Low Temperature Properties of PI/SiO_2 Nanocomposite Films

In this paper, the mechanical properties of PI/Si_O, nanocomposite hybrid films with different silica doping levels are experimentally studied at low temperature. Experimental results show that the coefficient of thermal expansion (CTE) of the PI/Si_O, nanocomposite hybrid films gradually reduces when the ambiance temperature is decreased. At the liquid nitrogen temperature (77 K), the CTE value is about five times less than that at room temperature (287 K). The measured CTEs of hybrid films greatly decrease when doped with inorganic silica, especially when the silica doping level is more than 1 wt.%. However, too high silica contents (more than 10 wt.%) can cause problem to disperse effectively and the specimens become quite opaque. Experimental results also show that the effects of the pre-applied stress levels can be neglected on the CTE testing. When the ambient temperature changes from 287 to 77 K, the measured average values of the films' ultimate tensile strength (UTS) and Young's modulus increase about 60 and 90%, respectively, while the breaking elongation decreases about 42%.

Fabrication and bio-functionalization of tetrahedral amorphous carbon thin films for bio sensor applications

Tetrahedral amorphous carbon (ta-C) thin films are a promising material for use as biocompatible interfaces in applications such as in-vivo biosensors. However, the functionalization of ta-C film surface, which is a pre-requisite for biosensors, remains a big challenge due to its chemical inertness. We have investigated the bio-functionalization of ta-C films fabricated under specific physical conditions through the covalent attachment of functional biomolecular probes of peptide nucleic acid (PNA) to ta-C films, and the effect of fabrication conditions on the bio-functionalization. The study showed that the functional bimolecular probes such as protected long-chain ω-unsaturated amine (TFAAD) can be covalently attached to the ta-C surface through a well-defined structure. With the given fabrication process, electrochemical methods can be applied to the detection of biomolecular interaction, which establishes the basis for the development of stable, label-free biosensors. © 2011 Elsevier B.V. All rights reserved.

The Nonlinear Phenomena Of Thin Polydimethylsiloxane (Pdms) Films In Electrowetting

Electrowetting (EW) is an effective way to manipulate small volume liquid in micro- and nano-devices, for it can improve its wettability. Since the late 1990s, electrowetting-on-dielectric (EWOD) has been used widely in bio-MEMS, lab-on-a-chip, etc. Polydimethlsiloxane (PDMS) is extensively utilized as base materials in the fabrication of biomedical micro- and nano-devices. The properties of thin PDMS films used as dielectric layer in EW are studied in this paper. The experimental results show that the thin PDMS films exhibit good properties in EWOD. As to PDMS films with different thicknesses, a threshold voltage and a hysteresis were observed in the EIWOD experiments.

Piezoelectricity Of Zno Films Prepared By Sol-Gel Method

ZnO piezoelectric thin films were prepared on crystal substrate Si(111) by sol-gel technology, then characterized by scanning electron microscopy, X-ray diffraction and atomic force microscopy (AFM). The ZnO films characterized by X-ray diffraction are highly oriented in (002) direction with the growing of the film thickness. The morphologies, roughness and grain size of ZnO film investigated by AFM show that roughness and grain size of ZnO piezoelectric films decrease with the increase of the film thickness. The roughness dimension is 2.188-0.914 nm. The piezoelectric coefficient d(33) was investigated with a piezo-response force microscope (PFM). The results show that the piezoelectric coefficient increases with the increase of thickness and (002) orientation. When the force reference is close to surface roughness of the films, the piezoelectric coefficient measured is inaccurate and fluctuates in a large range, but when the force reference is big, the piezoelectric coefficient d(33) changes little and ultimately keeps constant at a low frequency.