Intracellular copper/zinc superoxide dismutase from bay scallop Argopecten irradians: Its gene structure, mRNA expression and recombinant protein

Superoxide dismutases are an ubiquitous family of enzymes that function to efficiently catalyze the dismutation of superoxide anions. Two unique and highly compartmentalized bay scallop Argopecten irradians superoxide dismutases: MnSOD and ecCuZnSOD, have been molecularly characterized in our previous study. To complete characterize the SOD family in A. irradians, a novel intracellular copper/zinc SOD from the A. irradians (Ai-icCuZnSOD) was obtained and characterized. The full-length cDNA of Ai-icCuZnSOD was 1047 bp with a 459 bp open reading frame encoding 152 amino acids. The genomic length of the Ai-icCuZnSOD gene was about 4279 bp containing 4 exons and 3 introns. The promoter region containing many putative transcription factor binding sites were analyzed. Furthermore, quantitative reverse transcriptase real-time PCR (qRT-PCR) analysis indicated that the highest expression of the Ai-icCuZnSOD was detected in gill and the expression profiles in hemocytes of bay scallops challenged with bacteria Vibrio anguillarum and lipopolysaccharide (LPS) were different. The result presented an increased expression after injection with LPS whereas no significant changes were observed after V. anguillarum injection. A fusion protein containing Ai-icCuZnSOD was produced in vitro. The rAi-icCuZnSOD is a stable enzyme, retaining more than 80% of its activity between 10 and 60 degrees C and keeping above 88% of its activity at pH values between 5.8 and 9. Ai-icCuZnSOD is more stable under alkaline than acidic conditions. Crown Copyright (C) 2009 Published by Elsevier Ltd. All rights reserved.

Corrosion behaviour of hot dip zinc and zinc-aluminium coatings on steel in seawater

A comparative investigation of hot dip Zn-25Al alloy, Zn-55Al-Si and Zn coatings on steel was performed with attention to their corrosion performance in seawater. The results of 2-year exposure testing of these at Zhoushan test site are reported here. In tidal and immersion environments, Zn-25Al alloy coating is several times more durable than zinc coating of double thickness. At long exposure times, corrosion rate for the Zn-25Al alloy coating remains indistinguishable from that for the Zn-55Al-Si coating of similar thickness in tidal zone, and is two to three times lower than the latter in immersion zone. The decrease in tensile strength suggested that galvanized and Zn-55Al-Si coated steel suffer intense pitting corrosion in immersion zone. The electrochemical tests showed that all these coatings provide cathodic protection to the substrate metal; the galvanic potentials are equal to - 1,050, - 1,025 and - 880 mV (SCE) for zinc, Zn-25Al alloy and Zn-55Al-Si coating, respectively, which are adequate to keep the steel inside the immunity region. It is believed that the superior performance of the Zn-25Al alloy coating is due to its optimal combination of the uniform corrosion resistance and pitting corrosion resistance. The inferior corrosion performance by comparison of the Zn coating mainly results from its larger dissolution rate, while the failure of the Zn-55Al-Si coating is probably related to its higher susceptibility to pitting corrosion in seawater.

Triaqua(benzene-1,2-dicarboxylato-kO)-(1,10-phenanthroline-k(2)N,N ')zinc(II) monohydrate

The structure of the title compound, [Zn(C8H4O4)(C12H8N2)-(H2O)(3)]center dot H2O, displays a distorted octahedral coordination geometry, with two N atoms from the bidentate phenanthroline ligand, three O atoms from three meridional H2O molecules and one O atom from the monodentate phthalate ion.