Weathering degradation of polyester and polypropylene geotextiles

This paper presents results of physical and mechanical tests in polyester (PET) and polypropilene (PP) nonwoven geotextiles that were exposed to weathering conditions (solar radiation, humidity, wind, rain) after some specific periods of exposure (1, 2, 3 and 4 months). ASTM D5970 and Brazilian standards (NBR) recommendation were followed in this research. Results show variations in tensile properties and in the mass per unit area. Variations in the deformations were more significant in the PP geotextile when compared to the PET geotextile.

UV exposure of polymeric geomembranes

The break of polymer chemical bonds may occur due to penetration of sun short wavelengths. In sanitary landfills for instance, ultraviolet radiation affects uncovered materials and can be dangerous during the installation of the liner and before the placement of the waste. Only the ultraviolet part of the light is harmful to the geosynthetic materials, moreover, each material is sensitive to a particular wavelength. This article evaluates the effects of UV degradation and condensation in black HDPE (1.0 and 1.5 mm) and white HDPE (textured - 1.0 mm) geomembrane that were tested in laboratory during 6 months. The tests were performed using a weatherometer assembled at EESC-USP in accordance to ASTM G154. The results have shown variations in punction and tear resistance after each period of exposure.

Evaluation of geomembrane UV degradation using melt flow index and oxidative induction time tests

Many factors such as the sunlight, intensity of radiation, temperature, and moisture may influence the degradation process of geosynthetics. UV stabilizers are used especially in polyolefin geomembrane to prevent the degradation process. In these geomembranes the service lifetime is initially governed by the consumption of antioxidants. Tests like MFI and OIT are a alternative to detect the oxidative degradation in polyolefins. This article evaluates HDPE geomembrane degradation after UV exposure through the results of MFI and OIT tests. Two kinds of geomembranes were evaluated: a black and smooth (0.8, 1.0, 1.5, 2.5 mm) and a white and textured (1.0 mm). MFI test showed some levels of superficial degradation (crosslink) in HDPE geomembrane.

Degradation of [D-Leu]-Microcystin-LR by solar heterogeneous photocatalysis (TiO2)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

A comparative study of the non-isothermal degradation of natural rubber from Mangabeira (Hancornia speciosa Gomes) and Seringueira (Hevea brasiliensis)

Due to the increasing search for alternative sources of natural rubber (NR) whose properties are similar to Hevea brasiliesis, several sources have been studied in the past few years. Among them, Mangabeira (Hancornia speciosa Gomes), which is native to Amazon rainforest and other regions of Brazil, has a potential as another viable rubber source. As a continuation of a series of comparative studies between Hancornia and Hevea (clone RRIM 600) these two species by our research team, their thermal behavior was analyzed by thermogravimetry (TG) using Flynn-Wall-Ozawa's approach in order to obtain kinetic parameters (reaction order, pre-exponential factor and activation energy) of the decomposition process. Results indicated that the thermal behavior of NR from Hancornia was comparable to Hevea with some differences observed as follows: reaction order for Hancornia was higher than for Hevea at the beginning of degradation and very close for temperatures over 350 A degrees C; activation energy and pre-exponential factor had the same trend, i.e., increased with increasing degree of conversion remaining almost constant between 20 and 70% and then increasing for higher degrees, although Hevea was slightly more thermally stable than Hancornia. These major influences in the degradation process in the early stage are attributed to differences in non-rubber constituents present in these two species.

Effects of cyclosporin, phenytoin, and nifedipine on the synthesis and degradation of gingival collagen in tufted capuchin monkeys (Cebus apella): Histochemical and MMP-1 and -2 and collagen I gene expression analyses

Background: The purpose of this experimental study was to evaluate the collagen fiber distribution histologically after phenytoin, cyclosporin, or nifedipine therapy and to correlate it with collagen I and matrix metalloproteinase (MMP)-1 and -2 gene expression levels.Methods: Gingival samples from the canine area were obtained from 12 male monkeys (Cebus apella). The mesial part of each sample was assessed by reverse transcription-polymerase chain reaction, whereas the distal part was processed histologically for picrosirius red and hematoxylin and eosin stainings, as well as for collagen IV immunostaining. One week after the first biopsy, the animals were assigned to three groups that received daily oral dosages of cyclosporin, phenytoin, or nifedipine for 120 days. Additional gingival samples were obtained on days 52 and 120 of treatment from two animals from each group on the opposite sides from the first biopsies.Results: Picrosirius red staining showed a predominance of mature collagen fibers in the control group. Conversely, there was an enlargement of areas occupied by immature collagen fibers in all groups at days 52 and 120, which was not uniform over each section. There was a general trend to lower levels of MMP-1 gene expression on day 52 and increased levels on day 120. Phenytoin led to increased levels of MMP-2 and collagen I gene expression on day 120, whereas the opposite was observed in the nifedipine group.Conclusion: Cyclosporin, phenytoin, and nifedipine led to phased and drug-related gene expression patterns, resulting in impaired collagen metabolism, despite the lack of prominent clinical signs.

COLOR STABILITY of SEALED COMPOSITE RESIN RESTORATIVE MATERIALS AFTER ULTRAVIOLET ARTIFICIAL AGING and IMMERSION IN STAINING SOLUTIONS

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of addition of pigments and opacifier on the hardness, absorption, solubility and surface degradation of facial silicone after artificial ageing

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)