Análise da reversão do fundo de latas de alumínio para bebidas - Buckle

This work approaches the main methods of plastic deformation of metals, with a focus on the deep drawing process. The mechanical properties were evaluated with the tension tests. It is presented the aluminum alloys designation, followed by applying heat treatments and the designation of tempers. The manufacture of aluminum beverage cans is described step by step, in general terms. The main objective is to analyze how different cans background geometries have great influence on the dome reversal. To be able to achieve the goal it was necessary to use cans of different manufacturers, which were used in buckle tests to obtain the reversal pressures, tensile tests and geometric analysis. Finally empirical equations were obtained correlating these variables, and it was observed that the conformation of reforming change significantly it's behavior

Caracterização do fator de intensidade de tensão em corpos trincados através do método dos elementos finitos

The industry generally has sought materials with high mechanical resistance, low density, thermal stability and corrosion resistance. In the aerospace industry, for example, the use of aluminum alloys, such as Al 2024-T351 and Al 7075-T7351, have become essential. However, the use of these materials often do not resulted in a satisfactory performance of the component, since the presence of cracks can cause total rupture of the component, even with a tension below the yield stress of the material, unexpectedly. In this work, these aluminum alloys were analyzed and samples were modeled by the finite element method. Moreover, in the models were applied two different types of cracks, central and edge crack, a vertical force was applied to result in a tension 70% of the yield stress of the material analyzed. Through stress asymptotic distribution in the region near the crack tip were calculated the values of the stress intensity factors for each crack length, after the stress intensity factors characterized were compared graphically with the values of fracture toughness found in the available literature

Estudo da fadiga em liga de alumínio aeronáutico 7475-T761

This work will address the study of fatigue conditions with constant load in an alloy of aluminum analysis 7475 - T761, so we can better understand the conditions of the aircrafts which contain this alloy in their structures. A literature review, which was discussed the concepts of fracture mechanics, fatigue, aeronautical components, chemical analysis of aluminum alloys, fatigue problems that appears in the aircrafts, metallographic analysis, and testing of optical microscopy tensile, fatigue and microhardness, surface analysis (MEV) study of the chemical composition of the alloy in question, the main causes of crashes, was performed, completing the work, analysis of data from tensile test, hardness and fatigue together with the interpretation of images of optical microscopy and scanning electron was taken. The data indicated the high mechanical strength of the alloy, along with its microstructure indicating elongated grains and high surface contour, which shows such resistance by hindering the movement of dislocations. The grooves are clearly shown in the MEV images as well as the classic with increased fatigue loading and subsequent reduction of the number of cycles to rupture behavior shown in the graphs. Therefore we observed the optimal behavior is supported by the league when subjected to fatigue loadings