Desenvolvimento de catalisadores bifuncionais de óxido de zircônio modificado por óxidos de tungstênio e molibdênio contendo platina para a reação de isomerização de n-parafinas

Bifunctional catalysts based on zircon oxide modified by tungsten (W = 10, 15 and 20 %) and by molybdenum oxide (Mo= 10, 15 e 20 %) containg platinum (Pt = 1%) were prepared by the polymeric precursor method. For comparison, catalysts the tungsten base was also prepared by the impregnation method. After calcinations at 600, 700 and 800 ºC, the catalysts were characterized by X-ray diffraction, fourier-transform infrared spectroscopy, thermogravimetric and differential thermal analysis, nitrogen adsorption and scanning electron microscopy. The profile of metals reduction was determined by temperature programmed reduction. The synthesized catalysts were tested in n-heptane isomerization. X-ray diffractogram of the Pt/WOx-ZrO2 and Pt/MoOx-ZrO2 catalysts revealed the presence of tetragonal ZrO2 and platinum metallic phases in all calcined samples. Diffraction peaks due WO3 and ZrO2 monoclinic also were observed in some samples of the Pt/WOx-ZrO2 catalysts. In the Pt/MoOx-ZrO2 catalysts also were observed diffraction peaks due ZrO2 monoclinic and Zr(MoO4)2 oxide. These phases contained on Pt/WOx-ZrO2 and Pt/MoOx-ZrO2 catalysts varied in accordance with the W or Mo loading and in accordance with the calcination temperature. The infrared spectra showed absorption bands due O-W-O and W=O bonds in the Pt/WOx-ZrO2 catalysts and due O-Mo-O, Mo=O and Mo-O bonds in the Pt/MoOx-ZrO2 catalysts. Specific surface area for Pt/WOx-ZrO2 catalysts varied from 30-160 m2 g-1 and for the Pt/MoOx-ZrO2 catalysts varied from 10-120 m2 g-1. The metals loading (W or Mo) and the calcination temperature influence directly in the specific surface area of the samples. The reduction profile of Pt/WOx-ZrO2 catalysts showed two peaks at lower temperatures, which are attributed to platinum reduction. The reduction of WOx species was evidenced by two reduction peak at high temperatures. In the case of Pt/MoOx-ZrO2 catalysts, the reduction profile showed three reduction events, which are attributed to reduction of MoOx species deposited on the support and in some samples one of the peak is related to the reduction of Zr(MoO4)2 oxide. Pt/WOx-ZrO2 catalysts were active in the n-heptane isomerization with high selectivity to 3-methyl-hexane, 2,3- dimethyl-pentane, 2-methyl-hexane among other branched hydrocarbons. The Pt/MoOx-ZrO2 catalysts practically didn't present activity for the n-heptane isomerization, generating mainly products originating from the catalytic cracking

Efeitos estéricos e eletrônicos de substituintes alquilas em catalisadores titanocênicos solúveis na polimerização sindioespecífica de estireno

Titanocenos são catalisadores solúveis conhecidos para a polimerisação estereoespecífica de olefinas pró-quirais como o estireno. Nesse trabalho descrevemos as relações entre as características do poliestireno e a estrutura do precursor do catalisador, de fato aqueles da família (RCp)2TiCl2 (R = H, etila, iso-propila, n-propila, sec-butila, n-butila, iso-amila e ciclohexila). Todos os catalisadores são ativos para a produção de poliestireno acima de zero graus centígrados. A sindiotaticidade dos polímeros são dependentes da cadeia lateral dos anéis aromáticos do titanoceno e da temperatura da polimerização. A relação entre os fatores estéricos e eletrônicos do precursor do catalisador e os produtos de polimerização são apresentados e discutidos.

Método de detecção interferométrica de fase, com baixa profundidade de modulação, aplicado à medição de deslocamentos nanométricos em atuadores e mini-manipuladores piezoelétricos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudos sobre a síntese de piperidinas funcionalizadas através de reações pentacomponentes, utilizando compostos de nióbio como catalisadores

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preparação de catalisadores de reforma de glicerol para células a combustível de eletrólito sólido

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Catalisadores 'PT' e 'PTSN' modificados com 'SN''O IND.2' para a oxidação eletroquímica de etanol

Pós-graduação em Química - IQ

Catalisadores trimetálicos nanoestruturados a base de PtRu para oxidação de metanol

Pós-graduação em Química - IQ

Estudo do efeito do tempo e do meio de moagem de alta energia para obtenção de pós nanométricos de hidretos de titânio e nióbio

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Sínteses e caracterização de novos catalisadores zeolíticos e sua como suportes inorgânicos para imobilização de lipase produzida por Rhizomucor miehei e seu estudo catalítico na reação de transesterificação do óleo de soja para produção de biodiesel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Isolamento de fungos produtores de lipases catalisadores de reações de transesterificação para produção de biodiesel

Pós-graduação em Microbiologia - IBILCE

Síntese e aplicação de catalisadores à base de óxidos de cério, tungstênio e HZSM-5 para a produção do biodiesel

This work presents a study on the production of biodiesel by esterification reaction of oleic acid with methanol using batch reactor and different catalysts based on CeO2 and WO3 and HZSM-5. Acid treatment was performed in order to increase the catalytic activity. Different characterization techniques were performed, among them X-ray diffraction (XRD), Thermogravimetric analysis TGA/DTA, Spectroscopy in the Region in Fourier Transform Infrared (FTIR) and X-ray fluorescence (XRF). The effects of independent variables: temperature, molar ratio of oil: alcohol and the amount of catalyst and their interactions on the dependent variable (conversion of oleic acid to the corresponding ester). Overall, through the results obtained in the characterization was observed that the applied treatments were efficient, however the XRF technique, indicated that tungsten oxide leaching could occur during the preparation of the materials. The treatments performed on HZSM-5 caused no significant changes in the structure indicating that the zeolite was quite resistant to the treatments used. It was evaluated using complete 23 factorial design. For the catalysts investigated, the best reaction conditions were obtained when using higher levels of the independent variables temperature and amount of catalyst. However, for the variable molar ratio the lowest level showed significant yields for most of the synthesized catalyst, obtaining maximum conversion to the OC (67.97%), OW (74.37%), HZSM-5 (61.16%) OC-OW 1 (75.93%), OC-OW 2 (82.57%), OC-OW 3 (79.15%), S/OC-OW 1 (86.90%), S/OC-OW 2 (91.04%), S/OC-OW 3 (88.60%), S/OC-OW/H 1 (92.34%), S/OC-OW/H 2 (100%) and S/OC-OW/H 3 (98.16%). According to the experimental design, the temperature has the biggest influence on the reaction variable for all the synthesized catalysts. Among the catalysts investigated S/OC-OW/H 2 e S/OC-OW/H 3 were more effective. Reuse tests showed that the catalyst activity decreased after each cycle, indicating that the regeneration process was effective. The leaching test indicated that the catalysts are heterogeneous in the evaluated operating range. The catalysts investigated showed themselves promising for the production of biodiesel.

Estudo das reações de oxidação de metanol e etanol sobre catalisadores bimetálicos suportados preparados por métodos coloidais

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo da obtenção de biocombustíveis a partir da rota tecnológica de craqueamento utilizando carbonato de sódio e lama vermelha como catalisadores

Neste trabalho foi estudado o processo de destilação do produto líquido orgânico, obtido no craqueamento catalítico do óleo de palma (Elaeis guineensis, Jacq) bruto em escala piloto, empregando os catalisadores carbonato de sódio (Na₂CO₃) e a lama vermelha, variando o percentual de catalisador em 10% m/m e 15% m/m em relação à matéria prima utilizada, sendo fixada uma temperatura operacional de 450ºC, visando obter frações de biocombustíveis (bio-gasolina, bio-querosene e bio-óleo) semelhantes aos combustíveis derivados do petróleo. Os catalisadores foram submetidos a um pré-tratamento de desidratação durante 2 horas em uma estufa à 300ºC, posteriormente foram realizadas as análises de DRX, IR e TG. Quanto à matéria prima, foram realizadas análises físico-químicas, visando à caracterização do óleo de palma. Os produtos líquidos orgânicos (PLOs) obtidos foram submetidos a operações unitárias de separação, decantação e filtração simples em escala de bancada, para posteriormente serem realizadas análises físico-químicas e composicionais. Os PLOs foram destilados em uma coluna Vigreux de seis (06) estágios, e as frações condensadas foram coletadas de acordo com as faixas de destilação da gasolina (60ºC - 190ºC), querosene (190ºC - 235ºC) e diesel (235°C - 370ºC), para posteriormente serem caracterizadas. Verificou-se uma melhor eficiência para o catalisador carbonato de sódio a 15% m/m quanto a redução do índice de acidez, cerca de 1,7 mgKOH/g, assim como uma conversão mássica de 97% do óleo em PLO, notou-se também que, ao aumentar a quantidade de catalisador, isto favoreceu a obtenção de um produto final com uma melhor qualidade. A lama vermelha por outro lado, apresentou rendimentos de até 64% m/m e produtos com baixa acidez cerca de 62,90 mgKOH/g, comparando este resultado com dados encontrados na literatura. A partir dos resultados finais, verificou-se a eficiência dos catalisadores, no qual o catalisador carbonato de sódio forneceu produtos com baixa acidez e com boas características para uso como combustível.

Desenvolvimento de materiais catalisadores heterogêneos a base de estrôncio (Sr) e zircônio (Zr) para transesterificação de óleos e gorduras - síntese, caracterização e performance reacional

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influência de diferentes tipos e concentrações de catalisadores químicos na eficiência do clareamento dental

O objetivo deste estudo foi avaliar a eficiência de diferentes tipos e concentrações de catalisadores químicos sobre a efetividade de um gel a base de peróxido de hidrogênio a 35% no clareamento dental. Foram utilizados 170 dentes incisivos bovinos dos quais foram obtidos 510 discos de esmalte-dentina, com 3mm de diâmetro, utilizando-se broca tipo trefina. A leitura da cor dos espécimes foi realizada com um espectrofotômetro de refletância. Foi utilizado para todos os grupos um gel experimental a base de peróxido de hidrogênio a 35%. Para avaliação dos catalisadores químicos, os espécimes foram divididos em grupos de acordo com o tipo e a concentração da substância adicionada: SF - Sulfato Ferroso (0,001%, 0,002% e 0,003%), GF - Gluconato Ferroso (0,01%, 0,02% e 0,03%), CF - Cloreto Férrico (0,01%, 0,02% e 0,03%), GM - Gluconato de Manganês (0,01%, 0,02% e 0,03%) e CM - Cloreto de Manganês (0,01%, 0,02% e 0,03%). Dois grupos controle foram preparados, sendo eles um grupo controle positivo (CP), na qual não foi adicionado nenhum catalisador químico ao gel clareador, e um grupo controle negativo (CN), onde os espécimes não foram clareados e foram apenas submersos em saliva artificial. Sobre a superfície de esmalte foram realizadas 3 aplicações dos respectivos géis clareadores por 10 min cada, as quais foram repetidas após 7 dias, totalizando 2 sessões de 30 minutos. Foram feitas avaliações de cor antes do clareamento, 7 dias após da primeira sessão e 7 dias após a segunda. Os espécimes foram armazenados em saliva artificial e novamente avaliados após 1 ano. Os dados foram analisados pelos testes de análise da variância paramétrica (ANOVA) e teste de Tukey. Os resultados mostraram que o uso de alguns dos ativadores químicos testados foram efetivos em reduzir o amarelamento das amostras...