Electrochemical corrosion behavior of cast Mg-Al-RE-Mn Alloys in NaCl solution

The electrochemical corrosion behavior of Mg-6Al-0.4Mn and Mg-6Al-4RE-0.4Mn (RE = Mischmetal) alloys is investigated in 3.5% NaCl solution. The results of corrosion process, polarization behavior, and electrochemical impedance spectroscopy of the alloys reveal that Mg-6Al-4RE-0.4Mn exhibits enhanced corrosion resistance. The addition of RE stabilizes the solid solution and modifies the passive film through a finer microstructure.

Phase Behavior and self-assembly of poly[N-vinylformamide-co-(acrylic acid)] copolymers under highly acidic conditions

Copolymers of N-vinylformamide and acrylic acid were synthesized by conventional aqueous free-radical polymerization. The phase behavior of the copolymer solutions was investigated through the addition of hydrochloric acid and the variation of the temperature. With a moderate content of N-vinylformamide, the copolymers showed complex phase behaviors. Under low-acidity conditions, a suspending liquid was formed, whereas under high-acidity conditions, the random copolymers could assemble into round nanoparticles with a broad particle size distribution.

Study on the Cell Structure and Compressive Behavior of Biodegradable Poly(epsilon-caprolactone) Foam

Biodegradable poly(e-caprolactone) (PCL) foams with a series of controlled structures were prepared by using chemical foaming method. The cell morphology was detected by scanning electron microscope (SEM). The compressive behavior of the foams was investigated by uniaxial compression test. The effect of density and structural parameters on the foam compressive behavior was analyzed. It was found that the relative compressive modulus has a power law relationship with relative density. Increasing of both the cell wall thickness and the cell density lead to higher compressive modulus of the foam; however, the cell size has no distinct effect on compressive behavior.

Investigation of Degradation Behavior of Polymer on Surface of Film Due to the Existence of Monochromatic X-ray

Degradation and its temperature dependence of poly(methyl methacrylate) (PMMA) in the blend film of PMMA/SAN were investigated via ire-situ X-ray photoelectron spectroscopy(XPS). The results show that thermal degradation of PMMA takes place at 185, 130, 80 degrees C and even room temperature due to the existence of monochromatic X-ray. Furthermore, the degradation rate depends crucially on the experiment temperature.

Unique electrochemiluminescence behavior of Ru(bpy)(3)(2+) in a gold/Nafion/Ru(bpy)(3)(2+) composite

The unique electrochemiluminescence (ECL) behavior of tris(bipyridine) ruthenium(II) (Ru(bpy)(3)(2+) immobilized in a gold/Nafion/Ru(bpy)(3)(2+) composite material was investigated. In this composite, the Ru(bpy)(3)(2+) ECL was found mainly occurred at 0-0.4 V during the cathodic scan process and the ECL peak was at about 0.1 V, which was quite different to the reported Ru(bpy)(3)(2+) ECL. Similar to the generally observed Ru(bpy)(3)(2+) ECL, the present ECL also could be enhanced by tri-n-propylarnine (TPA). It is also unique that in the presence of TPA, another ECL peak at about 0.38 V occurred.