956 resultados para ALUMINUM-ALLOY
Resumo:
Plastic collapse modes of sandwich beams have been investigated experimentally and theoretically for the case of an aluminum alloy foam with cold-worked aluminum face sheets. Plastic collapse is by three competing mechanisms: face yield, indentation and core shear, with the active mechanism depending upon the choice of geometry and material properties. The collapse loads, as predicted by simple upper bound solutions for a rigid, ideally plastic beam, and by more refined finite element calculations are generally in good agreement with the measured strengths. However, a thickness effect of the foam core on the collapse strength is observed for collapse by core shear: the shear strength of the core increases with diminishing core thickness in relation to the cell size. Limit load solutions are used to construct collapse maps, with the beam geometrical parameters as axes. Upon displaying the collapse load for each collapse mechanism, the regimes of dominance of each mechanism and the associate mass of the beam are determined. The map is then used in optimal design by minimizing the beam weight for a given structural load index.
Resumo:
A finite element study has been performed on the effects of holes and rigid inclusions on the elastic modulus and yield strength of regular honeycombs under biaxial loading. The focus is on honeycombs that have already been weakened by a small degree of geometrical imperfection, such as a random distribution of fractured cell walls, as these imperfect honeycombs resemble commercially available metallic foams. Hashin-Shtrikman lower and upper bounds and self-consistent estimates of elastic moduli are derived to provide reference solutions to the finite element calculations. It is found that the strength of an imperfect honeycomb is relatively insensitive to the presence of holes and inclusions, consistent with recent experimental observations on commercial aluminum alloy foams.
Resumo:
Thermal failure of SiC particulate-reinforced 6061 aluminum alloy composites induced by both laser thermal shock and mechanical load has been investigated. The specimens with a single-edge notch were mechanically polished to 0.25 mm in thickness. The notched-tip region of the specimen is subjected to laser beam rapid heating. In the test, a pulsed Nd:glass laser beam is used with duration 1.0 ms or 250 mu s, intensity 15 or 70 kW/cm(2), and spot size 5.0 mm in diameter. Threshold intensity was tested and fracture behavior was studied. The crack-tip process zone development and the microcrack formation were macroscopically and microscopically observed. It was found that in these materials, the initial crack occurred in the notched-tip region, wherein the initial crack was induced by either void nucleation, growth, and subsequent coalescence of the matrix materials or separation of the SiC particulate-matrix interface. It was further found that the process of the crack propagation occurred by the fracture of the SiC particulates.
Resumo:
We previously proposed a method for estimating Young's modulus from instrumented nanoindentation data based on a model assuming that the indenter had a spherical-capped Berkovich geometry to take account of the bluntness effect. The method is now further improved by releasing the constraint on the tip shape, allowing it to have a much broader arbitrariness to range from a conical-tipped shape to a flat-ended shape, whereas the spherical-capped shape is just a special case in between. This method requires two parameters to specify a tip geometry, namely, a volume bluntness ratio V-r and a height bluntness ratio h(r). A set of functional relationships correlating nominal hardness/reduced elastic modulus ratio (H-n/E-r) and elastic work/total work ratio (W-e/W) were established based on dimensional analysis and finite element simulations, with each relationship specified by a set of V-r and h(r). Young's modulus of an indented material can be estimated from these relationships. The method was shown to be valid when applied to S45C carbon steel and 6061 aluminum alloy.
Resumo:
In this paper, a dynamic damage model in ductile solids under the application of a dynamic mean tensile stress is developed. The proposed model considers void nucleation and growth as parts of the damage process under intense dynamic loading (strain rates epsilon greater than or equal to 10(3) s(-1)). The evolution equation of the ductile void has the closed form, in which work-hardening behavior, rate-dependent contribution and inertial effects are taken into account. Meanwhile, a plate impact test is performed for simulating the dynamic fracture process in LY12 aluminum alloy. The damage model is incorporated in a hydrodynamic computer code, to simulate the first few stress reverberations in the target as it spalls and postimpact porosity in the specimen. Fair agreement between computed and experimental results is obtained. Numerical analysis shows that the influence of inertial resistance on the initial void growth in the case of high loading rate can not be neglected. It is also indicated that the dynamic growth of voids is highly sensitive to the strain rates.
Resumo:
In this paper, a mathematical model of dynamic fracture in porous ductile materials under intense dynamic general loading is developed. The mathematical model includes the influence of inertial effects and material rate sensitivity, as well as the contribution of surface energy of a void and material work-hardening. In addition, the condition of the void compaction is considered as well. The threshold stresses for the void growth and compaction are obtained. A simple criterion for ductile fracture which is associated with material distention and plastic deformation is adopted. As an application of the theoretical model, the processes of two-dimensional spallation in LY12 aluminum alloy are successfully simulated by means of two-dimensional finite-difference Lagrangian code.
Resumo:
The strain energy density criterion is used to characterize subcritical crack growth in a thin aluminum alloy sheet undergoing general yielding. A finite element analysis which incorporates both material and geometrical nonlinear behaviors of the cracked sheets is developed to predict fracture loads at varying crack growth increments. The predicted results are in excellent agreement with those measured experimentally, thus confirming the validity of the strain energy density criterion for characterizing ductile crack propagation.
Resumo:
对LY12铝合金在低周疲劳条件下的裂纹情况和随后进行的动态拉伸条件下裂纹的发展给予了观察和统计分析。发现裂纹的累积数密度分布在损伤演化过程中保持指数形式,用NAG模型对实验结果进行分析,得出该材料裂纹演化发展方程的各种参数。
Resumo:
采用有限元分析软件ANSYS,分析了快速凝固/粉末冶金(Rapidly Solidified/Powder Metallurgy,RS/PM)高阻尼铝合金FMS0714/10(Zn-30Al)的挤压成形过程,研究了模具与坯料间的摩擦条件和挤压比对阻尼铝合金成形过程的影响,探讨了挤压过程材料表面产生裂纹的机理,进行了成形工艺优化.研究结果表明:挤压过程中FMS0714/10(Zn-30Al)阻尼铝合金材料的流动与变形不均匀,导致了应力应变分布的不均匀:材料表面应力应变较大,芯部应力应变较小;表面过大的应变和轴向拉应力是表面裂纹的诱因;减小模具和坯料间的摩擦,增大挤压比,可以减小材料表面应力,使应变分布趋于均匀,从而减少材料表面损伤,优化材料表面质量,提高成品合格率.数值模拟的研究结果将为FMS0714/10(Zn-30Al)阻尼铝合金材料挤压工艺的制订以及新材料的设计和研制提供有益的参考.
Resumo:
通过调整电解液中硅酸钠的浓度,利用等离子体电解氧化(PEO)技术在铝合金LY12表面制备了各种陶瓷涂层,利用光学显微镜、XRD、电化学阻抗谱(EIS)对涂层的形貌、成分和涂层在NaCl溶液中耐腐蚀性能进行了研究.结果表明:提高电解液中硅酸钠的浓度可以使得涂层的总厚度增加,但过高或过低的浓度都会导致致密层厚度的减薄.当浓度为20g/L时,所制备的涂层的成分以氧化铝为主;当浓度为40g/L时,涂层的成分主要是莫来石和氧化铝;当浓度超过60g/L时,涂层的成分主要为非晶相.EIS的研究表明,涂层耐腐蚀性取决于涂层中的致密层,增加致密层的厚度可以提高PEO涂层的耐腐蚀性,在中性、酸性、碱性腐蚀介质中,PEO涂层都显示出对基体良好的保护作用.
Resumo:
The relationships between indentation responses and Young's modulus of an indented material were investigated by employing dimensional analysis and finite element method. Three representative tip bluntness geometries were introduced to describe the shape of a real Berkovich indenter. It was demonstrated that for each of these bluntness geometries, a set of approximate indentation relationships correlating the ratio of nominal hardness/reduced Young's modulus H (n) /E (r) and the ratio of elastic work/total work W (e)/W can be derived. Consequently, a method for Young's modulus measurement combined with its accuracy estimation was established on basis of these relationships. The effectiveness of this approach was verified by performing nanoindentation tests on S45C carbon steel and 6061 aluminum alloy and microindentation tests on aluminum single crystal, GCr15 bearing steel and fused silica.
Resumo:
采用等径角挤压技术对2A12铝合金在室温下进行挤压,成功制备了亚微米尺度的块体铝合金材料.挤压前材料的平均晶粒尺寸约5μm,两次挤压后,平均晶粒尺寸细化至200nm左右.合金中的Al2Cu相在挤压过程中由针状变成了块状颗粒,而Al2CuMg相在挤压过程中晶粒大小基本不变.研究发现,硬颗粒Al.2CuMg对基体α-Al有剪切和割裂作用,可以促进基体的晶粒细化过程,并初步给出了晶粒细化的模型.
Resumo:
The yield behaviour of two aluminum alloy foams (Alporas and Duocel) has been investigated for a range of axisymmetric compressive stress states. The initial yield surface has been measured, and the evolution of the yield surface has been explored for uniaxial and hydrostatic stress paths. It is found that the hydrostatic yield strength is of similar magnitude to the uniaxial yield strength. The yield surfaces are of quadratic shape in the stress space of mean stress versus effective stress, and evolve without corner formation. Two phenomenological isotropic constitutive models for the plastic behaviour are proposed. The first is based on a geometrically self-similar yield surface while the second is more complex and allows for a change in shape of the yield surface due to differential hardening along the hydrostatic and deviatoric axes. Good agreement is observed between the experimentally measured stress versus strain responses and the predictions of the models.
Resumo:
Light metal sandwich panel structures with cellular cores have attracted interest for multifunctional applications which exploit their high bend strength and impact energy absorption. This concept has been explored here using a model 6061-T6 aluminum alloy system fabricated by friction stir weld joining extruded sandwich panels with a triangular corrugated core. Micro-hardness and miniature tensile coupon testing revealed that friction stir welding reduced the strength and ductility in the welds and a narrow heat affected zone on either side of the weld by approximately 30%. Square, edge clamped sandwich panels and solid plates of equal mass per unit area were subjected to localized impulsive loading by the impact of explosively accelerated, water saturated, sand shells. The hydrodynamic load and impulse applied by the sand were gradually increased by reducing the stand-off distance between the test charge and panel surfaces. The sandwich panels suffered global bending and stretching, and localized core crushing. As the pressure applied by the sand increased, face sheet fracture by a combination of tensile stretching and shear-off occurred first at the two clamped edges of the panels that were parallel with the corrugation and weld direction. The plane of these fractures always lay within the heat affected zone of the longitudinal welds. For the most intensively loaded panels additional cracks occurred at the other clamped boundaries and in the center of the panel. To investigate the dynamic deformation and fracture processes, a particle-based method has been used to simulate the impulsive loading of the panels. This has been combined with a finite element analysis utilizing a modified Johnson-Cook constitutive relation and a Cockcroft-Latham fracture criterion that accounted for local variation in material properties. The fully coupled simulation approach enabled the relationships between the soil-explosive test charge design, panel geometry, spatially varying material properties and the panel's deformation and dynamic failure responses to be explored. This comprehensive study reveals the existence of a strong instability in the loading that results from changes in sand particle reflection during dynamic evolution of the panel's surface topology. Significant fluid-structure interaction effects are also discovered at the sample sides and corners due to changes of the sand reflection angle by the edge clamping system. © 2012 Elsevier Ltd. All rights reserved.
Resumo:
EPM seems to have good prospects for the future not only in the materials processing but also in environmental technologies by the help of superior features like contactless processing, clean heating and melting, and good controllability. In the present paper, the authors commentate on the possibility of EPM to avoid environmental issues of energy, resources and hazardous wastes by the use of the functions of Lorentz force and Joule heating. Firstly, the present situation and future trend of electric power generation is outlined, and then some examples of the application of EPM to environmental technologies are introduced, which have been performed by the author’s group. Examples are as follows: production of spherical solar cell from a liquid jet by using intermittent electromagnetic force; fabrication of semi-solid Al-Si slurry for die-casting of vehicle-parts to reduce the weight of vehicle; electromagnetic separation of nonmetallic inclusions from liquid Al scrap and its application to the fabrication of partially particle-reinforced aluminum alloy; electromagnetic melting of hazardous wastes from power plants to stabilize wastes in glass state.