Estudo da superfície do carbono vítreo reticulado após tratamento de implantação iônica por imersão em plasma (3IP) para a obtenção de eletrodos

In this work, RVC samples were treated by plasma immersion ion implantation (PIII) for electrodes production. High-voltage pulses with amplitudes of -3.0 kV or -10.0 kV were applied to the RVC samples while the treatment time was 10, 20 and 30 minutes. Nitrogen, atmospheric air and H2:N2 mixture were employed as plasma sources. The samples were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and electrochemical measurements. The SEM images present an apparent enhancement of the surface roughness after the treatment probably due to the surface sputtering during the PIII process. This observation is in agreement with the specific electrochemical surface area (SESA) of RVC electrodes. An increase was observed of the SESA values for the PIII treated samples compared to the untreated specimen. Some oxygen and nitrogen containing groups were introduced on the RVC surface after the PIII treatment. Both plasma-induced process: the surface roughening and the introduction of the polar species on the RVC surface are beneficial for the RVC electrodes application

Solution heat treatment of plasma nitrided 15-5PH stainless steel - Part I: Improvement of the corrosion resistance

The results of the investigation on Solution Heat Treatment of Plasma Nitrided (SHTPN) precipitation-hardened steel 15-5PH are presented. The layers have been obtained by the plasma nitriding process followed by solution heat treatment at different temperatures. The influence of the solution heat treatment after nitriding on the dissolution process of the nitrided layer has been considered. The nitrided layers were studied by scanning electron microscopy, X-ray microanalysis (EDX), and X-Ray diffraction. Micro-hardness tests of the nitrided layers and solubilized nitrided layers have been carried out and interpreted by considering the processing conditions. It was found that high nitrogen austenitic cases could be obtained after SHTPN of martensitic precipitation-hardened steel (15-5PH). When Solution Heat Treatment (SHT) was performed at 1100 °C, some precipitates were observed. The amount of precipitates significantly reduced when the temperature increased. The EDX microanalysis indicated that the precipitate may be chromium niobium nitride. When the precipitation on the austenite phase occurred in small amount, the corrosion resistance increased in SHTPN specimens and the pit nucleation potential also increased. The best corrosion result occurred for SHT at 1200 °C.

Influência de tratamentos a plasma na resistência à corrosão e na propriedade de adesão de uma camada protetiva sobre a superfície de ligas de alumínio

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Filmes finos depositados pela técnica de implantação iônica por imersão em plasma e deposição (IIIPD), utilizando o monômero HMDSN e os gases argônio, hélio e nitrogênio

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Nanosized precipitates in H13 tool steel low temperature plasma nitriding

A comprehensive study of pulsed nitriding in AISI H13 tool steel at low temperature (400 degrees C) is reported for several durations. X-ray diffraction results reveal that a nitrogen enriched compound (epsilon-Fe2-3N, iron nitride) builds up on the surface within the first process hour despite the low process temperature. Beneath the surface, X-ray Wavelength Dispersive Spectroscopy (WDS) in a Scanning Electron Microscope (SEM) indicates relatively higher nitrogen concentrations (up to 12 at.%) within the diffusion layer while microscopic nitrides are not formed and existing carbides are not dissolved. Moreover, in the diffusion layer, nitrogen is found to be dispersed in the matrix and forming nanosized precipitates. The small coherent precipitates are observed by High-Resolution Transmission Electron Microscopy (HR-TEM) while the presence of nitrogen is confirmed by electron energy loss spectroscopy (EELS). Hardness tests show that the material hardness increases linearly with the nitrogen concentration, reaching up to 14.5 GPa in the surface while the Young Modulus remains essentially unaffected. Indeed, the original steel microstructure is well preserved even in the nitrogen diffusion layer. Nitrogen profiles show a case depth of about similar to 43 mu m after nine hours of nitriding process. These results indicate that pulsed plasma nitriding is highly efficient even at such low temperatures and that at this process temperature it is possible to form thick and hard nitrided layers with satisfactory mechanical properties. This process can be particularly interesting to enhance the surface hardness of tool steels without exposing the workpiece to high temperatures and altering its bulk microstructure. (c) 2012 Elsevier B.V. All rights reserved.

Nitrogen excretion during embryonic development of the green iguana, Iguana iguana (Reptilia; Squamata)

Development within the cleidoic egg of birds and reptiles presents the embryo with the problem of accumulation of wastes from nitrogen metabolism. Ammonia derived from protein catabolism is converted into the less toxic product urea or relatively insoluble uric acid. The pattern of nitrogen excretion of the green iguana, Iguana iguana, was determined during embryonic development using samples from allantoic fluid and from the whole homogenized egg, and in hatchlings and adults using samples of blood plasma. Urea was the major excretory product over the course of embryonic development. It was found in higher concentrations in the allantoic sac, suggesting that there is a mechanism present on the allantoic membrane enabling the concentration of urea. The newly hatched iguana still produced urea while adults produced uric acid. The time course of this shift in the type of nitrogen waste was not determined but the change is likely to be related to the water relations associated with the terrestrial habit of the adult. The green iguana produces parchment-shelled eggs that double in mass during incubation due to water absorption: the eggs also accumulate 0.02 mM of urea, representing 82% of the total measured nitrogenous residues that accumulate inside the allantois. The increase in egg mass and urea concentration became significant after 55 days of incubation then were unchanged until hatching. (C) 2012 Elsevier Inc. All rights reserved.

Novel metallo-porphyrin based colourimetric amine sensors and their processing via plasma enhanced chemical vapour deposition at atmospheric pressure : synthesis, characterisation and mechanistic studies

Volatile amines are prominent indicators of food freshness, as they are produced during many microbiological food degradation processes. Monitoring and indicating the volatile amine concentration within the food package by intelligent packaging solutions might therefore be a simple yet powerful way to control food safety throughout the distribution chain.rnrnIn this context, this work aims to the formation of colourimetric amine sensing surfaces on different substrates, especially transparent PET packaging foil. The colour change of the deposited layers should ideally be discernible by the human eye to facilitate the determination by the end-user. rnrnDifferent tailored zinc(II) and chromium(III) metalloporphyrins have been used as chromophores for the colourimetric detection of volatile amines. A new concept to increase the porphyrins absorbance change upon exposure to amines is introduced. Moreover, the novel porphyrins’ processability during the deposition process is increased by their enhanced solubility in non-polar solvents.rnrnThe porphyrin chromophores have successfully been incorporated into polysiloxane matrices on different substrates via a dielectric barrier discharge enhanced chemical vapour deposition. This process allows the use of nitrogen as a cheap and abundant plasma gas, produces minor amounts of waste and by-products and can be easily introduced into (existing) roll-to-roll production lines. The formed hybrid sensing layers tightly incorporate the porphyrins and moreover form a porous structure to facilitate the amines diffusion to and interaction with the chromophores.rnrnThe work is completed with the thorough analysis of the porphyrins’ amine sensing performance in solution as well as in the hybrid coatings . To reveal the underlying interaction mechanisms, the experimental results are supported by DFT calculations. The deposited layers could be used for the detection of NEt3 concentrations below 10 ppm in the gas phase. Moreover, the coated foils have been tested in preliminary food storage experiments. rnrnThe mechanistic investigations on the interaction of amines with chromium(III) porphyrins revealed a novel pathway to the formation of chromium(IV) oxido porphyrins. This has been used for electrochemical epoxidation reactions with dioxygen as the formal terminal oxidant.rn

Analysis of plasma tocopherols alpha, gamma, and 5-nitro-gamma in rats with inflammation by HPLC coulometric detection

Reactive nitrogen oxide species (RNOS) have been implicated as effector molecules in inflammatory diseases. There is emerging evidence that gamma-tocopherol (gammaT), the major form of vitamin E in the North American diet, may play an important role in these diseases. GammaT scavenges RNOS such as peroxynitrite by forming a stable adduct, 5-nitro-gammaT (NGT). Here we describe a convenient HPLC method for the simultaneous determination of NGT, alphaT, and gammaT in blood plasma and other tissues. Coulometric detection of NGT separated on a deactivated reversed-phase column was linear over a wide range of concentrations and highly sensitive (approximately 10 fmol detection limit). NGT extracted from blood plasma of 15-week-old Fischer 344 rats was in the low nM range, representing approximately 4% of gammaT. Twenty-four h after intraperitoneal injection of zymosan, plasma NGT levels were 2-fold higher compared to fasted control animals when adjusted to gammaT or corrected for total neutral lipids, while alpha- and gammaT levels remained unchanged. These results demonstrate that nitration of gammaT is increased under inflammatory conditions and highlight the importance of RNOS reactions in the lipid phase. The present HPLC method should be helpful in clarifying the precise physiological role of gammaT.

AtPTR1, a plasma membrane peptide transporter expressed during seed germination and in vascular tissue of Arabidopsis

For the efficient translocation of organic nitrogen, small peptides of two to three amino acids are posited as an important alternative to amino acids. A new transporter mediating the uptake of di- and tripeptides was isolated from Arabidopsis thaliana by heterologous complementation of a peptide transport-deficient Saccharomyces cerevisiae mutant. AtPTR1 mediated growth of S. cerevisiae cells on different di- and tripeptides and caused sensitivity to the phytotoxin phaseolotoxin. The spectrum of substrates recognized by AtPTR1 was determined in Xenopus laevis oocytes injected with AtPTR1 cRNA under voltage clamp conditions. AtPTR1 not only recognized a broad spectrum of di- and tripeptides, but also substrates lacking a peptide bond. However, amino acids, omega-amino fatty acids or peptides with more than three amino acid residues did not interact with AtPTR1. At pH 5.5 AtPTR1 had an apparent lower affinity (K-0.5 = 416 mum) for Ala-Asp compared with Ala-Ala (K-0.5 = 54 mum) and Ala-Lys (K-0.5 = 112 mum). Transient expression of AtPTR1/GFP fusion proteins in tobacco protoplasts showed that AtPTR1 is localized at the plasma membrane. In addition, transgenic plants expressing the beta-glucuronidase (uidA) gene under control of the AtPTR1 promoter demonstrated expression in the vascular tissue throughout the plant, indicative of a role in long-distance transport of di- and tripeptides.

Nitrogen isotope, total organic carbon and element concentration data for piston core M77/2-024-5 from the Peruvian continental margin

Piston core M77/2-024-5 was retrieved during the M77/2 cruise of Research Vessel Meteor in December 2008. Total organic carbon concentrations were determined using a Carlo Erba Element Analyzer (NA1500). Prior to analysis carbon bound to carbonate minerals was removed by leaching the sediment with 1 M HCl. Bulk nitrogen isotope ratios were determined using a Carlo Erba Element Analyzer (NA1500) coupled to a DeltaPlusXL isotope ratio mass spectrometer. Major and trace metals were analyzed after microwave-assisted (CEM MARS-5) acid digestion (HCl, HNO3 and HF) by inductively coupled plasma optical emission spectrometry (aluminum, titanium and iron) (Teledyne Leeman Prodigy) and inductively coupled plasma mass spectrometry (molybdenum and uranium) (THERMO X-Series 2).

Benthic oxygen and nitrogen fluxes at different time series sites in the southern North Sea, 2012 to 2014

Benthic oxygen and nitrogen fluxes were quantified within the years 2012 to 2014 at different time series sites in the southern North Sea with the benthic lander NuSObs (Nutrient and Suspension Observatory). In situ incubations of sediments, in situ bromide tracer studies, sampling of macrofauna and pore water investigations revealed considerable seasonal and spatial variations of oxygen and nitrogen fluxes. Seasonal and spatial variations of oxygen fluxes were observed between two different time series sites, covering different sediment types and/or different benthic macrofaunal communities. On a sediment type with a high content of fine grained particles (<63 µm) oxygen fluxes of -15.5 to -25.1 mmol/m**2/d (June 2012), -2.0 to -8.2 mmol/m**2/d (March 2013), -16.8 to -21.5 mmol/m**2/d (November 2013) and -6.1 mmol/m**2/d (March 2014) were measured. At the same site a highly diverse community of small species of benthic macrofauna was observed. On a sediment type with a low content of fine grained particles (<63 µm) high oxygen fluxes (-33.2 mmol/m**2/d August 2012; -47.2 to -55.1 mmol/m**2/d November 2013; -16.6 mmol/m**2/d March 2014) were observed. On this sediment type a less diverse benthic macrofaunal community, which was dominated by the large bodied suspension feeder Ensis directus, was observed. Average annual rain rates of organic carbon and organic nitrogen to the seafloor of 7.44 mol C/m**2/y and 1.34 mol N/m**2/y were estimated. On average 79% of the organic bound carbon and 95% of the organic bound nitrogen reaching the seafloor are recycled at the sediment-water interface.

Comportamento em desgaste por erosão cavitação, erosão - corrosão e em ensaios de microesclerometria linear instrumentada de um aço inoxidável martensítico AISI 410 nitretado a plasma em baixa temperatura, utilizando a tecnologia de tela ativa.

Amostras de um aço inoxidável martensítico AISI 410 temperado e revenido foram nitretadas a plasma em baixa temperatura usando o tratamento de nitretação plasma DC e a nitretação a plasma com tela ativa. Ambos os tratamentos foram realizados a 400 °C, utilizando mistura gasosa de 75 % de nitrogênio e 25 % de hidrogênio durante 20 horas e 400 Pa de pressão. As amostras de aço AISI 410 temperado e revenido foram caracterizadas antes e depois dos tratamentos termoquímicos, usando as técnicas de microscopia óptica, microscopia eletrônica de varredura, medidas de microdureza, difração de raios X e medidas de teor de nitrogênio em função da distância à superfície por espectrometria WDSX de raios X. A resistência à erosão por cavitação do aço AISI 410 nitretado DC e com tela ativa foi avaliada segundo a norma ASTM G32 (1998). Os ensaios de erosão, de erosão - corrosão e de esclerometria linear instrumentada segundo norma ASTM C1624 (2005) somente foram realizados no aço AISI 410 nitretado com tela ativa. Ensaios de nanoindentação instrumentada forma utilizados para medir a dureza (H) e o módulo de elasticidade reduzido (E*) e calcular as relações H/E* e H3/E*2 e a recuperação elástica (We), utilizando o método proposto por Oliver e Pharr. Ambos os tratamentos produziram camadas nitretadas de espessura homogênea constituídas por martensita expandida supersaturada em nitrogênio e nitretos de ferro com durezas superiores a 1200 HV, porém, a nitretação DC produziu maior quantidade de nitretos de ferro do que o tratamento de tela ativa. Os resultados de erosão por cavitação do aço nitretado DC mostraram que a precipitação de nitretos de ferro é prejudicial para a resistência à cavitação já que reduziu drasticamente o período de incubação e aumentou a taxa de perda de massa nos estágios iniciais do ensaio; entretanto, depois da remoção desses nitretos de ferro, a camada nitretada formada somente por martensita expandida resistiu bem ao dano por cavitação. Já no caso do aço nitretado com tela ativa, a resistência à erosão por cavitação aumentou 27 vezes quando comparada com o aço AISI 410 sem nitretar, fato atribuído à pequena fração volumétrica e ao menor tamanho dos nitretos de ferro presente na camada nitretada, às maiores relações H/E* e H3/E*2 e à alta recuperação elástica da martensita expandida. A remoção de massa ocorreu, principalmente, pela formação de crateras e de destacamento de material da superfície dos grãos por fratura frágil sem evidente deformação plástica. As perdas de massa acumulada mostradas pelo aço nitretado foram menores do que aquelas do aço AISI 410 nos ensaios de erosão e de erosão corrosão. O aço nitretado apresentou uma diminuição nas taxas de desgaste em ambos os ensaios de aproximadamente 50 % quando comparadas com o aço AISI 410. O mecanismo de remoção de material foi predominantemente dúctil, mesmo com o grande aumento na dureza. Os resultados de esclerometria linear instrumentada mostraram que a formação de martensita expandida possibilitou uma diminuição considerável do coeficiente de atrito em relação ao observado no caso do aço AISI 410 sem nitretar. O valor de carga crítica de falha foi de 14 N. O mecanismo de falha operante no aço nitretado foi trincamento por tensão.

Carbon and nitrogen limitation increase chitosan antifungal activity in Neurospora crassa and fungal human pathogens

Chitosan permeabilizes plasma membrane and kills sensitive filamentous fungi and yeast. Membrane fluidity and cell energy determine chitosan sensitivity in fungi. A five-fold reduction of both glucose (main carbon (C) source) and nitrogen (N) increased 2-fold Neurospora crassa sensitivity to chitosan. We linked this increase with production of intracellular reactive oxygen species (ROS) and plasma membrane permeabilization. Releasing N. crassa from nutrient limitation reduced chitosan antifungal activity in spite of high ROS intracellular levels. With lactate instead of glucose, C and N limitation increased N. crassa sensitivity to chitosan further (4-fold) than what glucose did. Nutrient limitation also increased sensitivity of filamentous fungi and yeast human pathogens to chitosan. For Fusarium proliferatum, lowering 100-fold C and N content in the growth medium, increased 16-fold chitosan sensitivity. Similar results were found for Candida spp. (including fluconazole resistant strains) and Cryptococcus spp. Severe C and N limitation increased chitosan antifungal activity for all pathogens tested. Chitosan at 100 μg ml-1 was lethal for most fungal human pathogens tested but non-toxic to HEK293 and COS7 mammalian cell lines. Besides, chitosan increased 90% survival of Galleria mellonella larvae infected with C. albicans. These results are of paramount for developing chitosan as antifungal.