Effect of the association of nystatin with a tissue conditioner on its ultimate tensile strength

Purpose: This study evaluated the ultimate tensile strength of a tissue conditioner without nystatin incorporation (GI - control group) and the same tissue conditioner modified by the addition of nystatin in two concentrations: GII - 500,000 International Units (U) and GIII - 1,000,000 U, in which each milligram of the medicament corresponded to 6079 U. Materials and Methods: Dumbbell-shaped specimens (N = 7) with a central cross-sectional area of 33 × 6 × 3 mm were produced for the three experimental groups. After polymerization following manufacturer's instructions, specimens were immersed in distilled water at 37°C for either 24 hours or 7 days and then tested in tension in the MTS 810 at 40 mm/minute. Data were analyzed by two-way ANOVA followed by Tukey's test, at 95% level of confidence. Results: The means (force-grams (gf) ± standard deviation) of the ultimate tensile strength were: GI - 634.29 ± 122.80; GII - 561.92 ± 133.56; and GIII - 547.30 ± 73.47 for 24-hour storage, and GI - 536.68 ± 54.71; GII - 467.50 ± 143.51; and GIII - 500.62 ± 159.76 for 7-day storage. There were no statistically significant differences among the three experimental groups (p > 0.05). The ultimate tensile strength means of all experimental groups after 7 days were significantly lower than those observed after 24 hours (p = 0.04). Conclusions: The results of this study suggest that the addition of nystatin into the tissue conditioner investigated in concentrations below 1,000,000 U did not affect its ultimate tensile strength. Copyright © 2006 by The American College of Prosthodontists.

Does the thickness of the resin cement affect the bond strength of a fiber post to the root dentin?

This study aimed to evaluate the influence of cement thickness on the bond strength of a fiber-reinforced composite (FRC) post system to the root dentin. Eighteen single-rooted human teeth were decoronated (length: 16 mm), the canals were prepared, and the specimens were randomly allocated to 2 groups (n = 9): group 1 (low cement thickness), in which size 3 FRC posts were cemented using adhesive plus resin cement; and group 2 (high cement thickness), in which size 1 FRC posts were cemented as in group 1. Specimens were sectioned, producing 5 samples (thickness: 1.5 mm). For cement thickness evaluation, photographs of the samples were taken using an optical microscope, and the images were analyzed. Each sample was tested in push-out, and data were statistically analyzed. Bond strengths of groups 1 and 2 did not show significant differences (P = .558), but the cement thicknesses for these groups were significantly different (P < .0001). The increase in cement thickness did not significantly affect the bond strength (r2 = 0.1389, P = .936). Increased cement thickness surrounding the FRC post did not impair the bond strength.

Polishing methods of an alumina-reinforced feldspar ceramic

The purpose of this study was to test the hypothesis that mechanical polishing methods of ceramic surfaces allow similar superficial roughness to that of glazed surfaces. Twenty-five Vitadur Alpha ceramic discs (5 mm x 2 mm) were prepared according to the manufacturer's specifications. All specimens were glazed and randomly assigned to 5 groups (n=5), according to finishing and polishing protocols: G1: glazed (control); G2: diamond bur finishing; G3: G2 + silicon rubber tip polishing; G4: G3 + felt disc/diamond polishing paste; G5: G3 + felt disc impregnated with fine-particle diamond paste. Next, surface roughness means (Ra - μm) were calculated. Qualitative analysis was made by scanning electron microscopy. Surface roughness data were submitted to ANOVA and Tukey's test at 5% significance level. G1 and G4 were statistically similar (p>0.05). G2 presented the highest roughness means (p<0.05) followed by groups G3, G5, G4 and G1 in a decreasing order. The hypothesis was partially confirmed as only the mechanical polishing (G4) produced similar superficial roughness to that of surface glazing, although finishing and polishing are technically critical procedures.

Bond strength of adhesive systems to human tooth enamel

The purpose of this study was to evaluate in vitro three adhesive systems: a total etching single-component system (G1 Prime & Bond 2.1), a self-etching primer (G2 Clearfil SE Bond), and a self-etching adhesive (G3 One Up Bond F), through shear bond strength to enamel of human teeth, evaluating the type of fracture through stereomicroscopy, following the ISO guidance on adhesive testing. Thirty sound premolars were bisected mesiodistally and the buccal and lingual surfaces were embedded in acrylic resin, polished up to 600-grit sandpapers, and randomly assigned to three experimental groups (n = 20). Composite resin cylinders were added to the tested surfaces. The specimens were kept in distilled water (37°C/24 h), thermocycled for 500 cycles (5°C-55°C) and submitted to shear testing at a crosshead speed of 0.5 mm/min. The type of fracture was analyzed under stereomicroscopy and the data were submitted to Anova, Tukey and Chi-squared (5%) statistical analyses. The mean adhesive strengths were G1: 18.13 ± 6.49 MPa, (55% of resin cohesive fractures); G2: 17.12 ± 5.80 MPa (90% of adhesive fractures); and G3: 10.47 ± 3.14 MPa (85% of adhesive fractures). In terms of bond strength, there were no significant differences between G1 and G2, and G3 was significantly different from the other groups. G1 presented a different type of fracture from that of G2 and G3. In conclusion, although the total etching and self-etching systems presented similar shear bond strength values, the types of fracture presented by them were different, which can have clinical implications.

Tensile bond strength of self-etching versus total-etching adhesive systems under different dentinal substrate conditions

The use of acid etchants to produce surface demineralization and collagen network exposure, allowing adhesive monomers interdiffusion and consequently the formation of a hybrid layer, has been considered the most efficient mechanism of dentin bonding. The aim of this study was to compare the tensile bond strength to dentin of three adhesive systems, two self-etching ones (Clearfil SE Bond - CSEB and One Up Bond F - OUBF) and one total-etching one (Single Bond - SB), under three dentinal substrate conditions (wet, dry and re-wet). Ninety human, freshly extracted third molars were sectioned at the occlusal surface to remove enamel and to form a flat dentin wall. The specimens were restored with composite resin (Filtek Z250) and submitted to tensile bond strength testing (TBS) in an MTS 810. The data were submitted to two-way ANOVA and Tukey's test (p = 0.05). Wet dentin presented the highest TBS values for SB and CSEB. Dry dentin and re-wet produced significantly lower TBS values when using SB. OUBF was not affected by the different conditions of the dentin substrate, producing similar TBS values regardless of the surface pretreatments.

Bond strength of acrylic teeth to denture base resin after various surface conditioning methods before and after thermocycling

This study aimed to evaluate the durability of adhesion between acrylic teeth and denture base acrylic resin. The base surfaces of 24 acrylic teeth were flatted and submitted to 4 surface treatment methods: SM1 (control): No SM; SM2: application of a methyl methacrylate-based bonding agent (Vitacol); SM3: air abrasion with 30-μm silicone oxide plus silane; SM4: SM3 plus SM2. A heat-polymerized acrylic resin was applied to the teeth. Thereafter, bar specimens were produced for the microtensile test at dry and thermocyled conditions (60 days water storage followed by 12,000 cycles). The results showed that bond strength was significantly affected by the SM (P < .0001) (SM4 = SM2 > SM3 > SM1) and storage regimens (P < .0001) (dry > thermocycled). The methyl methacrylate-based adhesive showed the highest bond strength.

Evaluation of the thermoplasticity of different gutta-percha cones and Resilon®

The goal of this study was to evaluate the thermoplasticity of conventional and thermoplastic gutta-percha and Resilon®, a polyester polymer-based material. Specimens with standardised dimensions were made from the following materials: conventional and thermoplastic gutta-percha (Dentsply), conventional and thermoplastic gutta-percha (Endopoints) and Resilon®. After 24 h, the specimens were placed in water at 70°C for 60 s, and thereafter positioned between two glass slabs. Each set was compressed by a 5-kg weight. Digital images of the specimens before and after compression were obtained and analysed. The thermoplasticity of each material was confirmed by the difference between final and initial areas of each sample. The data were analysed statistically by ANOVA and Tukey's test at a 5% significance level. Resilon® had the highest thermoplasticity means (P < 0.05). Among the gutta-percha cones, Endopoints TP (thermoplastic) presented the highest thermoplasticity means and differed significantly from the other commercial brands (P < 0.05). Resilon® had good thermoplasticity, endorsing its use as a thermoplastic root canal filling material. © 2007 The Authors. Journal compilation © 2007 Australian Society of Endodontology.

Shear bond strength fatigue limit of rest seats made with dental restoratives

Purpose: This study compared the shear bond strength (SBS) to enamel of rest seats made with a glass-ionomer cement (Fuji IX GP Fast), a resin-modified glass-ionomer cement (Fuji II LC), and a composite resin (Z100 MP) under monotonic and cyclic loading. Materials and Methods: Rest seats were built up onto the lingual surfaces of 80 intact human mandibular incisors. Specimens (n=10) were stored in distilled water at 37°C for 30 days and subjected to shear forces in a universal testing machine (0.5 mm/min) until fracture. The SBS values were calculated (MPa) using the bonding area (9.62 mm2) delimited by adhesive tags. A staircase approach was used to determine the SBS fatigue limit of each material. Specimens were submitted to either 10,000 cycles (5 Hz) or until specimen fracture. A minimum of 15 specimens was tested for each material. Scanning electron microscopy was used to examine the mode of failure. Data were statistically analyzed with one-way ANOVA and Tukey HSD tests (α = 0.05). Results: Z100 MP yielded higher (p < 0.05) SBS (12.25 MPa) than Fuji IX GP Fast (7.21 MPa). No differences were found between Fuji II LC (10.29 MPa) and the other two materials (p > 0.05). Fuji II LC (6.54 MPa) and Z100 MP (6.26 MPa) had a similar SBS limit. Fuji IX GP Fast promoted the lowest (p < 0.05) SBS fatigue limit (2.33 MPa). All samples showed cohesive failure patterns. Conclusion: Fatigue testing can provide a better means of estimating the performance of rest seats made with dental restoratives.

In vivo preservation of the hybrid layer by chlorhexidine

Host-derived proteases have been reported to degrade the collagen matrix of incompletely-resin-infiltrated dentin. This study tested the hypothesis that interfacial degradation of resin-dentin bonds may be prevented or delayed by the application of chlorhexidine (CHX), a matrix metalloproteinase inhibitor, to dentin after phosphoric acid-etching. Contralateral pairs of resin-bonded Class I restorations in non-carious third molars were kept under intra-oral function for 14 months. Preservation of resin-dentin bonds was assessed by microtensile bond strength tests and TEM examination. In vivo bond strength remained stable in the CHX-treated specimens, while bond strength decreased significantly in control teeth. Resin-infiltrated dentin in CHX-treated specimens exhibited normal structural integrity of the collagen network. Conversely, progressive disintegration of the fibrillar network was identified in control specimens. Auto-degradation of collagen matrices can occur in resin-infiltrated dentin, but may be prevented by the application of a synthetic protease inhibitor, such as chlorhexidine.

The effect of water immersion on the shear bond strength between chairside reline and denture base acrylic resins: Basic science research

Purpose: The effect of water immersion on the shear bond strength (SBS) between 1 heat-polymerizing acrylic resin (Lucitone 550-L) and 4 autopolymerizing reline resins (Kooliner-K, New Truliner-N, Tokuso Rebase Fast-T, Ufi Gel Hard-U) was investigated. Specimens relined with resin L were also evaluated. Materials and Methods: One hundred sixty cylinders (20 × 20 mm) of L denture base resin were processed, and the reline resins were packed on the prepared bonding surfaces using a split-mold (3.5 × 5.0 mm). Shear tests (0.5 mm/min) were performed on the specimens (n = 8) after polymerization (control), and after immersion in water at 37°C for 7, 90, and 180 days. All fractured surfaces were examined by scanning electron microscopy (SEM) to calculate the percentage of cohesive fracture (PCF). Shear data were analyzed with 2-way ANOVA and Tukey's test; Kruskall-Wallis test was used to analyze PCF data (α = 0.05). Results: After 90 days water immersion, an increase in the mean SBS was observed for U (11.13 to 16.53 MPa; p < 0.001) and T (9.08 to 13.24 MPa, p = 0.035), whereas resin L showed a decrease (21.74 MPa to 14.96 MPa; p < 0.001). The SBS of resins K (8.44 MPa) and N (7.98 MPa) remained unaffected. The mean PCF was lower than 32.6% for K, N, and T, and higher than 65.6% for U and L. Conclusions: Long-term water immersion did not adversely affect the bond of materials K, N, T, and U and decreased the values of resin L. Materials L and U failed cohesively, and K, N, and T failed adhesively. © 2007 by The American College of Prosthodontists.

In vitro evaluation of marginal leakage in bonded restorations, with mechanical or chemical-mechanical (Carisolv) removal of carious tissue

This study carried out an in vitro evaluation and comparison of the occurrence of marginal leakage in bonded restorations using mechanical or chemical-mechanical (Carisolv) removal of carious tissue. For that purpose, 40 extracted decayed human molars were divided into 4 groups: GI (burs + Prime & Bond NT + TPH), GII (Carisolv + Prime & Bond NT + TPH), GIII (burs + SBMP + Z100) and GIV (Carisolv + SBMP + Z100). After accomplishment of the restorations and thermal cycling, the teeth were exposed to dye, sectioned and qualitatively evaluated. The results demonstrated that the system of removal of carious tissue did not influence the results of microleakage at any of the cavity margins. At dentinal margins, use of the Prime & Bond NT + TPH restorative system allowed the occurrence of less microleakage than the SBMP + Z100 system.

Microtensile bond strength of a repair composite to leucite-reinforced feldspathic ceramic

The purpose of this study was to evaluate the microtensile bond strength of a repair composite resin to a leucite-reinforced feldspathic ceramic (Omega 900, VITA) submitted to two surface conditionings methods: 1) etching with hydrofluoric acid + silane application or 2) tribochemical silica coating. The null hypothesis is that both surface treatments can generate similar bond strengths. Ten ceramic blocks (6x6x6 mm) were fabricated and randomly assigned to 2 groups (n=5), according to the conditioning method: G1- 10% hydrofluoric acid application for 2 min plus rinsing and drying, followed by silane application for 30 s; G2- airborne particle abrasion with 30 μm silica oxide particles (CoJet-Sand) for 20 s using a chairside air-abrasion device (CoJet System), followed by silane application for 5 min. Single Bond adhesive system was applied to the surfaces and light cured (40 s). Z-250 composite resin was placed incrementally on the treated ceramic surface to build a 6x6x6 mm block. Bar specimens with an adhesive area of approximately 1 ± 0.1 mm2 were obtained from the composite-ceramic blocks (6 per block and 30 per group) for microtensile testing. No statistically significant difference was observed between G1 (10.19 ± 3.1 MPa) and G2 (10.17 ± 3.1 MPa) (p=0.982) (Student's t test; á = 0.05). The null hypothesis was, therefore, accepted. In conclusion, both surface conditioning methods provided similar microtensile bond strengths between the repair composite resin and the ceramic. Further studies using long-term aging procedures should be conducted.

Surface conditioning of a composite used for inlay/onlay restorations: Effect on μTBS to resin cement

Purpose: To assess the effect of the composite surface conditioning on the microtensile bond strength of a resin cement to a composite used for inlay/onlay restorations. Materials and Methods: Forty-two blocks (6 × 6 × 4 mm) of a microfilled composite (Vita VMLC) were produced and divided into 3 groups (N = 14) by composite surface conditioning methods: Gr1 - etching with 37% phosphoric acid, washing, drying, silanization; Gr2 - air abrasion with 50-l̀m Al2O3 particles, silanization; Gr3 - chairside tribochemical silica coating (CoJet System), silanization. Single-Bond (one-step adhesive) was applied on the conditioned surfaces and the two resin blocks treated with the same method were cemented using RelyX ARC (dual-curing resin cement). The specimens were stored for 7 days in water at 37°C and then sectioned to produce nontrimmed beam samples, which were submitted to microtensile bond strength testing (μTBS). For statistical analysis (one-way ANOVA and Tukey's test, · = 0.05), the means of the beam samples from each luted specimen were calculated (n = 7). Results: μTBS values (MPa) of Gr2 (62.0 ± 3.9a) and Gr3 (60.5 ± 7.9a) were statistically similar to each other and higher than Gr1 (38.2 ± 8.9b). The analysis of the fractured surfaces revealed that all failures occurred at the adhesive zone. Conclusion: Conditioning methods with 50-l̀m Al2O3 or tribochemical silica coating allowed bonding between resin and composite that was statistically similar and stronger than conditioning with acid etching.

Influence of brush type as a carrier of adhesive solutions and paper points as an adhesive-excess remover on the resin bond to root dentin

Purpose: To evaluate the influence of the brush type as a earner of priming adhesive solutions and the use of paper points as a remover of the excess of these solutions on the push-out bond strength of resin cement to bovine root dentin. The null hypotheses were that brush type and the use of paper points do not affect the bond strength. Materials and Methods: The canals of 80 single-root bovine roots (16 mm in length) were prepared at 12 mm using the preparation drill (FRC Postec Plus, Ivoclar). Half of each root was embedded in acrylic resin and the specimens were divided into 8 groups, considering the factors brush type (4 levels) and paper point (2 levels) (n = 10): Gr 1: small microbrush (Cavi-Tip, SDI); Gr 2: Microbrush (Dentsply); Gr 3: Endobrush (Bisco); Gr 4: conventional brush (Bisco); Gr 5: Cavi-Tip (SDI) + paper points; Gr 6: Microbrush (Dentsply) + paper points; Gr 7: Endobrush (Bisco) + paper points; Gr 8: conventional brush (Bisco) + paper points. The root dentin was treated with a multistep total-etch adhesive system (All Bond 2). The adhesive system was applied using each microbrush, with and without using paper points. One fiber post was molded with addition silicon and 80 posts were made of resin cement (Duolink), The resin posts were luted (Duolink resin cement), and the specimens were stored for 24 h in water at 37°C. Each specimen was cut into 4 disk-shaped samples (1.8 mm in thickness), which were submitted to the push-out test. Results: The brush type (p < 0.0001) (small microbrush > microbrush = endobrush = conventional brush) and the use of paper points (p = 0.0001) (with > without) influenced the bond strength significantly (two-way ANOVA). The null hypotheses were rejected. Conclusion: The smallest brush (Cavi-Tip) and the use of paper points significantly improved the resin bond to bovine root dentin.

Fatigue resistance of bovine teeth restored with resin-bonded fiber posts: Effect of post surface conditioning

This study evaluated the effect of post surface conditioning on the fatigue resistance of bovine teeth restored with resin-bonded fiber-reinforced composite (FRC). Root canals of 20 single-rooted bovine teeth (16 mm long) were prepared to 12 mm using a preparation drill of a double-tapered fiber post system. Using acrylic resin, each specimen was embedded (up to 3.0 mm from the cervical part of the specimen) in a PVC cylinder and allocated into one of two groups (n = 10) based on the post surface conditioning method: acid etching plus silanization or tribochemical silica coating (30 μm SiOx + silanization). The root canal dentin was etched (H2PO3 for 30 seconds), rinsed, and dried. A multi-step adhesive system was applied to the root dentin and the fiber posts were cemented with resin cement. The specimens were submitted to one million fatigue cycles. After fatigue testing, a score was given based on the number of fatigue cycles until fracture. All of the specimens were resistant to fatigue. No fracture of the root or the post and no loss of retention of the post were observed. The methodology and the results of this study indicate that tribochemical silica coating and acid etching performed equally well when dynamic mechanical loading was used.