Annealing effect on the surface morphology and photoluminescence of InGaAs/GaAs quantum dots grown by molecular beam epitaxy

Postgrowth rapid thermal annealing was performed on InGaAs/GaAs quantum dots grown by molecular beam epitaxy. The blue shift of the emission peak and the narrowing of the luminescence line width are observed at lower annealing temperature. However, when the annealing temperature is increased to 850 degrees C, the emission line width becomes larger. The TEM image of this sample shows that the surface becomes rough, and some large clusters are formed, which is due to the interdiffusion of In, Ga atoms at the InGaAs/GaAs interface and to the strain relaxation. The material is found to degrade dramatically when the annealing temperature is further increased to 900 degrees C, while emission from quantum dots can still be detected, along with the appearance of the emission from excited state. (C) 2000 Elsevier Science B.V. All rights reserved.

Growth and characterization of strained superlattices delta-GaNxAs1-x/GaAs by molecular beam epitaxy

A series of superlattices delta-GaNxAs1-x/GaAs were grown by a DC plasma-N-2-assisted molecular beam epitaxy. The evolution of the surface reconstruction during the growth has been studied with the use of in situ reflection high-energy electron diffraction. The superlattices have been characterized by high-resolution X-ray diffraction measurements. Distinct satellite peaks indicate that the superlattices are of good quality. The N compositions in strained GaNxAs1-x monolayers are obtained from the dynamical simulations of the measured X-ray diffraction patterns. The periodicity fluctuations of N composition are obtained from a kinematical method dependent on the broadening of the satellite peaks of the X-ray diffraction. (C) 2000 Elsevier Science B.V. All rights reserved.

Effect of arsenic precipitates on Fermi level in GaAs grown by molecular-beam epitaxy at low temperature

A simple model is presented to discuss the effect of As precipitates on the Fermi level in GaAs grown by molecular-beam epitaxy at low temperature (LT-GaAs). This model implements the compensation between point defects and the depletion of arsenic precipitates. The condition that the Fermi level is pinned by As precipitates is attained. The shifts of the Fermi level in LT-GaAs with annealing temperature are explained by our model. Additionally, the role of As precipitates in conventional semi-insulating GaAs is discussed. (C) 2000 American Institute of Physics. [S0021-8979(00)09905-9].

Doping during low-temperature growth of materials for n-p-n Si/SiGe/Si heterojuction bipolar transistor by gas source molecular beam epitaxy

In situ doping for growth of n-p-n Si/SiGe/Si heterojuction bipolar transistor (HBT) structural materials in Si gas source molecular beam epitaxy is investigated. We studied high n-type doping kinetics in Si growth using disilane and phosphine, and p-type doping in SiGe growth using disilane, soild-Ge, and diborane with an emphasis on the effect of Ge on B incorporation. Based on these results, in situ growth of n-p-n Si/SiGe/Si HBT device structure is demonstrated with designed structural and carrier profiles, as verified from characterizations by X-ray diffraction, and spreading resistance profiling analysis. (C) 2000 Elsevier Science B.V. All rights reserved.

Effects of rapid thermal annealing on the optical properties of GaNxAs1-x/GaAs single quantum well structure grown by molecular beam epitaxy

The effect of rapid thermal annealing (RTA) on the optical properties of GaNxAs1-x/GaAs strained single quantum well (SQW) was studied by low-temperature photoluminescence (PL). The GaNxAs1-x/GaAs SQW structures were prepared by dc active nitrogen plasma assisted molecular beam epitaxy. PL measurements on a series of samples with different well widths and nitrogen compositions were used to evaluate the effects of RTA. The annealing temperature and time were varied from 650 to 850 degrees C and 30 s to 15 min, respectively. Remarkable improvements of the optical properties of the samples were observed after RTA under optimum conditions. The interdiffusion constants have been calculated by taking into account error function diffusion and solving the Schrodinger equation. The estimated interdiffusion constants D are 10(-17)-10(-16) cm(2)/s for the earlier annealing conditions. Activation energies of 6-7 eV are obtained by fitting the temperature dependence of the interdiffusion constants. (C) 2000 American Institute of Physics. [S0021-8979(00)10401-3].