Effects of the high-temperature plasma immersion ion-implantation treatment on corrosion behavior of Ti-6Al1-4V

Nitrogen implantation into Ti alloys at higher temperatures improves their mechanical and corrosion resistance properties by forming a thicker nitride layer. In this paper, two different sets of Ti-6Al-4V samples were plasma immersion ion implantation (PIII)-treated using nitrogen plasma, varying the treatment time from 30 to 150 min (800 degrees C) and the process temperature from 400 degrees C to 800 degrees C (t = 60 min). Nanoindentation measurements of the PIII-treated samples at 800 C during 150 min showed the highest hardness value, 24 GPa, which is about four times bigger than untreated sample hardness. The N penetration at these conditions reached approximately 150 nm as analyzed by Auger spectroscopy. on the other hand, the lowest passive current density (3 x 10(-7) A. cm(-2)) was obtained for a PIII-treated sample during 30 min at higher temperature (800 degrees C). The corrosion resistance of this sample is almost the same as for the untreated specimen. Corrosion behavior evidenced that in strong oxidizing media, all PIII-treated samples are more corrosion resistant than the untreated one. PIII processing at higher temperatures promotes smoothing of the sample surface as observed by scanning electron microscopy (SEM). Grazing incidence X-ray diffraction analyses of the untreated samples identified the two typical Ti phases, Ti alpha and Ti beta. After the implantation, Ti2N and TiO2 phases were also detected.

Sol-gel prepared Pt-modified oxide layers: Synthesis, characterization, and electrocatalytic activity

Thin films of pure RuO2 and IrO2 and mixed Ru0.5Ir0.5O2 oxide modified with Pt particles were prepared by a sol-gel method in the form of thin films of similar to 2 mu m thickness on Ti substrates. Surface morphology of these Pt- modified oxides was examined by scanning electron microscopy and was found to exhibit a significant influence of the chemical composition of the oxide matrix. Element mapping showed homogeneous distribution of the metals. X- ray diffraction and X- ray photoelectron spectroscopy analyses showed that these films consist of metallic Pt particles dispersed in an oxide matrix. Cyclic voltammetry in acid solutions showed that the sol- gel prepared layers have relatively high Pt surface areas. The electrocatalytic activity of these materials toward the anodic oxidation of formaldehyde and methanol was compared in terms of onset potential and current density and was found to follow the sequence: Pt- Ru0.5Ir0.5O2/ Ti > Pt- RuO2/ Ti > Pt- IrO2/ Ti.

A multi-cell variable frequency interleaved ZCS boost rectifier digitally controlled by FPGA

This paper presents a multi-cell single-phase high power factor boost rectifier in interleave connection, operating in critical conduction mode, employing a soft-switching technique, and controlled by Field Programmable Gate Array (FPGA). The soft-switching technique is based on zero-current-switching (ZCS) cells, providing ZC (zero-current) turn-on and ZCZV (zero-current-zero-voltage) turn-off for the active switches, and ZV (zero-vohage) turn-on and ZC (zero-current) turn-off for the boost diodes. The disadvantages related to reverse recovery effects of boost diodes operated in continuous conduction mode (additional losses, and electromagnetic interference (EMI) problems) are minimized, due to the operation in critical conduction mode. In addition, due to the interleaving technique, the rectifier's features include the reduction in the input current ripple, the reduction in the output voltage ripple, the use of low stress devices, low volume for the EMI input filter, high input power factor (PF), and low total harmonic distortion (THD) in the input current, in compliance with the IEC61000-3-2 standards. The digital controller has been developed using a hardware description language (VHDL) and implemented using a XC2S200E-SpartanII-E/Xilinx FPGA device, performing a true critical conduction operation mode for all interleaved cells, and a closed-loop to provide the output voltage regulation, like as a preregulator rectifier. Experimental results are presented for a implemented prototype with two and with four interleaved cells, 400V nominal output voltage and 220V(rms) nominal input voltage, in order to verify the feasibility and performance of the proposed digital control through the use of a FPGA device.

Electrochemical oxidation of an acid dye by active chlorine generated using Ti/Sn(1-x)Ir O-x(2) electrodes

The generation of active chlorine on Ti/Sn(1-x)Ir (x) O-2 anodes, with different compositions of Ir (x = 0.01, 0.05, 0.10 and 0.30 ), was investigated by controlled current density electrolysis. Using a low concentration of chloride ions (0.05 mol L-1) and a low current density (5 mA cm(-2)) it was possible to produce up to 60 mg L-1 of active chlorine on a Ti/Sn0.99Ir0.01O2 anode. The feasibility of the discoloration of a textile acid azo dye, acid red 29 dye (C.I. 16570), was also investigated with in situ electrogenerated active chlorine on Ti/Sn(1-x)Ir (x) O-2 anodes. The best conditions for 100% discoloration and maximum degradation (70% TOC reduction) were found to be: NaCl pH 4, 25 mA cm(-2) and 6 h of electrolysis. It is suggested that active chlorine generation and/or powerful oxidants such as chlorine radicals and hydroxyl radicals are responsible for promoting faster dye degradation. Rate constants calculated from color decay versus time reveal a zero order reaction at dye concentrations up to 1.0 x 10(-4) mol L-1. Effects of other electrolytes, dye concentration and applied density currents also have been investigated and are discussed.

The role of oxygen vacancies on the microstructure development and on the electrical properties of SnO2-based varistors

Variations on the microstructure development and on the electrical properties of SnO2-based varistors are discussed on the basis of the oxygen vacancies created or annihilated by the presence of different additives. Electron paramagnetic resonance (EPR) analysis of sintered samples evidenced a substantial increase in the paramagnetic oxygen vacancies concentration when Nb2O5 is added to the SnO2 center dot Co3O4 system. on the other hand, the observed diminution in the concentration of such species after the addition of Fe2O3 indicates solid solution formation. The quantification of paramagnetic oxygen vacancies allowed to confirm the proposed substitutions taking place in the lattice during sintering. These findings are supported by scanning electron microscopy, by density measurements and by current density versus electric field curves. The characterization of secondary phases through EDS assisted SEM and TEM is also reported in this work.

Degradation of Acid Blue 40 dye solution and dye house wastewater from textile industry by photo-assisted electrochemical process

In this paper, electrochemical and photo-assisted electrochemical processes are used for color, total organic carbon (TOC) and chemical oxygen demand (COD) degradation of one of the most abundant and strongly colored industrial wastewaters, which results from the dyeing of fibers and fabrics in the textile industry. The experiments were carried out in an 18L pilot-scale tubular low reactor with 70% TiO2/30% RuO2 DSA. A synthetic acid blue 40 solution and real dye house wastewater, containing the same dye, were used for the experiments. By using current density of 80 mA cm(-2) electrochemical process has the capability to remove 80% of color, 46% of TOC and 69% of COD. When used the photochemical process with 4.6 mW cm(-2) of 254nm UV-C radiation to assist the electrolysis, has been obtained 90% of color, 64% of TOC and 60% of COD removal in 90 minutes of processing; furthermore, 70% of initial color was degraded within the first 15 minutes. Experimental runs using dye house wastewater resulted in 78% of color, 26% of TOC and 49% of COD in electrolysis at 80 mA cm(-2) and 90 min; additionally, when photo-assisted, electrolysis resulted in removals of 85% of color, 42% of TOC and 58% of COD. For the operational conditions used in this study, color, TOC and COD showed pseudo-first-order decaying profiles. Apparent rate constants for degradation of TOC and COD were improved by one order of magnitude when the photo-electrochemical process was used.

Electrical conduction mechanism and phase transition studies using dielectric properties and Raman spectroscopy in ferroelectric Pb0.76Ca0.24TiO3 thin films

We have studied the phase transition behavior of Pb0.76Ca0.24TiO3 thin films using Raman scattering and dielectric measurement techniques. We also have studied the leakage current conduction mechanism as a function of temperature for these thin films on platinized silicon substrates. A Pb0.76Ca0.24TiO3 thin film was prepared using a soft chemical process, called the polymeric precursor method. The results showed that the dependence of the dielectric constant upon the frequency does not reveal any relaxor behavior. However, a diffuse character-type phase transition was observed upon transformation from a cubic paraelectric phase to a tetragonal ferroelectric phase. The temperature dependency of Raman scattering spectra was investigated through the ferroelectric phase transition. The soft mode showed a marked dependence on temperature and its disappearance at about 598 K. on the other hand, Raman modes persist above the tetragonal to cubic phase transition temperature, although all optical modes should be Raman inactive above the phase transition temperature. The origin of these modes must be interpreted in terms of a local breakdown of cubic symmetry by some kind of disorder. The lack of a well-defined transition temperature suggested a diffuse-type phase transition. This result corroborate the dielectric constant versus temperature data, which showed a broad ferroelectric phase transition in the thin film. The leakage current density of the PCT24 thin film was studied at elevated temperatures, and the data were well fitted by the Schottky emission model. The Schottky barrier height of the PCT24 thin film was estimated to be 1.49 eV. (C) 2003 American Institute of Physics.

The influence of residual stress and crystallite size on the magnetic properties of electrodepo sited nanocrystalline Pd-Co alloys

Nanocrystalline Pd-Co alloys were obtained by electrodeposition from an ammoniacal chloride bath. The influence of the crystallite size and the residual stress on the magnetic properties of the alloys was investigated. The residual stress increased as the applied current density was increased. It was associated to the high nucleation rate during electrodeposition and correlated to the lattice strain, estimated from the XRD patterns. Also from the XRD patterns the average crystallite size and the lattice constant were determined by Scherrer's and Rietveld's methods, respectively. Both parameters were directly influenced by the applied current density. Magnetic properties such as coercivity, remanence, saturation magnetization and squareness showed strong dependence on the residual stress and crystallite size. Coercivity higher than 1 kOe was achieved when a high current density was applied. High coercivity was attributed to the presence of residual stress and to the small crystallite size of deposits. (C) 2007 Elsevier B.V. All rights reserved.