The microstructures and mechanical properties of cast Mg-Zn-Al-RE alloys

The microstructures and mechanical properties of cast Mg-Zn-Al-RE alloys with 4 wt.% RE and variable Zn and At contents were investigated. The results show that the alloys mainly consist of alpha-Mg, Al2REZn2, Al4RE and tau-Mg-32(Al,Zn)(49) phases. and a little amount of the beta-Mg17Al12 phase will also be formed with certain Zn and At contents. When increasing the Zn or At content, the distribution of the Al2REZn2 and Al4RE phases will be changed from cluster to dispersed, and the content of tau-Mg-32(Al,Zn)(49) phase increased gradually. The distribution of the Al2REZn2 and Al4RE phases, and the content of beta- or tau-phase are critical to the mechanical properties of Mg-Zn-Al-RE alloys.

Age hardening of a sintered Al-Cu-Mg-Si-(Sn) alloy

The age hardening response of a sintered Al-3.8 wt% Cu-1.0 wt% Mg-0.70 wt% Si alloy with and without 0.1 wt% Sn was investigated. The sequence of precipitation was characterised using transmission electron microscopy. The ageing response of the sintered Al-Cu-Mg-Si-(Sn) alloy is similar to that of cognate wrought 2xxx series alloys. Peak hardness was associated with a fine, uniform dispersion of lath shaped precipitates, believed to be either the betaor Q phase, oriented along < 010 >. directions and theta' plates lying on {001}(alpha). planes. Natural ageing also resulted in comparable behaviour to that observed in wrought alloys. Porosity in the powder metallurgy alloys did not significantly affect the kinetics of precipitation during artificial ageing. Trace levels of tin, used to aid sintering, slightly reduced the hardening response of the alloy. However, this was compensated for by significant improvements in density and hardness. (c) 2005 Elsevier B.V. All rights reserved.

Quasicrystals and their crystalline homologues in the Al-Mn-Cu ternary alloys

Electron diffraction and high-resolution electron microscopy have been employed to differentiate among icosahedral, decagonal and crystalline particles that occur in as-cast and rapidly solidified Al-Mn-Cu alloys. The resemblance between decagonal quasicrystals and crystals in their electron diffraction patterns is striking. The crystalline structure is based on the orthorhombic 'Al3Mn' structure, but also a new monoclinic phase called 'X' has been discovered and described here. The present observations are also closely related to the orthorhombic structures in Al60Mn11Ni4. The occurrence of fine-scale twinning and fragmentation into domains explains the complex diffraction effects.

Isothermal transformation of beta-phase in Cu-rich Cu-Al-Sn alloys

Microstructural changes resulting from isothermal decomposition of the beta-phase have been studied in Cu-rich binary Cu-Al and ternary Cu-Al-Sn alloys containing up to 3 at.% Sn at temperatures from 873 to 673 K. Results are presented as TTT diagrams. The decomposition occurs in several stages, each of which involves the establishment of metastable equilibrium between beta and one or more of the product phases alpha, beta(1) and gamma(2). Addition of Sn has been shown to increase the stability of the ordered beta(1)-phase in relation to beta. In alloys containing more than 2 at.% Sn, the beta(1) emerges as a stable phase. At low Sn concentrations beta(1) is metastable. An important new finding is the existence of three-phase equilibrium microstructure containing alpha, beta(1) and gamma(2). Increasing addition of Sn alters the morphology of beta(1) from rosettes to dendrites and finally to Widmanstatten needles.

钠原子激光增强电离光谱研究—以石墨杯为原子化器 原子吸收光谱法对发样中Zn、Cu、Mn、Ap的测定

、I钠原子激光增强电离光谱(LEIS)方法的研究-以石墨杯为原子化器在LEIS方法中，最常见的原子化器是火焰。但由于火焰背景噪声严重且难以克服，在火焰原子化过程中，雾化和热离解不充分，仅有10~(-2)%的分析溶液参与吸收以及火焰气体使测定元素受到高度稀释等不利因素的影响，火焰原子化限制了LEIS方法灵敏度的进一步提高。考虑到石墨炉原子化器较火焰具有取样量少，绝对灵敏度高；样品（包括固态、液态）可直接引入石墨炉内；不会发生如同火焰中所存在的干扰效应；蒸发效率和原子化效率较高，几乎全部样品都能参与吸收等优点，本工作在已建立火焰LEIS方法的实验基础上，将原子化器改换为石墨杯进行了钠原子LEIS方法的研究。到目前为止，国内外仅有的几篇有关石黑炉LEIS的研究报告中，都报导了该方法对钠原子的检出限估计可达到10~(-14)-10~(-15)克，由于此项研究尚处于探索性研究阶段，故有关方法性的系统研究几乎还未见报导。本工作在未使用任何放大器的情况下（实验条件限制）对影响钠原子LEIS信号强度的诸因互进行了实验观察。主要包括：钠原子化条件；激光束位置、阳极电压、激光输出能量、电极位置以及激光脉冲重复率对LEIS信号强度的影响等。并绘制了校准曲线，统计方法的相对标准偏差分别为11%（高浓度）18.2%（低浓度），在现有仪器条件下，还不能测出检出限，测定下限为3*10~(-9)克。对固体粉末直接进行了尝试，检测下限为5*10~(-8)克，进样是为5毫克。在进一步的研究工作中，如有条件使用低噪声的放大器及Bxear积分器，选择门检时间窗，或采用分步激发等手段，估计本方法定会达到预想的高灵敏度，检敏度至少提高了个数量级。对石墨炉原子化LEIS法来说，似比较详细的研究报告，截至实验停止时还未见报导。II原子吸收光谱法对发样中Zn、Cu、Mn、Al的测定发中微量元素ZN、Cu、Mn均属人体必需元素，与人体的生长发育和多种生理功能，临床医学等方面有着极为密切的关系，而Al则被认为是异致某种疾病的元素之一。本工作报告了用火焰法测定Zn、Cu；石墨炉法测定Al、Mn的结果，其中，对Al的测定，为摆脱基体干扰，加入改进剂Mg(NO_3)_2，并采用平台石墨炉进行试验，得到了线性较好的工作曲线，但在实际测定时，由于实验条件的限制，只能采用一般石墨管加基体改进剂对少娄样品中Al含量进行测定。Zn、Cu、Al三种元素由标准曲线法测定；而Mn由于Fe的干扰无法消除而采用标准加入法测定，并因此限制了测定样品数。Cu、ZN、Mn三种元素的回收率分别为102.8%, 99.7%, 102.5%，变异系数为9.6%, 11.3%, 9.7%，对本地居民发中（30个发样）Zn、Cu含量进行测定，Zn、Cu的含量范围为148-318ppm，7.2-15ppm，并计算了Zn/Cu比。本方法对发样中四种元素的测定结果与ICP法进行对照。两种方法测定结果吻合得较好。

The influence of mischmetal and tin on the microstructure and mechanical properties of Mg-6Zn-5Al-based alloys

The influence of the addition of mischmetal (MM) and tin (Sn) (total content of mischmetal and tin = 4 wt.%) on the microstructure, aging behavior and mechanical properties of Mg-6Zn-5Al-based alloys has been investigated. The microstructure of the as-cast alloys consists of alpha-Mg. Mg-32(Al,Zn)(49), Al2Mg5Zn2, Mg2Sn and Al2MMZn2 phases, and the morphology of these intermetallic phases varies with different MM and Sri additions.

Microstructures and mechanical properties of extruded Mg-8Gd-0.4Zr alloys containing Zn

Microstructures and mechanical properties of the Mg-8Gd-xZn-0.4Zr (x = 0, 1 and 3 wt.%) alloys in the as-cast, as-extruded and extruded-T5 conditions, have been investigated. The peak-aged Mg-8Gd-1Zn-0.4Zr alloy during isothermal ageing at 423 K acquires highest mechanical properties, with the highest ultimate tensile strength and yield tensile strength of 314 and 217 MPa, respectively. Addition of Zn has obvious effect on age hardening responses, especially for 1 wt.% Zn addition. It is due to a uniform distribution of beta' phase which can impede the movement of dislocations. However, addition of 3 wt.% Zn to the Mg-8Gd-0.4Zr alloy leads to a precipitation of Mg3Zn3Gd2 phase (W-phase). This phase is incoherent with interface of the matrix and becomes cores of the fracture in tensile test at room or elevated temperature.

Effect of Zn concentration on the microstructures and mechanical properties of extruded Mg-7Y-4Gd-0.4Zr alloys

Microstructures and mechanical properties of the Mg-7Y-4Gd-xZn-0.4Zr (x = 0.5, 1.5, 3, and 5 wt.%) alloys in the as-cast, as-extruded, and peak-aged conditions have been investigated by using optical microscopy, scanning electron microscope, X-ray diffraction, and transmission electron microscopy. It is found that the peak-aged Mg-7Y-4Gd-1.5Zn-0.4Zr alloys have the highest strength after aging at 220 A degrees C. The highest ultimate tensile strength and yield tensile strength are 418 and 320 MPa, respectively. The addition of 1.5 wt.% Zn to the based alloys results in a greater aging effect and better mechanical properties at both room and elevated temperatures. The improved mechanical properties are mainly ascribed to both a fine beta' phase and a long periodic stacking-ordered structure, which coexist together in the peak-aged alloys.

Efeitos da suplementação de fitase sobre a disponibilidade aparente de Mg, Ca, Zn, Cu, Mn e Fe em alimentos vegetais para a tilápia-do-nilo

Cem juvenis de tilápia-do-nilo (Oreochromis niloticus; PV = 100.0 ± 5.0 g) foram distribuídos em 10 tanques-rede com o objetivo de avaliar o efeito da suplementação da enzima fitase (0, 1.000 e 2.000 UFA/kg) sobre a disponibilidade de minerais em alguns alimentos energéticos (milho, milho extrusado, farelo de trigo, farelo de arroz e farelo de sorgo) e protéicos (farelo de soja extrusado, farelo de soja, farelo de girassol, farelo de algodão e glúten de milho) utilizados na alimentação de tilápia-do-nilo (Oreochromis niloticus). Para determinação dos coeficientes de disponibilidade aparente (CDA) do cálcio (Ca), magnésio (Mg), zinco (Zn), cobre (Cu), ferro (Fe) e manganês (Mn), foram confeccionadas 31 rações, marcadas com 0,10% de óxido de crômio III uma referência (ração purificada) e 30 contendo os dez alimentos e os diferentes níveis de suplementação da enzima fitase. O CDA dos nutrientes foi calculado com base no teor de crômio da ração e das fezes. A fitase aumenta, nos vegetais, a disponibilidade do Mg, Cu, Zn e Mn, os quais apresentam tendência diferenciada, em razão do seu valor biológico e do nível de suplementação de enzima.

Effect of magnesium addition on the vacancy-Mg binding free enthalpy in Al-Cr alloys

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal behavior of alpha-(Cu-Al-Ag) alloys

Thermal behavior of alpha-(Cu-Al-Ag) alloys, i.e. alloys with composition less than about 8.5 mass% Al, was studied using differential scanning calorimetry (DSC), differential thermal analysis (DTA), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffractometry (XRD). The results indicated that the presence of silver introduces new thermal events ascribed to the formation of a silver-rich phase and, after addition higher amounts than 8 mass% Ag to the Cu-8 mass% Al alloy it is possible to observe the formation of the gamma(1) phase (Al4Cu9), which is only observed in alloys containing minimum of 9 mass% Al. These results may be attributed to some Ag characteristics and its interaction with Cu and Al.

Martensite decomposition in Cu-Al-Mn-Ag alloys

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of iron on grain refinement of high-purity MG-Al alloys

The effect of iron on the grain refinement of high-purity Mg-3%Al and Mg-91%Al alloys has been investigated using anhydrous FeCl3 as an iron additive at 750degreesC in carbon-free aluminium titanite crucibles. It was shown that grain refinement was readily achievable for both alloys. Fe- and Al-rich intermetallic particles were observed in many magnesium grains. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Corrosion resistance of anodised single-phase Mg alloys

This work studied the effect of the impurity iron and the alloying elements aluminium and zinc in single-phase substrate magnesium alloys on the corrosion resistance of the alloys after anodisation. It was found that increasing zinc content (0-2%) led to increased corrosion resistance of an anodised single-phase Mg-Zn alloy. The addition of Al lowered the corrosion resistance of an anodised commercial purity Mg-Al single-phase alloy, whereas the same addition was found to be beneficial to the corrosion resistance of an anodised high purity Mg-Al single-phase alloy. Heat-treatment made the substrate Mg-Al and Mg-Zn alloys more uniform and hence improved the corrosion resistance of the alloys after anodisation. The detrimental effect of iron impurity on corrosion performance of the unanodised substrate single-phase magnesium alloys was inherited by the anodised alloys. The corrosion resistance of the anodised Mg alloys was found to be closely correlated with the corrosion performance of the unanodised as-cast Mg alloys. (c) 2005 Elsevier B.V. All rights reserved.