Influence of heat treatment on spectroscopic properties of Er3+ in multicomponent ZrF4-ZnF2-AlF3-YF3-MF2 (M = Ca, Sr, Ba) based glass

Er3+ doped multicomponent fluoride based glass was prepared. These precursor fluoride glass samples were then heated using different schedules. Crystalline phase particles were successfully precipitated in the multicomponent fluoride glass samples after heat treatment. The influence of heat treatment on the spectroscopic properties of Er3+ in multicomponent fluoride based glass samples were discussed. Small changes of the Judd-Ofelt parameters Omega(i) (i = 2,4,6) were found in multicomponent fluoride glass samples before and after heat treatment compared to oxyfluoride telluride glass. Preparation conditions used to produce transparent multicomponent fluoride glass ceramics doped with rare-earth ions are discussed. (c) 2007 Elsevier B.V. All rights reserved.

Spectroscopic properties of neodymium doped high silica glass and aluminum codoping effects on the enhancement of fluorescence emission

Nd3+ -codoped and Al3+-Nd3+-codoped high silica glasses have been prepared by sintering nanoporous glasses impregnated with Nd3+ stop and Al3+ ions. The Judd-Ofelt intensity parameters Omega(2,4,6) of Nd3+-doped high silica glasses were obtained and used to analyze aluminum codoping effects. Fluorescence properties of Nd3+-doped high silica glasses strongly depend on the Al3+ concentration. While Nd3+ ion absorption and emission intensities of obviously increase when aluminum is added to Nd3+-doped high silica glasses, fluorescence lifetimes decrease and aluminum codoping has almost no influence on the radiative quantum efficiencies. This indicates that aluminum codoping is responsible for an anti-quenching effect through a local modification of rare-earth environments rather than through physical cluster dispersion.

980 nm 抽运下Yb-Tm-Ho 三掺氟磷酸盐玻璃的2 μm 荧光性质

The thermal stability, 2 μm fluorescence properties and energy transfer mechanism in Ho³⁺ doped fluorophosphate glass sensitized by Yb³⁺ and Tm³⁺ were investigated. The characteristic temperatures, absorption spectrum and fluorescence spectrum of the glass sample were measured. ΔT calculated from the characteristic temperatures shows that the thermal stability of fluorophosphate glass is better than fluoride glass. According to the absorption spectrum, several spectroscopic parameters of the glass sample, such as Judd-Ofelt parameters and spontaneous transition probability were calculated and compared with other glass hosts. The largest spontaneous transition probability for Ho³⁺:⁵ I7&rarr⁵I8 transition in fluorophosphate glass which is 78.48 s^-1 indicates that fluorophosphate glass is an appropriate base glass to achieve 2 m fluorescence. From the fluorescence spectrum of the glass sample, the extremely strong 2.0 μm fluorescence intensity is observed, which is higher than the intensity of 1.8 μm fluorescence, showing that Ho³⁺ ions sensitized by Yb³⁺ and Tm³⁺ is efficient. Meanwhile, the absorption sections and emission sections of Yb³⁺, Tm³⁺ and Ho³⁺ were calculated and the pumping scheme and energy transfer mechanism among Yb³⁺, Tm³⁺ and Ho³⁺ are discussed. The study indicates that Yb-Tm-Ho tri-doped fluorophosphate glass is a significant sensitization glass system under 980 nm excitation for 2 μm applications.

Optical transitions and upconversion luminescence of Er3+/Yb3+-codoped halide modified tellurite glasses

Er3+-doped halide modified tellurite glasses were synthesized by conventional melting and quenching method. The Judd-Ofelt analysis was performed on the absorption spectra and the transition probabilities, excited state lifetimes, and the branching ratios were calculated and discussed. The intense infrared and visible fluorescence spectra under 980 nm excitation were obtained. Strong upconversion signal was observed at pumping power as low as 30 mW in the glasses with halide ions. The upconversion mechanisms and power dependent intensities were discussed, which showed two-photon process are involved for the green and red emissions. The decay times of the emitting states and the corresponding quantum efficiency were determined and explained. (C) 2004 American Institute of Physics.

Characterization of Er3+-doped Na2O-WO3-TeO2 glass for ion-exchanged waveguide amplifiers and lasers

Er^(3+)-doped Na2O-WO3-TeO2 glass consistent with standard ion-exchange technology has been fabricated and characterized. The measured absorption and emission spectra of the glass were analyzed by the Judd-Ofelt and McCumber theories. The intensity parameters are Ω2 = 7.01

UV-blue upconverted emission from Nd3+-doped InF3-based heavy-metal fluoride glasses for blue upconversion fibre laser

We report spectral properties and thermal stability of Nd3+-doped InF3-based heavy-metal fluoride glasses. Fluoroindate glasses in the chemical compositions (in mol%) of (38-x)InF3-16BaF(2)-20ZnF(2)-20SrF(2)-3GdF(3)-1GaF(3-)2NaF-xNdF(3) (x = 0.1, 0.5, 1, 2, 3) have been prepared under a controlled atmosphere in a dry box. Strong UVblue upconversion emission from a green excitation wavelength has been observed and the involved mechanisms have been explained. Near-infrared emission occurs simultaneously upon excitation of the UV-blue upconversion emissions with a cw Ar(+)laser. The upconversion spectra have revealed four dominant emissions at 354, 380, 412 and 449 nm, which belong to the transitions of D-4(3/2) -> I-4(9/2), D-4(3/2) -> I-4(11/2) and P-2(3/2) -> I-4(9/2), D-4(3/2) -> I-4(13/2) and P-2(3/2) -> I-4(11/2), D-4(3/2) -> I-4(15/2) and P-2(3/2) -> I-4(13/2), respectively.

Effect of Al(PO3)(3) content on physical, chemical and optical properties of fluorophosphate glasses for 2 mu m application

The effect of Al(PO3)(3) content on physical, chemical and optical properties of fluorophosphate glasses for 2 mu m application, such as thermal stability, chemical durability, surface hardness, absorption spectra and emission spectra, is investigated. With the increment of Al(PO3)(3) content, the thermal stability characterized by the gap of T-g and T,, increases first and then decreases, and reaches the maximum level containing 5 mol% Al(PO3)(3) content. The density and chemical durability decrease monotonously with the introduction of Al(PO3)(3) content increasing, while the refractive index and surface hardness increase. Above properties of fluorophosphate glasses are also compared with fluoride glasses and phosphate glasses. The Judd-Ofelt parameters, absorption and emission cross sections are discussed based on the absorption spectra of Tm-doped glasses. The emission spectra are also measured and the 1.8 mu m fluorescence of the sample is obvious indicating that it is suitable to 2 mu m application. (c) 2008 Elsevier B.V. All rights reserved.

碱金属和碱土金属氟化物对掺Er^3＋氟磷酸盐玻璃光谱性质的影响

研究了碱金属和碱土金属离子修饰的掺Er^3＋氟磷酸盐玻璃的光谱性质，讨论了碱金属和碱土金属对铒氟磷玻璃的吸收和发射截面、荧光半高宽，Judd-Ofelt强度参数和上转换发光强度等光谱性质的影响，并与一些传统氧化物玻璃系统进行了比较．研究表明碱金属K^＋和碱土金属Sr^2＋掺杂高的玻璃更适宜用作光放大器基质．含12mol％K^＋的氟磷玻璃展现出7．83×10^-21cm^2的高发射截面和最小的荧光上转换强度；含23mol％Sr^2＋的氟磷玻璃则有7．58×10^-21cm^2的高发射截面、65nm的荧光半高

用于波导放大器的Er^3＋／Yb^3＋共掺磷酸盐玻璃的性能研究

通过优化熔融条件和玻璃组份，成功开发出一种新的Er^3+／Yb^3+共掺磷酸盐玻璃，其在沸水和熔盐中均表现出很好的化学稳定性。通过分析室温下Er^3+／Yb^3+共掺磷酸盐玻璃的吸收光谱，计算得到了Er^3+离子在波长1533nm处的峰值发射截面和杜得-奥菲而特强度参数；其中Er^3+离子在波长1533nm处的峰值发射截面为0．72×10^20cm^2，大于Schott的IOG1玻璃中Er^3+离子的峰值发射截面0．67×10^-20cm^2。通过改变离子交换的条件，获得了1．55μm单模光波导的制作条件

Preparation and spectroscopic properties of Er3+-doped high silica glass fabricated by sintering nanoporous glass

A compact nonporous high silica (SiO2 % > 96%) glass containing 3400 ppm Er3+ ions, which was about ten times higher than that in Er-doped silica fiber amplifier (EDSFA), was synthesized by sintering porous glass immersed into erbium nitrate solution. The 1532 nm fluorescence has a FWHM (Full Width at Half Maximum) of 45 nm wider than that of EDSFA and possesses the glass with potential application in broadband fiber amplifiers. The Judd-Ofelt theoretical analysis reflects that Er3+ ions are located in a higher covalent environment which are comparable to those of aluminosilicate glass. (c) 2005 Elsevier B.V. All rights reserved.

High quantum efficiency and high concentration erbium-doped silica glasses fabricated by sintering nanoporous glasses

A new method was used to prepare erbium-doped high silica (SiO2% > 96%) glasses by sintering nanoporous glasses. The concentration of erbium ions in high silica glasses can be considerably more than that in silica glasses prepared by using conventional methods. The fluorescence of 1532 nm has an FWHM (Full Wave at Half Maximum) of 50 nm, wider than 35 nm of EDSFA (erbium-doped silica fiber amplifer), and hence the glass possesses potential application in broadband fiber amplifiers. The Judd-Ofelt theoretical analysis reflects that the quantum efficiency of this erbium-doped glass is about 0.78, although the erbium concentration in this glass (6 x 103) is about twenty times higher than that in silica glass. These excellent characteristics of Er-doped high silica glass will be conducive to its usage in optical amplifiers and microchip lasers.

Spectroscopic properties of Nd3+:(La,Sr)(Al,Ta)O-3 crystal

A new laser crystal Nd3+:(La, Sr)(Al, Ta)O-3 (abbreviated as Nd3+:LSAT) has been grown by the conventional Czochralski method. The absorption and luminescence spectra of trivalent neodymium in Nd3+:LSAT crystal were measured at room temperature. The value of absorption and emission cross-section was calculated. The Judd-Ofelt analysis was applied to the crystal to get the phenomenological parameters (Omega(i), i = 2,4,6), the line strengths, the radiative transition rates, the branching ratios and the radiative lifetime. (C) 2006 Elsevier B.V. All rights reserved.

掺Er3+玻璃上转换发光特性研究

采用高温熔制工艺制备了掺Er3+硅酸盐玻璃，应用Judd-Ofelt 理论计算了Er3+光谱参数， 发现玻璃中含有0.15 mol%Er2O3 时各参数取得最大值；分析了玻璃的吸收光谱随Er3+离子浓度的变 化关系；上转换光谱分析表明在522 nm、544 nm、658 nm 处有较强的绿光和红光，分别对应于 2H11/2→4I15/2、4 S3/2→4I15/2、4 F9/2→4I15/2 的跃迁，且522 nm 绿光强度和658nm 红光强度要远大于544 nm 绿光强度. 分析了上转换发光强度随泵浦功率和Er3+离子浓度的变化关系，揭示了上转换发光机制 主要是激发态吸收和能量转换，且均为双光子吸收过程.

铒镱共掺铅硅酸盐玻璃的光谱分析

采用传统的高温熔融工艺制备了铒镱共掺铅硅酸盐玻璃. 测量了样品的吸收光谱、荧光光谱和折射率， 利用McCumber 理论和Judd-Ofelt 理论计算了该玻璃系统中Er3+离子4I13/2→4I15/2 能级跃迁受激发射截面和荧 光寿命.该玻璃在1 536 nm 处受激发射截面σemi 为8.62×10-21 cm2；荧光寿命长达11.32 ms（实验测量值为9.26 ms）；在1536 nm 附近有很强的荧光发射，荧光有效线宽为46.5 nm；样品存在中心波长为580 nm 的4S3/2→4I15/2 跃迁的上转换荧光. 结果表明，该样品荧光寿命长，受激发射截面大，同时具有较弱的上转换发光等特性， 是制作高能脉冲光纤激光器的理想材料