Surface roughness analysis of dental ceramics treated with hydrofl uoric acid and aluminum oxide jet

The aim of this study was to evaluate the surface roughness of 5 indirect restorative materials treated with hydrofluoric acid to 10%, with aluminum oxide jet and a combination of both. The specimens was prepared with 10 mm in diameter and 2 mm thickness, divided into fi ve groups: (1) Ceromer (CeseadII-Kuraray), (2) Leucite crystals ceramics (IPS EmpressIIIvoclarforcasket), (3) glass ceramic with fluorapatite (IPS D. Sign-Ivoclar), (4) lithium disilicate ceramic (IPS Empress II-Ivoclar restorations), (5) ceramics (Cergogold-Degussa). For all groups were performed the controls, and the surfaces with the 3 types of treatment. For testing roughness used the rugosimeter Taylor/Hobson-Precision, model form tracerSV-C525 high sensitivity. After confi rmation of variance analysis with a signifi cance level of 1% (p < 0.01), there was equality between the average roughness of materials from groups 1, 3 and 5, and the group 2 was different from the others. It was also found that the ceramics of the group 5 behaved similar to group 4. However the lowest average roughness was observed in group 2 ceramic. In the evaluation between the types of treatment, the aluminum oxide jet and associations and blasting with hydrofl uoric acid were similar, and different isolated hydrofl uoric acid, and 3 types of treatment signifi cantly higher than the control group. All treatments promoted superfi cial alterations in all tested materials.

In vitro study of staining agents effects on optical properties of esthetic restorative materials

The authors have studied the effect of four staining agents on the optical properties of esthetic restorative materials through translucency tests. Two commercial brands of composite resins were used: Point 4 (Kerr) and Charisma (Heraeus-Kulzer). The liquids tested were: wine, cola, chlorhexidine solution and nicotine solution. The translucency was measured at different periods of time: P0 – before immersion (baseline), P1 - 1 h after immersion, P2 - 2 h after immersion and successively, P3 – 24 h after immersion up to a period of 7 weeks. ANOVA statistical analysis was applied to the data (p < 0.05). The results lead to the following conclusions: (1) Composite resins submitted to the tested immersion mediums were stained, (2) the lower percentage of translucency was observed for nicotine containing solution, (3) The percentage of translucency decreased with the period of immersion.