Structure and electrochemical characteristics of melted composite Ti0.10Zr0.15V0.35Cr0.10Ni0.30-LaNi5 hydrogen storage alloys

The structure and electrochemical characteristics of melted composite Ti0.10Zr0.15V0.35Cr0.10Ni0.30+x% LaNi5 (x=0, 1, 5 and 10) hydrogen storage alloys have been investigated systematically. XRD shows that the matrix phase structure of V-based solid solution phase with a BCC structure and C14 Laves phase with hexagonal structure is not changed after adding LaNi5 alloy. However, the amount of the secondary phase increases with increasing LaNi5 content. Field emission scanning electron microscopy-energy dispersive spectroscopy (FESEM-EDS) shows that the C14 Laves phase contains more Zr and the white lard phase has a composition close to (Zr, Ti)(V, Cr, Ni, La)(2).

Structures and electrochemical characteristics of Ti0.26Zr0.07V0.24Mn0.1Ni0.33Mox (x=0-0.1) hydrogen storage alloys

Microstructures and electrochemical properties of Ti0.26Zr0.07V0.21Mn0.1Ni0.33Mox (x=0,0.025,0.05,0.075, 0.10) electrode alloys have been investigated. The results of XRD analysis show that the alloys are mainly composed of V-based solid solution phase with body centered cubic (bcc) structure and C14 Laves phase with hexagonal structure. The addition of Mo element can imp ove the activation characteristics, maximum discharge capacity and cyclic durability for the electrode alloys

Preparation and characterization of Gd2O3:Eu3+ luminescence nanotubes

The size controllable Gd2O3:Eu3+ luminescence nanotubes were successfully prepared using a simple method by coating gadolinium compounds on the carbon nanotubes and then firing the carbon nanotubes. The morphology of the obtained Gd2O3:Eu3+ nanotubes was determined by transmission electron microscopy (TEM). It was found that the obtained nanotubes have the outer diameters of similar to 100 nm, the inner diameters of similar to 50 nm, and the lengths of several tens of microns. The sizes of Gd2O3:Eu3+ nanotubes can be easily controlled by changing the reaction times and the concentration of reactants.

Combustion synthesis and luminescent properties of the Eu3+-doped yttrium oxysulfide nanocrystalline

Nanocrystallinc Y2O2S:Eu3+ was successfully prepared with a combustion synthesis method, the corresponding bulk Y2O2S:Eu3+ was synthesized by conventional sulfur flux method. The results of XRD indicated that both bulk and nanocrystalline Y2O2S:Eu3+ have Pure hexagonal phases. The crystallite size was calculated to be about 20 nm according to Scherrer formula, which was consistent with the size as indicated by transmission electron microscopy (TEM).