Fabrication and optical properties of core-shell structured spherical SiO2@GdVO4 : Eu3+ phosphor via sol-gel process

Europium-doped nanocrystalline GdVO4 phosphor layers were coated on the surface of preformed submicron silica spheres by sol-gel method. The resulted SiO2@Gd0.95Eu0.05VO4 core-shell particles were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra, low voltage cathodoluminescence (CL), time resolved PL spectra and kinetic decays. The XRD results demonstrate that the Gd0.95Eu0.05VO4 layers begin to crystallize on the SiO2 spheres after annealing at 600 C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have spherical shape, narrow size distribution (average size ca. 600 nm), non-agglomeration. The thickness of the Gd0.95Eu0.05VO4 shells on the SiO2 cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). PL and CL show that the emissions are dominated by D-5(0)-F-7(2) transition of Eu3+ (618 nm, red).

Assembly of Prussian blue onto SiO2 nanoparticles and carbon nanotubes by electrostatic interaction

Prussian blue (PB) was modified onto surface of SiO2 nanoparticles and multiwall carbon nanotubes (MWNTs) by electrostatic assembled method. SiO2 nanoparticles and MWNTs firstly modified by polyelectrolyte exhibited positive charges and negative charged PB could be assembled onto them. UV-vs spectroscopy, Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM), field-emitted scanning electron microscopy (FE-SEM) and electrochemical methods were used to characterize these composite nanomaterials. TEM and FE-SEM images showed that PB was easily assembled onto polyelectrolyte modified SiO2 nanoparticles and MWNTs. Moreover, PB on the surface of nanomaterials was stable and still kept its intrinsic electrochemical properties and high electrocatalytic activity towards hydrogen peroxide.

Well defined carbazole-based hole-transporting amorphous molecular materials

Monodisperse carbazole-based oligomers have been synthesized via C-N bonds formation by the modified Ullmann reaction. The full characterization of their structure is presented. These derivatives are highly thermally stable amorphous compounds with glass transition temperatures of 167-171 degrees C and thermal decomposition temperatures of ca. 400 degrees C. Amorphous films of the materials were fabricated and their hole-transporting properties were tested in a light emitting device with Alq(3) as an electroluminescent and electron-transporting material.

Preparation and properties of ternary polyimide/SiO2/polydiphenyisiloxane composite films

A series of novel ternary polyimide/SiO2/polydiphenylsiloxane (PI/SiO2/PDPhS) composite films were prepared through co-hydrolysis and condensation between tetramethoxysilane, diphenyldimethoxysilane (DDS) and aminopropyltriethoxysilane-terminated polyamic acid, using an in situ sol-gel method. The composite films exhibited good optical transparency up to 30 wt% of total content of DDS and SiO2. SEM analysis showed that the PDPhS and SiO2 were well dispersed in the PI matrix without macroscopic separation of the composite films. TGA analysis indicated that the introduction of SiO2 could improve the thermal stability of the composite films. Dynamic mechanical thermal analysis showed that the composite films with low DDS content (5 wt%) had a higher glass transition temperature (T-g) than pure PI matrix. When the content of DDS was above 10 wt%, the T-g of the composite decreased slightly due to the plasticizing effect of flexible PDPhS linkages on the rigid PI chains. The composite films with high SiO2 content exhibited higher values of storage modulus. Tensile measurements also showed that the modulus and tensile strength of the composite films increased with increasing SiO2 content, and the composite films still retained a high elongation at break due the introduction of DDS.