Processing and mechanical properties of cast aluminum containing scandium, zirconium, and ytterbium

A series of aluminum alloys containing additions of scandium, zirconium, and ytterbium were cast to evaluate the effect of partial ytterbium substitution for scandium on tensile behavior. Due to the high price of scandium, a crucible-melt interaction study was performed to ensure no scandium was lost in graphite, alumina, magnesia, or zirconia crucibles after holding a liquid Al-Sc master alloy for 8 hours at 900 °C in an argon atmosphere. The alloys were subjected to an isochronal aging treatment and tested for conductivity and Vickers microhardness after each increment. For scandium-containing alloys, peak hardnesses of 520-790 MPa, and peak tensile stresses of 138-234 MPa were observed after aging from 150-350 °C for 3 hours in increments of 50 °C, and for alloys without scandium, peak hardnesses of 217-335 MPa and peak tensile stresses of 45-63 MPa were observed after a 3 hour, 150 °C aging treatment. The hardness and tensile strength of the ytterbium containing alloy was found to be lower than in the alloy with no ytterbium substitution.

SOLUTE-DERIVED THERMAL STABILITY OF NANOCRYSTALLINE ALUMINUM AND PROCESSING FACTOR INFLUENCE ON THE FORMATION OF AL6MN QUASICRYSTALS IN MELT-SPINNING

Thermal stability of nanograined metals can be difficult to attain due to the large driving force for grain growth that arises from the significant boundary area constituted by the nanostructure. Kinetic approaches for stabilization of the nanostructure effective at low homologous temperatures often fail at higher homologous temperatures. Thermodynamic approaches for thermal stabilization may offer higher temperature stability. In this research, modest alloying of aluminum with solute (1 at.% Sc, Yb, or Sr) was examined as a means to thermodynamically stabilize a bulk nanostructure at elevated temperatures. After using melt-spinning and ball-milling to create an extended solid-solution and nanostructure with average grain size on the order of 30-45 nm, 1 h annealing treatments at 673 K (0.72 Tm) , 773 K (0.83 Tm) , and 873 K (0.94 Tm) were applied. The alloys remain nanocrystalline (<100 nm) as measured by Warren-Averbach Fourier analysis of x-ray diffraction peaks and direct observation of TEM dark field micrographs, with the efficacy of stabilization: Sr>Yb>Sc. Disappearance of intermetallic phases in the Sr and Yb alloys in the x-ray diffraction spectra are observed to occur coincident with the stabilization after annealing, suggesting that precipitates dissolve and the boundaries are enriched with solute. Melt-spinning has also been shown to be an effective process to produce a class of ordered, but non-periodic crystals called quasicrystals. However, many of the factors related to the creation of the quasicrystals through melt-spinning are not optimized for specific chemistries and alloy systems. In a related but separate aspect of this research, meltspinning was utilized to create metastable quasicrystalline Al6Mn in an α-Al matrix through rapid solidification of Al-8Mn (by mol) and Al-10Mn (by mol) alloys. Wheel speed of the melt-spinning wheel and orifice diameter of the tube reservoir were varied to determine their effect on the resulting volume proportions of the resultant phases using integrated areas of collected x-ray diffraction spectra. The data were then used to extrapolate parameters for the Al-10Mn alloy which consistently produced Al6Mn quasicrystal with almost complete suppression of the equilibrium Al6Mn orthorhombic phase.

An Investigation of the Properties of some of the White Metal Alloys

Although there is no standardized list of alloys, most investigators have, to avoid confusion, concurred in at least grouping the metals under several general heads. Precious metals: gold, silver and the platinum group; the light metals: aluminum and magnesium; the non-ferrous metals (excluding all steels and iron-base alloys); and the antifriction metals.

The Age-Hardening of Magnesium with Aluminum and Zinc

Magnesium is one of the most active elements and forms oxides, nitrides, and carbides, but not hydrides. Due to its activity, low melting point, low strength when unalloyed, and the difficulty with which it is worked, magnesium has not been and is not at present well developed.

Age Hardening of Copper-Aluminum Alloy Castings

Age hardening occurs in alloys of the solid solution type containing a hardening constituent, be it metal or metallic compound, which is more soluble in the solvent phase at higher temperatures than at lower ones.

Alcoa structural handbook ; a design manual for aluminum.

"Supplement; a reprint of ASCE Proceedings ...: Paper number 970, Specifications for structures of aluminum alloy 6061-T6; second progress report of the Committee of the Structural Division on Design in Lightweight Structural Alloys [and] Paper number 971, Specifications for structures of aluminum alloy 2014-T6; third progress report of the Committee of the Structural Division on Design in Lightweight Structural Alloys": 34, 32 pages at end.

Methods for the analysis of columbium and its alloys /

This report consists of the analytical procedures modified or developed at Pratt & Whitney Aircraft, CANEL, for the determination of alloying constituents and impurities in columbium and its alloys. Included are spectrophotometric methods for chromium, columbium, iron, molybdenum, tungsten, nickel, nitrogen and titanium; volumetric methods for chromium, vanadium and zirconium; emission and X-ray spectrographic methods for various alloying elements; a spectrographic method for zirconium and trace impurities and miscellaneous methods for aluminum, carbon, oxygen and hydrogen.

Enriched uranium fuel materials : a bibliography of unclassified literature /

Unclassified reports on processing of enriched UF₆ into U metal, U-base alloys, UO₂, and UO₂SO₄ for use a reactor fuels are annotated. Recovery of enriched U scrap, methods of isotopic analysis, health physics, criticality problems, and materials management are emphasized. A few references to papers presented at the Geneva Conference, 1955, and other recent nonreport literature are included. 254 references.

Cyclic creep buckling of integrally stiffened aluminum alloy panels

ASTIA Document no. AD 155834.

Rapid manufacturing of aluminum components

A manufacturing technique for the production of aluminum components is described. A resin-bonded part is formed by a rapid prototyping technique and then debound and infiltrated by a second aluminum alloy under a nitrogen atmosphere. During thermal processing, the aluminum reacts with the nitrogen and is partially transformed into a rigid aluminum nitride skeleton, which provides the structural rigidity during infiltration. The simplicity and rapidity of this process in comparison to conventional production routes, combined with the ability to fabricate complicated parts of almost any geometry and with high dimensional precision, provide an additional means to manufacture aluminum components.

Strength-ductility behaviour of Al-Si-Cu-Mg casting alloys in T6 temper

A comparative study of the mechanical properties of 20 experimental alloys has been carried out. The effect of different contents of Si, Cu, Mg, Fe and Mn, as well as solidification rate, has been assessed using a strength-ductility chart and a quality index-strength chart developed for the alloys. The charts show that the strength generally increases and the ductility decreases with an increasing content of Cu and Mg. Increased Fe (at Fe/Mn ratio 0.5) dramatically lowers the ductility and strength of low Si alloys. Increased Si content generally increases the strength and the ductility. The increase in ductility with increased Si is particularly significant when the Fe content is high. The charts are used to show that the cracking of second phase particles imposes a limit to the maximum achievable strength by limiting the ductility of strong alloys. The (Cu + Mg) content (at.%), which determines the precipitation strengthening and the volume fraction of Cu-rich and Mg-rich intermetallics, can be used to select the alloys for given strength and ductility, provided the Fe content stays below the Si-dependent critical level for the formation of pre-eutectic alpha-phase particles or beta-phase plates.

On the sintering of uncompacted, pre-alloyed Al powder alloys

The effect of the addition of elemental Mg, Sri and Pb on the sintering of impressed prealloyed 2124 and 6061 powder has been investigated. Despite being sintered at a temperature that resulted in similar to20 vol.% liquid phase, high density was possible only upon the addition of similar to1% elemental Mg as well as trace amounts of Sri or Pb. Additions of Mg facilitated oxide disruption, while Sri and Pb segregated to the liquid phase, where they reduced the liquid's surface tension, thus improving sintering. (C) 2002 Elsevier Science B.V. All rights reserved.

The influence of strontium on porosity formation in Al-Si alloys

Strontium modification is known to alter the amount, characteristics, and distribution of porosity in Al-Si castings. Although many theories have been proposed to account for these effects, most can be considered inadequate because of their failure to resolve contradictions and discrepancies in the literature. In an attempt to critically appraise some of these theories, the amount, distribution, and morphology of porosity were examined in sand-cast plates of Sr-free and Sr-containing pure Al, Al-l wt pet Si, and Al-9 wt pet Si alloys. Statistical significance testing was used to verify apparent trends in the porosity data. No apparent differences in the amount, distribution, and morphology of porosity were observed between Sr-free and Sr-containing alloys with no or very small eutectic volume fractions. However, Sr modification significantly changed the amount, distribution, and morphology of porosity in alloys with a significant volume fraction of eutectic. ne addition of Sr reduced porosity in the hot spot region of the casting, and the pores became well dispersed and rounded. This result can be explained by considering the combined effect of the casting design and the differences in the pattern of eutectic solidification between unmodified and Sr-modified alloys.

A critical review of the stress corrosion cracking (SCC) of magnesium alloys

This review aims to provide a foundation for the safe and effective use of magnesium (Mg) alloys, including practical guidelines for the service use of Mg alloys in the atmosphere and/or in contact with aqueous solutions. This is to provide support for the rapidly increasing use of Mg in industrial applications, particularly in the automobile industry. These guidelines should be firmly based on a critical analysis of our knowledge of SCC based on (1) service experience, (2) laboratory testing and (3) understanding of the mechanism of SCC, as well as based on an understanding of the Mg corrosion mechanism.