The origin of "Rare Earth" texture development in extruded Mg-based alloys and its effect on tensile ductility

The extrusion behaviour, texture and tensile ductility of five binary Mg-based alloys have been examined and compared to pure Mg. The five alloying additions examined were Al, Sn, Ca, La and Gd. When these alloys are compared at equivalent grain size, the La- and Gd-containing alloys show the best ductilities. This has been attributed to a weaker extrusion texture. These two alloying additions, La and Gd, were found to also produce a new texture peak with View the MathML source parallel to the extrusion direction. This “rare earth texture” component was found to be suppressed at high extrusion temperatures. It is proposed that the View the MathML source texture component arises from oriented nucleation at shear bands.

Effect of microalloying with rare-earth elements on the texture of extruded magnesium-based alloys

A series of alloys have been produced with microalloying additions of rare-earth (RE) elements in the range of 0.1–0.4 wt.%. The alloys have been extruded to produce grain sizes of 23 ± 5 μm. The texture of the extruded alloys was measured, and it was found that the extrusion texture was weakened by the addition of RE elements. The samples with weakened extrusion textures exhibited an increase in the tensile elongation.

Are day-active small mammals rare and small birds abundant in Australian desert environments because small mammals are inferior thermoregulators?

Small desert birds are typically diurnal and highly mobile (hence conspicuous) whereas small non-volant mammals are generally nocturnal and less mobile (hence inconspicuous). Birds are more mobile than terrestrial mammals on a local and geographic scale, and most desert birds are not endemic but simply move to avoid the extremes of desert conditions. Many small desert mammals are relatively sedentary and regularly use physiological adjustments to cope with their desert environment (e.g., aestivation or hibernation). It seems likely that prey activity patterns and reduced conspicuousness to predators have reinforced nocturnality in small desert mammals. Differences such as nocturnality and mobility simply reflect differing life-history traits of birds and mammals rather than being a direct result of their differences in physiological capacity for tolerating daytime desert conditions.

The corrosion inhibition mechanism of new rare earth cinnamate compounds — electrochemical studies

A combination of linear polarisation resistance (LPR) and cyclic potentiodynamic polarisation (CPP) measurements demonstrated that the lanthanum-4 hydroxy cinnamate compound could inhibit both the cathodic and anodic corrosion reactions on mild steel surfaces exposed to 0.01 M NaCl solutions. However, the dominating response was shown to vary with inhibitor concentration. At the concentrations for which the highest level of protection was achieved, both REM-4 hydroxy cinnamate (REM being lanthanum and mischmetal) displayed a strong anodic behaviour for mild steel and their inhibition performance, including their resistance against localised attack, improved with time.

Electrochemical impedance spectroscopy (EIS) measurements and modelling were carried out so as to propose a simple electrical model and correlate the extracted parameters to the inhibition mechanism put forward for REM-cinnamate based compounds. The results supported the high corrosion inhibition performance of the compounds as well as the build-up of a protective film with time. Based on a two-layer model the results suggested that the upper layer of the inhibitor film seemed to offer less resistance to the diffusion of electrochemically active species than the highly resistive inner layer at the film/metal interface.

Corrosion mitigation of mild steel by new rare earth cinnamate compounds

Corrosion rate measurements based on weight loss (i.e., mild steel immersed for seven days in 0.01 M NaCl) and linear polarization resistance (LPR) techniques have shown that even low concentrations (200 ppm) of cerium and lanthanum cinnamates are able to significantly inhibit corrosion. Of all the compounds investigated in this work Ce(4-methoxycinnamate)3· 2 H2O and La(4-methoxycinnamate)3· 2 H2O compounds exhibited the greatest inhibition and, in comparison with the component inhibitors, a synergy was clearly observed. The mechanism of corrosion inhibition was investigated using cyclic potentiodynamic polarization (CPP) measurements. The results suggest that La(4-nitrocinnamate)3· 2 H2O and Ce(4-methoxycinnamate)3· 2 H2O behave as mixed inhibitors and improve the resistance of steel against localized attack.