High temperature operation of 5.5 mu m strain-compensated quantum cascaded lasers

We develop 5.5-mu m InxGa1-xAs/InyAl1-yAs strain-compensated quantum cascade lasers with InP and InGaAs cladding layers by using solid-source molecular-beam epitaxy. Pulse operation has been achieved up to 323 K (50 degrees C) for uncoated 20-mu m-wide and 2-mm-long devices. These devices display an output power of 36 mW with a duty cycle of 1% at room temperature. In continuous wave operation a record peak optical power of 10 mW per facet has been measured at 83 K.

Effects of shape and magnetic field on the optical properties of wurtzite quantum rods

The optical properties of quantum rods in the absence and presence of the magnetic field are studied in the framework of effective-mass envelope function theory. The two-dimensional (2D) and 1D transition dipoles of wurtzite quantum rods are investigated. It is found that the transition dipoles change from 2D to 1D as the aspect ratio of the ellipsoid increases, in agreement with the experimental results. The linear polarization factors of optical transitions of quantum rods with critical aspect ratio are zero at every orientation of the wave propagation. So quantum rods with critical aspect ratio have isotropic transition dipoles. Due to the 2D or 1D transition dipoles, the linear polarization factors of optical transitions of quantum rods change from negative or positive values to zero as the orientation of the wave propagation changes from the x axis of the crystal structure to the z axis, in agreement with the experimental results. Under magnetic field applied along the z axis of the crystal structure, the negative linear polarization factors in the 2D transition dipole case decrease as the magnetic field increases, while under magnetic field applied along the x axis, the negative linear polarization factors increase as the magnetic field increases. The antisymmetric Hamiltonian is very important to these effects of the magnetic field. It is found that quantum rods with a given radius at a given temperature have dark excitons in a range of aspect ratio. The dimensions along the x, y axes of the crystal structure play opposite roles to the dimension along the z axis on the dark exciton phenomenon. Dark excitons become bright under appropriate magnetic field.

GaAs-based room-temperature continuous-wave 1.59 mu m GaInNAsSb single-quantum-well laser diode grown by molecular-beam epitaxy

Starting from the growth of high-quality 1.3 mu m GaInNAs/GaAs quantum well (QW), the QW emission wavelength has been extended up to 1.55 mu m by a combination of lowering growth rate, using GaNAs barriers and incorporating some amount of Sb. The photoluminescence properties of 1.5 mu m range GaInNAsSb/GaNAs QWs are quite comparable to the 1.3 mu m QWs, revealing positive effect of Sb on improving the optical quality of the QWs. A 1.59 mu m lasing of a GaInNAsSb/GaNAs single-QW laser diode is obtained under continuous current injection at room temperature. The threshold current density is 2.6 kA/cm(2) with as-cleaved facet mirrors. (c) 2005 American Institute of Physics.

Time-resolved photoluminescence of sub-monolayer InGaAs/GaAs quantum-dot-quantum-well heterostructures

Time-resolved photoluminescence (PL) of sub-monolayer (SML) InGaAs/GaAs quantum-dot-quantum-well heterostructures was measured at 5 K for the first time. The radiative lifetime of SML quantum dots (QDs) increases from 500 ps to 800 ps with the increase of the size of QDs, which is related to the small confinement energy of the excitons inside SML QDs and the exciton transfer from smaller QDs to larger ones through tunneling. The rise time of quantum-dot state PL signal strongly depends on the excitation power density. At low excitation power density, the rise time is about 35 ps, the mechanism of carrier capture is dominated by the emission of longitudinal-optical phonons. At high excitation power density, the rise time decreases as the excitation density increases, and Auger process plays an important role in the carrier capture. These results are very useful for understanding the working properties of sub-monolayer quantum-dot devices.

Structural and optical properties of InAs/In0.52Al0.48As self-assembled quantum wires on InP(001)

Six-stacked InAs/In0.52Al0.48As self-assembled quantum wires (QWRs) on InP(001) by molecular-beam epitaxy (MBE) have been studied by high-resolution transmission electron microscopy (HRTEM) and polarized PL measurements. We obtained the chemical lattice fringe (CLF) image of InAs self-assembled QWRs embedded in the In0.52Al0.48As matrix by the interference between the (002)-diffracted beam and the transmitted beam in the image plane of the objective lens. The results show that the InAs QWRs were bounded by (113), (001) and (114) facets. Both the size and strain distribution in QWRs were determined. It was found that with the growth of successive periods, the height and height fluctuation of InAs QWRs decreased from the bottom period to the upper one. Some suggestions are put forward for further improving the uniformity of the stacked InAs QWRs. (c) 2005 Elsevier B.V. All rights reserved.

1.3 mu m InAs/GaAs self-assembled quantum dots grown on In0.2Ga0.8As-GaAs combined strain-buffer layer

Optical properties and surface structures of InAs/CaAs self-assembled quantum dots (QDs) grown on 2 nm In-0.2 Ga0.8As and x ML GaAs combined strain-buffer layer were investigated systematically by photoluminescence ( PL) and atomic force microscopy (AFM). The QD density increased from similar to 1.7 x 10(9) cm(-2) to similar to 3.8 x 10(9) cm(-1) due to the decreasing of the lattice mismatch. The combined layer was of benefit to increasing In incorporated into dots and the average height-to-width ratios, which resulted in the red-shift of the emission peaks. For the sample of x = 10 ML, the ground state transition is shifted to 1350 nm at room temperature.

Electron transport through hierarchical self-assembly of GaAs/AlxGa1-xAs quantum dots

The transmission of electrons through a hierarchical self-assembly of GaAs/AlxGa(1-)xAs quantum dots (QDs) is calculated using the coupled-channel recursion method. Our results reveal that the number of conductance peaks does not change when the barrier widths change, but the intensities decrease as the barrier widths increase. The conductance peaks will shift towards low Fermi energies as the transverse width of GaAs QD increases, as the thickness of GaAs quantum well increases, or as the height of GaAs QDs decreases. Our calculated results may be useful in the application of QDs to photoelectric devices. (c) 2005 American Institute of Physics.

Thermal quenching of luminescence from buried and surface InGaAs self-assembled quantum dots with high sheet density

Variable-temperature photoluminescence (PL) spectra of Si-doped self-assembled InGaAs quantum dots (QDs) with and without GaAs cap layers were measured. Narrow and strong emission peak at 1075 nm and broad and weak peak at 1310 nm were observed for the buried and surface QDs at low temperature, respectively. As large as 210 meV redshift of the PL peak of the surface QDs with respect to that of the buried QDs is mainly due to the change of the strain around QDs before and after growth of the GaAs cap layer. Using the developed localized-state luminescence model, we quantitatively calculate the temperature dependence of PL peaks and integrated intensities of the two samples. The results reveal that there exists a large difference in microscopic mechanisms of PL thermal quenching between two samples. (c) 2005 American Institute of Physics.

1.55-mu m ridge DFB laser integrated with a buried-ridge-stripe dual-core spot-size converter by quantum-well intermixing

A ridge distributed feedback laser monolithically integrated with a buried-ridge-stripe spot-size converter operating at 1.55 mu m was successfully fabricated by means of low-energy ion implantation quantum-well intermixing and dual-core technologies. The passive waveguide was optically combined with a laterally exponentially tapered active core to control the mode size. The devices emit in a single transverse and single longitudinal mode with a sidemode suppression ratio of 38.0 dB. The threshold current was 25 mA. The beam divergence angles in the horizontal and vertical directions were as small as 8.0 degrees x 12.6 degrees, respectively, resulting in 3.0-dB coupling loss with a cleaved single-mode optical fiber.

Effect of annealing on optical properties of InAs quantum dots grown by MOCVD on GaAs (100) vicinal substrates

Thermal annealing effect on InAs quantum dots grown on vicinal (100) GaAs substrates is studied in comparison with dots on exact (100) GaAs substrates. We find that annealing acts stronger effect on dots with vicinal substrates by greatly accelerating the degradation of material quality. as well as slightly increasing the blueshift of the emission wavelength and the narrowing of PL linewidth. It is attributed to the higher strain in the dots formed on the vicinal substrates.

Influence of rapid thermal annealing on InAs/InAlAs/InP quantum wires with different InAs deposited thickness

We have studied the effect of the post-growth rapid thermal annealing on optical and electrical properties of InAs/InAlAs/InP quantum wires with various InAs deposited thickness. Quite different annealing behaviors in photoluminescence and dark resistance are observed, which can be attributed to dislocations in samples. After annealing at 800 degrees C, quantum wires still exist in the sample with two monolayer InAs deposited thickness, but the temperature-dependent PL properties are changed greatly due to the intermixing of In/Al atoms. (c) 2005 Elsevier B.V. All rights reserved.

High structural and optical quality 1.3 mu m GaInNAs/GaAs quantum wells with higher indium content grown by molecular-beam expitaxy

High structural and optical quality 1.3 mu m GaInNAs/GaAs quantum well (QW) samples with higher (42.5%) indium content were successfully grown by molecular-beam epitaxy. The cross-sectional transmission electron microscopy measurements reveal that there are no structural defects in such high indium content QWs. The room-temperature photoluminescence peak intensity of the GaIn0.425NAs/GaAs (6 nm/20 nm) 3QW is higher than, and the full width at half maximum is comparable to, that of In0.425GaAs/GaAs 3QW, indicating improved optical quality caused by strain compensation effect of introducing N to the high indium content InGaAs epilayer. (C) 2005 American Institute of Physics.

Raman study on self-assembled InAs/InAlAs/InP(001) quantum wires

The phonons of self-assembled InAs/InAlAs/InP quantum wires (QWRs) have been studied by Raman scattering. The QWR LO phonons show an unusual frequency shift with the increase of the InAs deposited thickness due to dislocations. The QWR LO phonons are found to follow the selection rule of the LO phonons in bulk zinc-blende semiconductors. Because of the intermixing of In/Al atoms and the multiplication of dislocations, the post-growth thermal annealing treatment leads to a shift of the QWR LO phonons to lower frequency.

High-quality GaNAs/GaAs quantum wells with light emission up to 1.44 mu m grown by molecular-beam epitaxy

High-quality GaNAs/GaAs quantum wells with high substitutional N concentrations, grown by molecular-beam epitaxy, are demonstrated using a reduced growth rate in a range of 0.125-1 mu m/h. No phase separation is observed and the GaNAs well thickness is limited by the critical thickness. Strong room-temperature photoluminescence with a record long wavelength of 1.44 mu m is obtained from an 18-nm-thick GaN0.06As0.94/GaAs quantum well. (C) 2005 American Institute of Physics.

Theoretical investigation of intersubband transition in AlxGa1-xN/GaN/AlyGa1-yN step quantum well

A modified self-consistent method is introduced for the design of AlxGa1-xN/GaN step quantum well (SQW) with the position and energy-dependent effective mass. The effects of nonparabolicity are included. It is shown that the nonparabolicity effect is minute for the lowest subband energy level and grows in size for the higher subband states. The effects of nonparabolicity have significant influence on the transition energies and the oscillator strengths and should be taken into account in the investigation of the optical transitions. The strong asymmetric property introduced by the step quantum well magnifies the weak intersubband transition from the ground state to the third state (1 -> 3). It is shown that in an appropriate scope, the intersubband transition (1 -> 3) has the comparable oscillator strength with transition from the ground state to the second one (1 -> 2), which suggests the possible application of the two-color photodetectors. The results of this work should provide useful guidance for the design of optically pumped asymmetric quantum well lasers and quantum well infrared photodetectors (QWIPs). (c) 2005 Elsevier B.V. All rights reserved.