Magnetically separable mesoporous Fe3O4/silica catalysts with very low Fe3O4 content

Two magnetically separable Fe3O4/SiO2 (aerogel and MSU-X) composites with very low Fe3O4 content (<1 wt%) have been successfully prepared at room temperature by co-condensation of MPTES-functionalized Fe3O4 nanoparticles (NPs) with a silicon alkoxide. This procedure yields a homogeneous incorporation of the Fe3O4 NPs on silica supports, leading to magnetic composites that can be easily recovered using an external magnetic field, despite their very low Fe3O4 NPs content (ca. 1 wt%). These novel hybrid Fe3O4/SiO2 materials have been tested for the oxidation reaction of 3,3′,5,5′-tetramethylbenzidine (TMB) with hydrogen peroxide showing an enhancement of the stability of the NPs in the Fe3O4/silica aerogel as compared to the Fe3O4 NPs alone, even after five catalytic cycles, no leaching or agglomeration of the Fe3O4/SiO2 systems.

Hybrid magnetic graphitic nanocomposites for catalytic wet peroxide oxidation applications

Hybrid magnetic graphitic nanocomposites (MGNC) prepared by inclusion of magnetite nanoparticles (obtained by coprecipitation) into an organic-organic self-assembly system, followed by calcination, revealed high activity for the catalytic wet peroxide oxidation (CWPO) of 4-nitrophenol solutions (5 g L-l), with pollutant removais up to 1245 mg g-' h-l being obtained when considering the mass ratio [pollutant]/[catalyst] =10. The stability of the MGNC catalyst against metal leaching was ascribed to the confinement effect of the carbon based material. These observations, together with the magnetically recoverable characteristics of MGNC, open new prospects for the wide use of this catalyst in highly efficient CWPO applications.

Core-shell nanocomposites prepared by hierarchical co-assembly: the role of the carbon shell in catalytic wet peroxide oxidation processes

The diffraction pattern of Fe3O4 (not shown) confirmed the presence of only one phase, corresponding to magnetite with a lattice parameter a = 8.357 Å and a crystallite size of 16.6 ± 0.2 nm. The diffraction pattern of MGNC (not shown) confirmed the presence of a graphitic phase, in addition to the metal phase, suggesting that Fe3O4 nanoparticles were successfully encapsulated within a graphitic structure during the synthesis of MGNC. The core-shell structure of MGNC is unequivocally demonstrated in the TEM micrograph shown in Fig. 1b. Characterization of the MGNC textural and surface chemical properties revealed: (i) stability up to 400 oC under oxidizing atmosphere; (ii) 27.3 wt.% of ashes (corresponding to the mass fraction of Fe3O4); (iii) a micro-mesoporous structure with a fairly well developed specific surface area (SBET = 330 m2 g-1); and (iv) neutral character (pHPZC = 7.1). In addition, the magnetic nature of MGNC (Fig. 2) is an additional advantage for possible implementation of in situ magnetic separation systems for catalyst recovery.