, especially in the group irradiated with infrared laser (p = 0.004 for MTT conversion and p < 0.001 for neutral red uptake). Considering the parameters and protocol of phototherapy used, it can be concluded that phototherapy stimulated the viability of fibroblasts cultured under nutritional deficit resembling those found in traumatized tissue in which cell viability is reduced. (C) 2011 Society of Photo-Optical Instrumentation Engineers (SPIE). [DOI: 10.1117/1.3602850]

Substrate/semiconductor interface effects on the emission efficiency of luminescent polymers

The importance of interface effects for organic devices has long been recognized, but getting detailed knowledge of the extent of such effects remains a major challenge because of the difficulty in distinguishing from bulk effects. This paper addresses the interface effects on the emission efficiency of poly(p-phenylene vinylene) (PPV), by producing layer-by-layer (LBL) films of PPV alternated with dodecylbenzenesulfonate. Films with thickness varying from similar to 15 to 225 nm had the structural defects controlled empirically by converting the films at two temperatures, 110 and 230 degrees C, while the optical properties were characterized by using optical absorption, photoluminescence (PL), and photoluminescence excitation spectra. Blueshifts in the absorption and PL spectra for LBL films with less than 25 bilayers (<40-50 nm) pointed to a larger number of PPV segments with low conjugation degree, regardless of the conversion temperature. For these thin films, the mean free-path for diffusion of photoexcited carriers decreased, and energy transfer may have been hampered owing to the low mobility of the excited carriers. The emission efficiency was then found to depend on the concentration of structural defects, i.e., on the conversion temperature. For thick films with more than 25 bilayers, on the other hand, the PL signal did not depend on the PPV conversion temperature. We also checked that the interface effects were not caused by waveguiding properties of the excited light. Overall, the electronic states at the interface were more localized, and this applied to film thickness of up to 40-50 nm. Because this is a typical film thickness in devices, the implication from the findings here is that interface phenomena should be a primary concern for the design of any organic device. (C) 2011 American Institute of Physics. [doi:10.1063/1.3622143]

Micro-hardness evaluation of a micro-hybrid composite resin light cured with halogen light, light-emitting diode and argon ion laser

This in vitro study aimed to determine whether the micro-hardness of a composite resin is modified by the light units or by the thickness of the increment. Composite resin disks were divided into 15 groups (n = 5), according to the factors under study: composite resin thickness (0 mm, 1 mm, 2 mm , 3 mm and 4 mm) and light units. The light activation was performed with halogen light (HL) (40 s, 500 mW/cm(2)), argon ion laser (AL) (30 s, 600 mW/cm(2)) or light-emitting diode (LED) (30 s, 400 mW/cm(2)). Vickers micro-hardness tests were performed after 1 week and were carried out on the top surface (0 mm-control) and at different depths of the samples. Analysis of variance (ANOVA) and Tukey tests (P a parts per thousand currency signaEuro parts per thousand 0.05) revealed no statistically significant difference among the light units for the groups of 0 mm and 1 mm thickness. At 2 mm depth, the AL was not statistically different from the HL, but the latter showed higher micro-hardness values than the LED. In groups with 3 mm and 4 mm thickness, the HL also showed higher micro-hardness values than the groups activated by the AL and the LED. Only the HL presented satisfactory polymerization with 3 mm of thickness. With a 4 mm increment no light unit was able to promote satisfactory polymerization.