Growth of ultrahigh density single-walled carbon nanotube forests by improved catalyst design.

We have grown vertically aligned single-walled carbon nanotube forests with an area density of 1.5 × 10(13) cm(-2), the highest yet achieved, by reducing the average diameter of the nanotubes. We use a nanolaminate Fe-Al(2)O(3) catalyst design consisting of three layers of Al(2)O(3), Fe, and Al(2)O(3), in which the lower Al(2)O(3) layer is densified by an oxygen plasma treatment to increase its diffusion barrier properties, to allow a thinner catalyst layer to be used. This high nanotube density is desirable for using carbon nanotubes as interconnects in integrated circuits.

Fishtail effects and improved critical current density in polycrystalline bulk MgB2 containing carbon nanotubes

Bulk, polycrystalline MgB2 samples containing 2.5 wt.% multi-walled carbon nanotubes (CNTs) have been prepared by conventional solid state reaction at 800 °C. The effect of Mg precursor powders composed of two different particle sizes on the critical current density (Jc) of the as-sintered samples has been investigated. An enhancement of Jc at high field has been observed in MgB2 samples containing CNTs prepared with fine Mg powders, whereas the values of Jc in the sample prepared using the coarser Mg powders was slightly decreased. These results contrast significantly with measurements on pure, undoped, MgB2 samples prepared from the same Mg precursor powders. They suggest that carbon substitution into the MgB2 lattice, which accounts for increased flux pinning, and therefore Jc, is more effective in precursor Mg powders with a larger surface area. Rather surprisingly, the so-called fishtail effect, observed typically in MgB2 single crystals and in the (RE)BCO family of high temperature superconductors (HTSs), was observed in both sets of CNT-containing polycrystalline samples as a result of lattice defects associated with C substitution. Significantly, analytical fits to the data for each sample suggest that the same flux pinning mechanism accounts for the fishtail effect in polycrystalline MgB2 and (RE)BCO. © 2013 Elsevier B.V. All rights reserved.

Low temperature growth of ultra-high mass density carbon nanotube forests on conductive supports

We grow ultra-high mass density carbon nanotube forests at 450°C on Ti-coated Cu supports using Co-Mo co-catalyst. X-ray photoelectron spectroscopy shows Mo strongly interacts with Ti and Co, suppressing both aggregation and lifting off of Co particles and, thus, promoting the root growth mechanism. The forests average a height of 0.38 μm and a mass density of 1.6 g cm -3. This mass density is the highest reported so far, even at higher temperatures or on insulators. The forests and Cu supports show ohmic conductivity (lowest resistance ∼22 kΩ), suggesting Co-Mo is useful for applications requiring forest growth on conductors. © 2013 AIP Publishing LLC.