Artificial Pinning Center Studies in BI2212 Tapes and Bulks With Zirconium Oxide Inclusion

Zirconium oxide inclusion in Bi2212 superconducting tapes and bulks was studied as possible artificial pinning centers (APC). In order to analyze the zirconium oxide APC addition in Bi2212 samples, magnetization measurements were performed in bulks and transport properties measurements were performed on tapes. In magnetization measurements, the critical current densities are proportional to the width of the magnetization loop at each applied magnetic field. Addition of ZrO(2) in Bi2212 superconductors broadened the magnetization loop and enhanced the critical current densities at 4.2 K in bulks, as a clear indication that ZrO(2) addition improved the pinning and acted as APCs. In contrast, the transport critical current densities decreased in tapes.

Laboratory and mill scale evaluation of biopulping of Eucalyptus grandis Hill ex Maiden with Phanerochaete chrysosporium RP-78 under non-aseptic conditions

Biopulping of Eucalyptus grandis wood chips with Phanerochaete chrysosporium RP-78 was evaluated under non-aseptic conditions in laboratory and mill wood-yard. The ability of P. chrysosporium to compete with indigenous fungi present in fresh wood chips was notorious under controlled laboratory experiments. A subsequent step involved an industrial test performed with 10-ton of fresh wood chips inoculated and maintained at 37 +/- 38 degrees C for 39 days in a biopulping pilot plant. Biotreated wood chips were pulped in a chemithermomechanical pulping mill. Net energy consumption during refining was 745 kWh ton(-1) and 610 kWh ton(-1) of processed pulp for control and biotreated wood chips, respectively. Accordingly, 18.5% net energy saving could be achieved. Biopulps contained lower shive content and had improved strength properties compared to control pulps. Tensile index improved from 25 +/- 1 N m g(-1) to 33.6 +/- 0.5 N m g(-1) and delamination strength from 217 +/- 19 kPa to 295 +/- 30 kPa.