Partial oxidation of ethane to syngas in an oxygen-permeable membrane reactor

A perovskite-type oxide of Ba0.5Sr0.5Co0.8Fe0.2O3-delta (BSCFO) with mixed electronic and oxygen ionic conductivity at high temperatures was used as an oxygen-permeable membrane. A tubular membrane of BSCFO made by extrusion method has been used in the membrane reactor to exclusively transport oxygen for the partial oxidation of ethane (POE) to syngas with catalyst of LiLaNiO/gamma-Al2O3 at temperatures of 800-900 degreesC. After only 30 min POE reaction in the membrane reactor, the oxygen permeation flux reached at 8.2 ml cm(-2) min(-1). After that, the oxygen permeation flux increased slowly and it took 12 h to reach at 11.0 ml cm(-2) min(-1). SEM and EDS analysis showed that Sr and Ba segregations occurred on the used membrane surface exposed to air while Co slightly enriched on the membrane surface exposed to ethane. The oxygen permeation flux increased with increasing of concentration of C2H6, which was attributed to increasing of the driving force resulting from the more reducing conditions produced with an increase of concentration of C2H6 in the feed gas. The tubular membrane reactor was successfully operated for POE reaction at 875 degreesC for more than 100 h without failure, with ethane conversion of similar to 100%, CO selectivity of >91% and oxygen permeation fluxes of 10-11 ml cm(-2) min(-1). (C) 2002 Elsevier Science B.V. All rights reserved.

Alkaline treatment of the cellulose fiber affecting membrane column behaviour for high-performance immunoaffinity chromatography

The original cellulose fibers and those treated by alkaline solution were both used to prepare the acrylic membranes. The two kinds of membranes were packed into the columns for high-performance immunoaffinity chromatography by the immobilization of protein A on them. It was observed that the alkaline treatment of the cellulose fiber decreased the pressure resistance of the membrane to the mobile phases and greatly increased the accessible volume to the proteins, but affected the adsorption capacity of human IgG on the protein A membrane columns less. There is little difference between those two kinds of membranes on the adsorption capacities of HIgG, which means that the alkaline treatment of the cellulose fiber only significantly changes the void volume inter-membrane, and the porosity and surface area of membrane less. Alkaline treatment of the cellulose fiber reduced the membrane-column efficiency significantly. Some typical examples for the immunoaffinity analysis of IgG from human and dog plasma on the protein A membrane columns are illustrated. Copyright (C) 2000 John Wiley & Sons, Ltd.

Syngas production using an oxygen-permeating membrane reactor with cofeed of methane and carbon dioxide

CH4-CO2-O-2 reforming to syngas in a never Ba0.5Sr0.5Co0.8Fe0.2O3.delta oxygen-permeable membrane reactor using LiLaNiO/gamma-Al2O3 as catalyst was successfully reported. Excellent reaction performance was achieved with around 92% methane conversion efficiency, 95% CO2 conversion rate, and nearly 8.5mL/min.cm(2) oxygen permeation flux. In contrast to the oxygen permeation model with the presence of large concentration of CO2 (under such condition the oxygen permeation flux deteriorates with time), the oxygen permeation flux is really stable under the CH4CO2-O-2 reforming condition.

Easy fabrication of dense ceramic membrane for oxygen separation

A combined EDTA-citrate complexing method was developed for the easy preparation of mixed oxygen-ionic and electronic conducting dense ceramic membrane for oxygen separation. The nea method takes the advantage of lower calcination temperature for phase formation. lower membrane sintering temperature and higher relative density over the standard ceramic method.

Synthesis and gas permeation properties of an NaA zeolite membrane

A high quality NaA zeolite membrane, which shows a H-2/n-C4H10 permselectivity of 106, has been synthesized on a seeded alpha-Al2O3 support by a multistage synthesis method.

Fast formation of NaA zeolite membrane in the microwave field

NaA zeolite membrane was successfully synthesized on the porous alpha-Al2O3 support by microwave heating. The synthesis of NaA zeolite membrane in the microwave field only needs 15 min and the synthesis time is 10 times shorter than that by conventional heating. SEM characterization indicates that the zeolite crystals in the NaA zeolite membrane synthesized by microwave heating are uniform in size; the membrane thickness is about 4 mu m and is thinner than that of the NaA zeolite membrane synthesized by conventional heating. Gas permeation studies indicate that the permeances of the NaA zeolite membrane synthesized by microwave heating are 3-4 times higher than those of the NaA zeolite membrane synthesized by conventional heating, while their permselectivities are comparable.

Composite anode for CO tolerance proton exchange membrane fuel cells

Fuel of proton exchange membrane fuel cells (PEMFC) mostly comes from reformate containing CO. which will poison the fuel cell electrocatalyst. The effect of CO on the performance of PEMFC is studied in this paper. Several electrode structures are investigated for CO containing fuel. The experimental results show that thin-film catalyst electrode has higher specific catalyst activity and traditional electrode structure can stand for CO poisoning to some extent. A composite electrode structure is proposed for improving CO tolerance of PEMFCs. With the same catalyst loading. the new composite electrode has improved cell performance than traditional electrode with PtRu/C electrocatalyst for both pure hydrogen and CO/H-2. The EDX test of composite anode is also performed in this paper, the effective catalyst distribution is found in the composite anode. (C) 2002 Elsevier Science B.V. All rights reserved.

Synthesis of a high-permeance NaA zeolite membrane by microwave heating

Zeolite membranes with high permeance and separation factors are highly desirable for practical applications. Although, in the past, very good separation factors have been obtained, it has proved difficult to achieve a high permeance. Ken a comparative study of microwave versus conventional heating in the hydrothermal synthesis of NaA zeolite membranes is made. It is demonstrated that membranes prepared by microwave heating have not only a higher permeance but also a considerably shorter synthesis time. These observations are rationalized by examining the mechanism of membrane formation.