A simple and low-cost method for the preparation of self-supported TiO2-WO3 ceramic heterojunction wafers

Robust, bilayer heterojunction photodiodes of TiO₂-WO₃ were prepared successfully by a simple, low-cost powder pressing technique followed by heat-treatment. Exclusive photoirradiation of the TiO₂ side of the photodiode resulted in a rapid colour change (dark blue) on the WO₃ surface as a result of reduction of W⁶⁺ to W⁵⁺ (confirmed by X-ray photoelectron spectroscopy). This colour was long lived and shown to be stable in a dry environment in air for several hours. A similar photoirradiation experiment in the presence of a mask showed that charge transfer across the heterojunction occurred approximately normal to the TiO₂ surface, with little smearing out of the mask image. As a result of the highly efficient vectorial charge separation, the photodiodes showed a tremendous increase in photocatalytic activity for the degradation of stearic acid, compared to wafers of the respective individual materials when tested separately.

WC/CNT, WC/CNT/Pt Composite Material and Preparation Process Therefor and Use Thereof. (International Patent)

(EN)Disclosed are a WC/CNT， WC/CNT/Pt composite material and a preparation process therefor and use thereof. The WC/CNT/Pt composite material comprises mesoporous spherical tungsten carbide with a diameter of 1-5 microns, carbon nanotubes and platinum nano particles, with the carbon nanotubes growing on the surface of the mesoporous spherical tungsten carbide and expanding outward, and the platinum nano particles growing on the surfaces of the mesoporous spherical tungsten carbide and carbon nanotubes. The WC/CNT composite material comprises mesoporous spherical tungsten carbide with a diameter of 1-5 microns, and carbon nanotubes, with the carbon nanotubes growing on the surface of the mesoporous spherical tungsten carbide and expanding outward. The WC/CNT/Pt composite material of the present invention can be used as an electro-catalyst in a methanol flue battery, significantly improving the catalytic conversion rate and the service life of the catalyst. The WC/CNT composite material can be used as an electro-catalyst in the electro-reduction of a nitro aromatic compound, significantly improving the efficiency of organic electro-synthesis.

WC/CNT, WC/CNT/Pt Composite Material and Preparation Process Therefor and Use Thereof. (US patent)

Disclosed are a WC/CNT， WC/CNT/Pt composite material and a preparation process therefor and use thereof. The WC/CNT/Pt composite material comprises mesoporous spherical tungsten carbide with a diameter of 1-5 microns, carbon nanotubes and platinum nano particles, with the carbon nanotubes growing on the surface of the mesoporous spherical tungsten carbide and expanding outward, and the platinum nano particles growing on the surfaces of the mesoporous spherical tungsten carbide and carbon nanotubes. The WC/CNT composite material comprises mesoporous spherical tungsten carbide with a diameter of 1-5 microns, and carbon nanotubes, with the carbon nanotubes growing on the surface of the mesoporous spherical tungsten carbide and expanding outward. The WC/CNT/Pt composite material of the present invention can be used as an electro-catalyst in a methanol flue battery, significantly improving the catalytic conversion rate and the service life of the catalyst. The WC/CNT composite material can be used as an electro-catalyst in the electro-reduction of a nitro aromatic compound, significantly improving the efficiency of organic electro-synthesis.

Mechanochemical preparation of Ag catalysts for the n-octane-SCR de-NOx reaction: Structural and reactivity effects

Mechanochemical preparation of Ag/Al2O3 catalysts used for the selective catalytic reduction of NOx using hydrocarbons has been shown to substantially increase the activity of the catalyst in comparison with Ag/Al2O3 prepared by wet impregnation. The effect of using different ball-milling experimental parameters on both the structure of the material as well as the catalyst activity has been investigated and the optimum conditions established. A phase transition from γ- to α-alumina was observed milling at high speeds which was found to result in lower catalyst activities. At lower milling speeds both fracturing and agglomeration of the alumina support can be observed depending on the grinding time. However, due to ball-milling, a general enhancement in the NOx reduction activity was observed for all catalysts compared with the conventionally prepared catalysts irrespective of the reductant used. Transient DRIFTS-MS experiments were performed to investigate the effect of H2 in the absence and presence of water on the SCR reaction over catalysts prepared by both ball milling and wet impregnation. In-situ DRIFTS-MS analysis revealed significant differences in both gas phase and surface species. Most notably, isocyanate species were formed significantly more quickly and at higher surface concentration in the case of the mechanochemically prepared catalyst.

Microwave-Assisted Preparation of Hydrogel-Forming Microneedle Arrays for Transdermal Drug Delivery Applications

A microwave (MW)-assisted crosslinking process to prepare hydrogel-forming microneedle (MN) arrays was evaluated. Conventionally, such MN arrays are prepared using processes that includes a thermal crosslinking step. Polymeric MN arrays were prepared using poly(methyl vinyl ether-alt-maleic acid) crosslinked by reaction with poly(ethylene glycol) over 24 h at 80 °C. Polymeric MN arrays were prepared to compare conventional process with the novel MW-assisted crosslinking method. Infrared spectroscopy was used to evaluate the crosslinking degree, evaluating the area of the carbonyl peaks (2000–1500 cm−1). It was shown that, by using the MW-assisted process, MN with a similar crosslinking degree to those prepared conventionally can be obtained in only 45 min. The effects of the crosslinking process on the properties of these materials were also evaluated. For this purpose swelling kinetics, mechanical characterisation, and insertion studies were performed. The results suggest that MN arrays prepared using the MW assisted process had equivalent properties to those prepared conventionally but can be produced 30 times faster. Finally, an in vitro caffeine permeation across excised porcine skin was performed using conventional and MW-prepared MN arrays. The release profiles obtained can be considered equivalent, delivering in both cases 3000–3500 μg of caffeine after 24 h.

Synthesis by extrusion: continuous, large-scale preparation of MOFs using little or no solvent

Grinding solid reagents under solvent-free or low-solvent conditions (mechanochemistry) is emerging as a general synthetic technique which is an alternative to conventional solvent-intensive methods. However, it is essential to find ways to scale-up this type of synthesis if its promise of cleaner manufacturing is to be realised. Here, we demonstrate the use of twin screw and single screw extruders for the continuous synthesis of various metal complexes, including Ni(salen), Ni(NCS)(2)(PPh3)(2) as well as the commercially important metal organic frameworks (MOFs) Cu-3(BTC)(2) (HKUST-1), Zn(2-methylimidazolate)(2) (ZIF-8, MAF-4) and Al(fumarate)(OH). Notably, Al(fumarate)(OH) has not previously been synthesised mechanochemically. Quantitative conversions occur to give products at kg h(-1) rates which, after activation, exhibit surface areas and pore volumes equivalent to those of materials produced by conventional solvent-based methods. Some reactions can be performed either under completely solvent-free conditions whereas others require the addition of small amounts of solvent (typically 3-4 mol equivalents). Continuous neat melt phase synthesis is also successfully demonstrated by both twin screw and single screw extrusion for ZIF-8. The latter technique provided ZIF-8 at 4 kg h(-1). The space time yields (STYs) for these methods of up to 144 x 10(3) kg per m(3) per day are orders of magnitude greater than STYs for other methods of making MOFs. Extrusion methods clearly enable scaling of mechanochemical and melt phase synthesis under solvent-free or low-solvent conditions, and may also be applied in synthesis more generally.