Phase conversion and spectral properties of long lasting phosphor Zn-3 (PO4)(2): Mn2+, Ga3+

A red long lasting phosphor Zn-3(PO4)(2): Mn2+ Ga3+ (ZPMG) was prepared by ceramic method, and phase conversion and spectral properties were investigated. Results indicated that the phase conversion from alpha-Zn-3(PO4), beta-Zn-3(PO4)(2) to gamma-Zn-3(PO4)(2) occurs with different manganese concentration incorporated and sinter process. The structural change induced by the phase transformation results in a remarkable difference in the spectral properties. The possible luminescence mechanism for this red LLP with different forms has been illustrated.

Pink light emitting long-lasting phosphorescence in Sm3+-doped CdSiO3

Novel pink light emitting long-lasting afterglow CdSiO3:SM3+ phosphors are prepared by the conventional high-temperature solid-state method and their luminescent properties are investigated. XRD and photolurflinescence (PL) spectra are used to characterize the synthesized phosphors. The phosphors are well crystallized by calcinations at 1050degreesC for 5 h. These phosphors emit pink light and show long-lasting phosphorescence after they are excited with 254 nm ultraviolet light. The phosphorescence lasts for nearly 5 h in the light perception of the dark-adapted human eye (0.32mcd/m(2)). The phosphorescence mechanism is also investigated. All the results indicate that these phosphors have promising potential practical applications.

Spectra and long-lasting properties of Sm3+-doped yttrium oxysulfide phosphor

We reported, for the first time to the best of our knowledge, the Sm3+ -doped yttriurn oxysulfide phosphors has reddish orange long-lasting phosphorescence. The phosphor show prominent luminescence in reddish orange due to the electronic transitions of (4)G(5/2) --> H-6(J) (J = 5/2, 7/2, 9/2), the afterglow color of this type of phosphors is a mixture of the three above mentioned electronic transition emissions and have a little different when the concentration of the Sm3+ dopant changes. Synthesis procedure of the Sm3+-yttrium oxysulfide reddish orange phosphor through the flux fusion method with binary flux compositions was presented. The synthesized phosphors were analyzed using X-ray diffraction (XRD) to interpret the structural characterization. The XRD analysis result reveal that the Y2O2S:Sm3+ phosphor synthesized with a binary flux composition containing (S and Na2CO3 at a ratio of 1: 1 at 30 wt.% of total raw material) at 1050degreesC for 3 h was in single-phase. Luminescence properties of the Y2O2S:Sm3+ long-lasting phosphor was analyzed by measuring the excitation spectra, emission spectra and afterglow decay curve. The mechanism of the strong afterglow from Y2O2S:Sm3+ was also discussed in this paper.

Long-lasting properties of rare earth-doped Y2O2S phosphors

The aim of this presentation is to report a new result of afterglow materials. The Y2OS: Ln(3+) (Ln = Sm, Tm) phosphors show bright reddish orange and orange-yellow colors when excited by UV or visible light. The main spectroscopic characterizations of Sin(3+) and Tin(3+) in yttrium oxysulfide and their long-lasting phosphorescence were measured and discussed in this presentation. Their long-lasting phosphorescence can be seen by the naked eyes clearly for about one hour in the dark room after the Irradiation light sources were removed. XRD and photoluminescence (PL) spectra as well as the luminance decay were used to characterize these long-lasting phosphorescence phosphors. The results of XRD indicate that the products synthesized through the flux fusion method tinder 1050 degreesC, for 6 It have a good crystallization without any detectable amount of impurity phase. Both the PL spectra and luminance decay results reveal that these phosphors have efficient luminescent and good long-lasting properties. We believe that the experimental data gathered in our present work will be. useful in finding some new long-lasting phosphors with different colors.

A novel white light emitting long-lasting phosphor

A novel white light emitting long-lasting phosphor Cd1-xDyxSiO3 is reported in this letter. The Dy3+ doped CdSiO3 phosphor emits white light. The phosphorescence can be seen with the naked eye in the dark clearly even after the 254 nm UV irradiation have been removed for about 30 min. In the emission spectrum of 5% Dy3+ doped CdSiO3 phosphor, there are two emission peaks of Dy3+, 580 mn (F-4(9/2)-->H-6(13/2)) and 486 nm (F-4(9/2)-->H-6(15/2)), as well as a broad band emission located at about 410 nm. All the three emissions form a white light with CIE chromaticity coordinates x=0.3874, y=0.3760 and the color temperature is 4000 K under 254 mn excitation. It indicated that this phosphor is a promising new luminescent material for practice application.

Redshift phenomenon of the excitation light of long life emission phosphor

We observed that the SrMg2(PO4)(2):Eu phosphor could emit long life phosphorescence with the excitation light whose wavelength was shorter than 420 nm, however, when La, Ce, or Gd was codoped, the wavelength of the excitation light to cause the phosphorescence had a redshift of 40 nm. A possible mechanism and related discussion for this redshift phenomenon of the excitation light was given. It was suggested that the threshold between the trap and valence band was decreased with the addition of the codopants.

Column chromatographic purification free synthesis of long-chain monodisperse oligo(1,4-phenyleneethynylene)s: towards large-scale automatic synthesis of molecular wires

A facile, mild and rapid solid phase synthetic route free of column chromatographic purification to the synthesis of soluble monodisperse long-chain oligo(1,4-phenyleneethynylene)s is presented.

Evaluation of bioeffects of a long-term administering ChangLe on rat by proton NMR method and biochemical examination

High resolution H-1 nuclear magnetic resonance ( NMR) spectroscopy has been employed to assess long-term toxicological effects of ChangLe (a kind of rare earth complex applied in agriculture). Male Wistar rats were administrated orally with ChangLe at doses of 0, 0.1, 0.2, 2.0, 10 and 20 mg/kg body weight daily, respectively, for 6 months. Urine was collected at-day 30, 60, go and serum samples were taken after 6 months. Many low-molecular weight metabolites were identified by H-1 NMR spectra of rat urine. A decrease in citrate and an increase in ketone bodies, creatinine, DMA, DMG, TMAO, and taurine in the urine of the rats. receiving high doses were found by H-1 NMR spectra. These may mean that high-dosage of ChangLe impairs the specific region of liver and kidney, such as renal tubule and mitochondria. The decrease in citrate and the increase in succinate and alpha-ketoglutarate were attributed to a combination of the inhibition of certain citric acid enzymes, renal tubular acidosis and the abnormal fatty acid catabolism. The information of the renal capillary necrosis could be derived from the increase in DMIA, DMG and TMAO. The increase in taurine was due to hepatic mitochondria dysfunction. The conclusions were supported by the results of biochemical measure. merits and enzymatic assay.

Novel indigo light emitting long-lasting phosphors CdSiO3: RE3+ (RE = Y, La, Gd, Lu)

A series of novel indigo light emitting long-lasting phosphors CdSiO3: RE3+ (RE = Y, La, Gd, Lu) was prepared by the conventional high-temperature solid-state method. The XRD, photoluminescence (PL) spectra and afterglow intensity decay were used to characterize the synthesized phosphors. These phosphors emitted indigo light and showed long-lasting phosphorescence. The phosphorescence can be seen with the naked eye in the dark clearly even after the 254-nm UV irradiation have been removed for more than 30 min.

Multi-color long-lasting phosphorescence of rare earth ions in CdSiO3 matrix

A series of rare earth ions doped CdSiO3:RE3+(RE=Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) multi-color long-lasting phosphorescence phosphors are prepared by the conventional high-temperature solid-state method. The results of XRD measurement indicate that the products fired under 1050degreesC for 3 h have a good crystallization without any detectable amount of impurity phase. Rare earth ions doped CdSiO3 phosphors possess excellent luminescence properties. When rare earth ions such as Y3+, La3+, Gd3+, Lu3+, Ce3+, Nd3+, Ho3+, Er3+, Tm3+ and Yb3+ are introduced into the CdSiO3 host, one broadband centered at about 420 nm resulting from traps can be observed. In the case of other earth ions such as Pr3+, Sm3+, Eu3+, Tb3+ and Dy3+, their characteristic line emitting as well as the similar to420 nm broadband luminescence can be obtained. The mixture of their characteristic line emitting with the similar to420 nm broadband luminescence results in various afterglow color.

Multi-color long-lasting phosphorescence in Mn2+-doped ZnO-B2O3-SiO2 glass-ceramics

Multi-color LLP phenomenon was observed in Mn2+-doped ZnO-B2O3-SiO2 glassceramics after the irradiation of a UV lamp at room temperature. Transparent ZnO-B2O3-SiO2 glass emitted reddish LLP while opaque glass-ceramics prepared by the glass sample after heat treatment emitted yellowish or greenish LLP. The change of the phosphorescence is due to the alteration of co-ordination state of Mn2+. The phosphorescence of the samples was seen in the dark with naked eyes even 12 h after the irradiation with a UV lamp (lambda(max) = 254 nm) for 30 min. Based on the approximative t(-1) decay law of the phosphorescence, we suggest that the LLP is attributed to the thermally assisted electron-hole recombination.

Long lasting phosphorescence, thermoluminescence and electron spin resonance property of Mn2+ activated ZnO-Al2O3SiO2 ceramic

The long lasting phosphorescence (LLP) phenomenon in Mn2+-doped ceramic based on ZnO-Al2O3-SiO2 (ZASM) is observed. After irradiation by a UVP standard mercury lamp peaking at 254 nm with a power of 0.6 mW/cm(2) for 15 min, the ceramic sample emits a bright green light peaking at 519 nm, which can be seen in the dark even 15 h after the removal of UVP standard mercury lamp by the naked eyes whose limit of light perception is 0.32 mcd/m(2). The initial afterglow intensity reaches about 1900 mcd/m(2), and the color coordinate (X, Y) is (0.2280, 0.5767) at about 10 s after stopping irradiation. The thermoluminescence (TL) spectra show that there are at least three kinds of trap centers with different trap levels while electron spin resonance (ESR) spectra indicate that there are electron- and hole-trapping centers induced after irradiation by a UVP standard mercury lamp. Based on these measurements, the LLP is considered to be due to the recombination of electrons and holes at trapping centers with different levels, which are firstly thermally released back to Mn2+ and then give rise to the bright green LLP at room temperature.

A NEW SIMPLE LONG-PATH-LENGTH THIN-LAYER SPECTROELECTROCHEMICAL CELL IN VARIOUS USES

This article describes the design of a new type of long-path-length thin-layer cell (LPTLC), which is constructed by inserting two Teflon cell bodies into a standard cuvette. This cuvette holder enables the LPTLC to combine with photometric instrumentation conveniently. Gold, platinum, glassy carbon, and other materials can be used for the working electrode. Since no soluble adhesive material is used, the cell can meet various needs (in situ conventional and derivative W-vis, in situ circular dichroism, etc.) in both aqueous and nonaqueous systems.

THE FRACTURE-BEHAVIOR OF PHENOLPHTHALEIN POLYETHER ETHER KETONE AT ELEVATED-TEMPERATURE FOR LONG TERMS

The fracture behavior of phenolphthalein polyether-ether ketone (PEK-C) affected by physical aging at 200 degrees C was studied by tensile experiments, scanning electron microscopy, and differential scanning calorimetry observations. The ductile-brittle fracture transition (DBT) caused by physical aging can be considered as a competition between fracture mechanisms of crazing and shear yielding. The aging time required for the DBT is found to be around 400 h, based on the morphological studies and tensile experiments. The shear yielding component of the mechanical deformation could erase the aging effect, thus a deaging phenomenon occurs. We found that the deaging phenomenon has an intrinsic relationship with the extent of aging in the specimen and as a result of the fracture behavior. (C) 1995 John Wiley and Sons, Inc.

HIGHLY SENSITIVE AND SELECTIVE DETERMINATION OF RIBOFLAVIN BY FLOW-INJECTION ANALYSIS USING PARALLEL DUAL-CYLINDER MICROELECTRODES

A novel wall-jet cell with parallel dual cylinder (PDC) microelectrodes was constructed and used for flow injection analysis (FLA). The detector takes the advantages of ''redox recycling'' between bipotentiostated microcylinder electrodes (- 0.4 V/SCE an