Nd3+-doped LaF3 nanoparticles with a larger emission cross-section

A series of Nd3+-doped LaF3 nanoparticles with Nd3+ concentrations from 0.5 to 10 mol% were synthesized. The fluorescence intensity and lifetime of the nanoparticles at various Nd3+ doping concentration were investigated. The nanoparticles displayed strongest fluorescence intensity at 3 mol% Nd3+ concentration. Eighty-eight percentage quantum efficiency was obtained when the Nd3+ concentration was 0.5 mol%. Optical properties of nanoparticles were studied according to Judd-Ofelt theory. A larger emission cross-section, sigma(em), for F-4(3/2) -> I-4(11/2) transition of the Nd3+ ion was obtained as 3.21 x 10(-20) cm(2), which was two times of the currently reported value. The larger emission cross-section and strong fluorescence intensity demonstrate that these nanoparticles are promising materials for laser applications. (C) 2010 Published by Elsevier B. V.

Electron spin dynamics in heavily Mn-doped (Ga,Mn)As

Electron spin relaxation and related mechanisms in heavily Mn-doped (Ga,Mn) As are studied by performing time-resolved magneto-optical Kerr effect measurements. At low temperature, s-d exchange scattering dominates electron spin relaxation, whereas the Bir-Aronov-Pikus mechanism and Mn impurity scattering play important roles at high temperature. The temperature-dependent spin relaxation time exhibits an anomaly around the Curie temperature (T(c)) that implies that thermal fluctuation is suppressed by short-range correlated spin fluctuation above T(c). (C) 2010 American Institute of Physics. [doi:10.1063/1.3531754]

Modification of C-doped a-SiO2 after Swift Heavy-Ion Irradiation

Amorphous SiO2 (a-SiO2) thin films were thermally grown on single-crystalline silicon. These a-SiO2/Si samples were first implanted (C-doped) with 100-keV carbon ion at room temperature (RT) at a dose of 5.0 x 10(17) C-ions/cm(2) and were then irradiated at RT by using 853 MeV Pb ions at closes of 5.0 x 10(11), 1.0 x 10(12), 2.0 x 10(12) and 5.0 x 10(12) Pb-ions/cm(2), respectively. The microstructures and the photoluminescence (PL) properties of these samples induced by Pb ions were investigated using fluorescence spectroscopy and transmission electron microscopy. We found that high-energy Pb-ion irradiation could induce the formation of a new phase and a change in the PL property of C-doped a-SiO2/Si samples. The relationship between the observed phenomena and the ion irradiation parameters is briefly discussed.