Effect of airborne particle abrasion protocols on surface topography of Y-TZP ceramic

This study aimed to evaluate Y-TZP surface after different airborne particle abrasion protocols. Seventy-six Y-TZP ceramic blocks (5×4×4) mm3 were sintered and polished. Specimens were randomly divided into 19 groups (n=4) according to control group and 3 factors: a) protocol duration (2 and 4 s); b) particle size (30 μm, alumina coated silica particle; 45 μm, alumina particle; and 145 μm, alumina particle) and; c) pressure (1.5, 2.5 and 4.5 bar). Airborne particle abrasion was performed following a strict protocol. For qualitative and quantitative results, topography surfaces were analyzed in a digital optical profilometer (Interference Microscopic), using different roughness parameters (Ra, Rq, Rz, X-crossing, Mr1, Mr2 and Sdr) and 3D images. Surface roughness also was analyzed following the primer and silane applications on Y-TZP surfaces. One-way ANOVA revealed that treatments (application period, particle size and pressure of particle blasting) provided significant difference for all roughness parameters. The Tukey test determined that the significant differences between groups were different among roughness parameters. In qualitative analysis, the bonding agent application reduced roughness, filing the valleys in the surface. The protocols performed in this study verified that application period, particle size and pressure influenced the topographic pattern and amplitude of roughness.

Development of silicon carbide substrates for aerospace applications

Payload and high-tech are important characteristics when the goals are aerospace applications. The development of the technologies associated to these applications has interests that transcend national boundaries and are of strategic importance to the nations. Ultra lightweight mirrors, supports and structures for optical systems are important part of this subject. This paper reports the development of SiC substrates, obtained by pressing, to be applied on embedded precision reflective optics. Different SiC granulometries, having YAG as sintering additive, were processed by: ball milling, drying and deagglomeration, sift, uniaxial and isostatic pressing, and, finally, argon atmosphere sintering at 1900°C. Different porosities were obtained according to the amount of organic material added. Into one side of the samples pellets of organic material were introduced to generate voids to reduce the weight of samples as a whole. The substrates were grinding and polished, looking for a SiC surface having low porosity, as porosity is directly related to light scattering that should be avoided on optical surfaces. Laser surface treatments were applied (using or not SiC barbotine) as a method to improve the surface quality. The samples were characterized by optical and laser confocal microscopy, roughness measurements and mechanical tests. The results are very promissory for future applications. © 2012 Materials Research Society.

Influence of optimized lubrication-cooling and minimum quantity lubrication on the cutting forces, on the geometric quality of the surfaces and on the micro-structural integrity of hardened steel parts

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

CO 2 adsorption on polar surfaces of ZnO

Physical and chemical adsorption of CO 2 on ZnO surfaces were studied by means of two different implementations of periodic density functional theory. Adsorption energies were computed and compared to values in the literature. In particular, it was found that the calculated equilibrium structure and internuclear distances are in agreement with previous work. CO 2 adsorption was analyzed by inspection of the density of states and electron localization function. Valence bands, band gap and final states of adsorbed CO 2 were investigated and the effect of atomic displacements analyzed. The partial density of states (PDOS) of chemical adsorption of CO 2 on the ZnO(0001) surface show that the p orbitals of CO 2 were mixed with the ZnO valence band state appearing at the top of the valence band and in regions of low-energy conduction band. [Figure not available: see fulltext.] © 2012 Springer-Verlag Berlin Heidelberg.

Shellac and hydroxyapatitte coatings on titanium niobium and AISI 316L steel surfaces produced by dip-coating

Shellac is a natural resin used for the preservation of fruits, bones and as a coating on drugs. The hydroxyapatite (HA), which is naturally found in human bones, is used as filler to substitute amputated bone or as a coating for prosthetics, promoting bone growth in implants of prostheses. The objective of this work is to immobilize HA from an alcoholic solution of shellac on plates of titanium, niobium and AISI 316L steel using the simple dip-coating method. The corrosion resistance of the uncoated films is compared with ones coated with shellac and shellac plus HA. The deterioration of the film composed of shellac with hydroxyapatite in saline solution follows the ascending order: AISI 316L steel, titanium, niobium. The elemental analysis of the shellac showed that it mainly consists of the elements C, H, N and O. We used the FT-IR spectrum to characterize the shellac and HA. ©The Electrochemical Society.

The effect of laminin-1-doped nanoroughened implant surfaces: Gene expression and morphological evaluation

Aim. This study aimed to observe the morphological and molecular effect of laminin-1 doping to nanostructured implant surfaces in a rabbit model. Materials and Methods. Nanostructured implants were coated with laminin-1 (test; dilution, 100 g/mL) and inserted into the rabbit tibiae. Noncoated implants were used as controls. After 2 weeks of healing, the implants were removed and subjected to morphological analysis using scanning electron microscopy (SEM) and gene expression analysis using the real-time reverse transcriptase-polymerase chain reaction (RT-PCR). Results. SEM revealed bony tissue attachment for both control and test implants. Real-time RT-PCR analysis showed that the expression of osteoblast markers RUNX-2, osteocalcin, alkaline phosphatase, and collagen I was higher (1.62-fold, 1.53-fold, 1.97-fold, and 1.04-fold, resp.) for the implants modified by laminin-1 relative to the control. All osteoclast markers investigated in the study presented higher expression on the test implants than controls as follows: tartrate-resistant acid phosphatase (1.67-fold), calcitonin receptor (1.35-fold), and ATPase (1.25-fold). The test implants demonstrated higher expression of inflammatory markers interleukin-10 (1.53-fold) and tumour necrosis factor-α (1.61-fold) relative to controls. Conclusion. The protein-doped surface showed higher gene expression of typical genes involved in the osseointegration cascade than the control surface. © 2012 Humberto Osvaldo Schwartz-Filho et al.

In vitro assessment of dentin erosion after immersion in acidic beverages: Surface profile analysis and energy-dispersive X-ray fluorescence spectrometry study

The aim of this study was to investigate the effects of some acidic drinks on dentin erosion, using methods of surface profile (SP) analysis and energy-dispersive X-ray fluorescence spectrometry (EDXRF). One hundred standardized dentin slabs obtained from bovine incisor roots were used. Dentin slabs measuring 5x5 mm were ground flat, polished and half of each specimen surface was protected with nail polish. For 60 min, the dentin surfaces were immersed in 50 mL of 5 different drinks (Gatorade®, Del Valle Mais orange juice®, Coca-Cola®, Red Bull® and white wine), 20 blocks in each drink. The pH of each beverage was measured. After the erosive challenge, the nail polish was removed and SP was analyzed. The mineral concentration of dentin surfaces was determined by means of EDXRF. Data were analyzed statistically by ANOVA and Tukey's test (α=0.05). SP analysis showed that Red-Bull had the highest erosive potential (p<0.05). EDXRF results exhibited a decrease in phosphate in the groups immersed in Red-Bull, orange juice and white wine (p<0.05), and no significant difference in calcium content between the reference surface and eroded surface. In conclusion, this study demonstrated that all studied beverages promoted erosion on root dentin and Red Bull had the highest erosive potential. There was no correlation between pH of beverages and their erosive potential and only the P content changed after erosive challenge.