A comparison of the film thickness of two adhesive luting agents and the effect of thermocycling on their microTBs to feldspathic ceramic.

The aim of the present study was to evaluate the effect of thermocycling (TC) on the microtensile bond strength (microTBS) of two luting agents to feldspathic ceramic and to measure their film thickness (FT). For the microTBS test, sixteen blocks (6.4 x 6.4 x 4.8 mm) were fabricated using a feldspathic ceramic, etched with 10% hydrofluoric acid, rinsed and treated with the silane agent. The ceramic blocks were divided into two groups (n= 8): Gr1: dual-cured resin cement and Gr2: flowable resin. The luting agents were applied on the treated surfaces. Microsticks (1 +/-0. 1mm2) were prepared and stored under two conditions: dry, specimens immediately submitted to the microTBS test, and TC (6,000 cycles; 5 degrees C-55 degrees C). The microTBS was evaluated using a universal testing machine (1 mm/min). The microTBS data (MPa) were submitted to two-way ANOVA and Tukey' test (5%). For the FT test (ISO 4049), 0.05 ml of each luting agent (n=8) was pressed between two Mylar-covered glass plates (150 N) for 180 seconds and light polymerized. FT was measured using a digital paquimeter (Model 727-2001). The data (mm) were submitted to one-way ANOVA. The luting cement did not influence the microTBS results (p= 0.4467). Higher microtensile bond values were found after TC (20.5 +/- 8.6 MPa) compared to the dry condition (13.9 +/- 4. 7MPa), for both luting agents. The luting agents presented similar film thicknesses: Gr1- 0.052 +/- 0.016 mm; Gr2-0.041 +/- 0.003 mm. The luting agents presented similar film thickness and microTBS values, in dry and TC conditions and TC increased the bond strength regardless of the luting agent.

An in vitro thermal analysis during different light-activated hydrogen peroxide bleaching

This study measured the critical temperature reaching time and also the variation of temperature in the surface of the cervical region and within the pulp chamber of human teeth submitted to dental bleaching using 35% hydrogen peroxide gel activated by three different light sources. The samples were randomly divided into 3 groups (n = 15), according to the catalyst light source: Halogen Light (HL), High Intensity Diode Laser (DL), and Light Emmited Diode (LED). The results of temperature variation were submitted to the analysis of variance and Tukey test with p < 0.05. The temperature increase (mean value and standard deviation) inside the pulp chamber for the HL group was 6.8 ± 2.8°C; for the DL group was 15.3 ± 8.8°C; and for the LED group was 1.9 ± 1.0°C for. The temperature variation (mean value and standard deviation) on the tooth surface, for the group irradiated with HL was 9.1 ± 2.2°C; for the group irradiated with DL were 25.7 ± 18.9°C; and for the group irradiated with LED were 2.6 ± 1.4°C. The mean temperature increase values were significantly higher for the group irradiated with DL when compared with groups irradiated with HL and LED (p < 0.05). When applying the inferior limits of the interval of confidence of 95%, an application time of 38.7 s was found for HL group, and 4.4 s for DL group. The LED group did not achieve the critical temperatures for pulp or the periodontal, even when irradiated for 360 s. The HL and DL light sources may be used for dental bleaching for a short period of time. The LED source did not heat the target tissues significantly within the parameters used in this study. © 2010 Pleiades Publishing, Ltd.

Effects of five carbamide peroxide bleaching gels on composite resin microhardness.

The purpose of this study was to evaluate the effects of five home bleaching products containing 15-16% carbamide peroxide on the microhardness of microhybrid composite resin Z-250 (3M/Espe). A total of 72 specimens were fabricated in cylindrical acrylic matrices (4 x 2 mm), filled with composite resin and photo-activated for 40 seconds. They were divided in 6 study groups (n = 12), according to the bleaching product: Review (SS White), Magic Bleaching (Vigodent), Opalescence (Ultradent), Whiteness Perfect (FGM), Claridex (Biodinâmica), and a control group (not bleached). Specimens were exposed to 1 cc of bleaching gel for 6 hours daily for 2 weeks. The control group specimens were kept in artificial saliva throughout this time. All the specimens were then analyzed in a microhardness tester. Knoop hardness measurements were performed, and the results were submitted to parametric statistical analysis (analysis of variance and Tukey's test). Mean Knoop values and standard deviation were: baseline, 68.52a (4.28); control, 63.42b (7.16); Whiteness Perfect, 57.57c (1.81); Magic Bleaching, 57.22c (3.84); Opalescence, 57.03cd (4.00); Claridex, 53.64de (3.33); Review 51.45e (2.82). Identical letters mean statistical equality according to Tukey's test at the 5% significance level. The products significantly decreased Z-250 (3M/Espe) microhardness.

Effect of photochemical activation of hydrogen peroxide bleaching gel with and without TiO2 and different wavelengths

Aim: To evaluate the effect of photochemical activation of hydrogen peroxide (H2O2) bleaching gel with different wavelengths. Methods: In the study, 80 bovine incisors were used, which were stained in 25% soluble coffee and divided in 4 groups. The initial color was measured with the Easy Shade spectrophotometer by CIE Lab. An experimental 35% H2O2 bleaching gel was used, either with or without the presence of titanium dioxide (TiO2) pigment, associated with two light sources: G1 - Transparent Gel (TG) and no activation; G2 - Gel with TiO2 and activation with blue LED (l=470nm)\laser (Easy Bleach) appliance; G3 - Gel with TiO2 and activation with ultraviolet (l=345nm - UV); G4 - TG and activation with UV. Three applications of the gels were made for 10 min, and in each, 3 activations of 3 min, with interval of 30 s between them. The coloration was evaluated again and the variation in color perception (DE) was calculated. The data were submitted to one-way ANOVA and Tukey's test at 5% significance level. Results: There were significant differences between G1 and G4. The greatest E value was observed in G4 (13.37). There was no statistically significant difference (p>0.05) between the groups 2, 3 and 4. Conclusions: The presence of TiO2 particules in the bleaching gel did not interfere at the bleaching results.

Association of enamel microabrasion and dentinal bleaching in recovering an adolescent patient's smile: a case report

This article presents the enamel microabrasion protocol for removing intrinsic white stains of hard texture on the enamel surface, using a 37% phosphoric acid/pumice mixture associated with a carbamide peroxide-based bleaching agent in custom-made mouth trays. We observed that these clinical procedures were safe and effective, and solved our patient's esthetic problem. © 2010 Nova Science Publishers, Inc.

A comparison between diuretics and angiotensin-receptor blocker agents in patients with stage I hypertension (PREVER-treatment trial): Study protocol for a randomized double-blind controlled trial

Background: Cardiovascular disease is the leading cause of death in Brazil, and hypertension is its major risk factor. The benefit of its drug treatment to prevent major cardiovascular events was consistently demonstrated. Angiotensin-receptor blockers (ARB) have been the preferential drugs in the management of hypertension worldwide, despite the absence of any consistent evidence of advantage over older agents, and the concern that they may be associated with lower renal protection and risk for cancer. Diuretics are as efficacious as other agents, are well tolerated, have longer duration of action and low cost, but have been scarcely compared with ARBs. A study comparing diuretic and ARB is therefore warranted.Methods/design: This is a randomized, double-blind, clinical trial, comparing the association of chlorthalidone and amiloride with losartan as first drug option in patients aged 30 to 70 years, with stage I hypertension. The primary outcomes will be variation of blood pressure by time, adverse events and development or worsening of microalbuminuria and of left ventricular hypertrophy in the EKG. The secondary outcomes will be fatal or non-fatal cardiovascular events: myocardial infarction, stroke, heart failure, evidence of new subclinical atherosclerosis and sudden death. The study will last 18 months. The sample size will be of 1200 participants for group in order to confer enough power to test for all primary outcomes. The project was approved by the Ethics committee of each participating institution.Discussion: The putative pleiotropic effects of ARB agents, particularly renal protection, have been disputed, and they have been scarcely compared with diuretics in large clinical trials, despite that they have been at least as efficacious as newer agents in managing hypertension. Even if the null hypothesis is not rejected, the information will be useful for health care policy to treat hypertension in Brazil. Clinical trials registration number: ClinicalTrials.gov: NCT00971165. © 2011 Fuchs et al; licensee BioMed Central Ltd.

Chromatin modifying agents in the in vitro production of bovine embryos

The low efficiency observed in cloning by nuclear transfer is related to an aberrant gene expression following errors in epigenetic reprogramming. Recent studies have focused on further understanding of the modifications that take place in the chromatin of embryos during the preimplantation period, through the use of chromatin modifying agents. The goal of these studies is to identify the factors involved in nuclear reprogramming and to adjust in vitro manipulations in order to better mimic in vivo conditions. Therefore, proper knowledge of epigenetic reprogramming is necessary to prevent possible epigenetic errors and to improve efficiency and the use of in vitro fertilization and cloning technologies in cattle and other species. Copyright © 2011 Fabio Morato Monteiro et al.

Influence of dental exposure to oral environment on smear layer removal and collagen exhibition after using different conditioning agents

Although in vitro studies have shown encouraging results for root surface conditioning with demineralizing agents, in vivo studies have failed to show its benefits in periodontal healing. This can be attributed to several factors, among which, the hypermineralization of dental surface. Therefore, this in vitro study compared, using scanning electron microscopy (SEM), the effect of root surface conditioning with different conditioners (1% and 25% citric acid, 24% EDTA and 50 mg/mL tetracycline hydrochloride) in impacted teeth and in teeth that had their roots exposed to the oral environment. One trained examiner assessed the SEM micrographs using a root surface modification index. There was a tendency of more root surface modification in the group of impacted teeth, suggesting that the degree of root mineralization influences its chemical demineralization.