Resumo:

For polyamide used in reverse osmosis (RO) membranes, the content of pendant acid groups is critical to its performance. In this work, FTIR was used to analyze the acid contents in the polyamide films prepared via interfacial polymerization of trimesic acid trichloride (TMC) in hexane and 1,3-phenylenediamine (MPDA) in water, and the effects of reaction conditions, including monomer concentrations, time, and temperature, were studied. It was found that more pendant acid groups are present in the polyramide film at higher TMC concentrations or lower MPDA concentrations, and longer reaction times and lower temperatures also favor the formation of the free acids. These results can be explained by the monomer diffusion in the interfacial polymerization process. This work may help the design and fabrication of RO membranes with different hydrophilicity and target performance.

Relevância:

10.00% 10.00%

Publicador:

Resumo:

利用羧基同导电聚苯胺(cPANI)主链上的氮原子的相互作用,制备了静电作用型水基导电聚苯胺/二氧化硅杂化材料,研究了杂化材料涂层对冷轧钢板的防腐性能.在3.5%NaCl中,含11 wt%cPANI的杂化材料涂层的腐蚀电位比纯二氧化硅涂层正移了200 mV,腐蚀电流从13.4μA降到2.4μA,下降了5倍,表明含cPANI的静电作用型杂化涂料使冷轧钢板表面变得更惰性.阻抗分析结果表明,cPANI含量为11 wt%的静电作用型杂化材料的阻抗比纯无机二氧化硅涂层大一个数量级,而且在碱性介质中浸泡10天后,杂化材料涂层的阻抗仍然保持稳定,而纯无机二氧化硅涂层的阻抗比初始值下降了一个数量级.杂化材料的形态分析结果表明,cPANI在静电作用型cPANI/二氧化硅杂化材料中的分布比在普通cPANI/二氧化硅杂化材料中更加均匀一致,从而使得它比普通的cPANI/二氧化硅杂化材料具有更好的防腐效果.

Relevância:

10.00% 10.00%

Publicador:

Resumo:

Layered organic-inorganic composite materials (C5H10N3)PbX4 (X = Br 1, Cl 2) containing histaminium dications were grown via a solution-cooling process, and their structure and optical properties were determined. The organic ligand-histaminium introduced into the corner-sharing octahedra of the 'PbX4- layer' contains both primary ammonium and imidazolium different from the traditionally primary amine found in this system. As comparison, another analogous amine of 3-amino-1,2,4-triazol was used as ligand to coordinate with PbBr2 in acid solution. A novel complex (C2H2N4)PbBr3 (3) was obtained with zigzag PbBr2 chains different from the PbX4 layer in compound as 1 and 2. The hybrid (C5H10N3)PbX4 show exciton absorption at 339 nm for X = Cl and 419 nm for X = Br with the corresponding emission at 360 and 436 nm, respectively. The different PbBr2 chain structure of compound 3 does not show photo luminescence.