Conditions giving rise to intense visible room temperature photoluminescence in SrWO4 thin films: the role of disorder

The nature of intense visible photoluminescence at room temperature of SrWO4 (SWO) non-crystalline thin films is discussed in the light of experimental results and theoretical calculations. The SWO thin films were synthesized by the polymeric precursors method. Their structural properties have been obtained by X-ray diffraction data and the corresponding photoluminescence (PL) spectra have been measured. The UV-vis optical spectra measurements suggest the creation of localized states in the disordered structure. The photoluminescence measurements reveal that the PL changes with the degree of disorder in the SWO thin film. To understand the origin of visible PL at room temperature in disordered SWO, we performed quantum-mechanical calculations on crystalline and disordered SWO periodic models. Their electronic structures are analyzed in terms of DOS, hand dispersion and charge densities. We used DFT method with the hybrid non-local B3LYP approximation. The polarization induced by the symmetry break and the existence of localized levels favors the creation of trapped holes and electrons, giving origin to the room temperature photoluminescence phenomenon in the SWO thin films. (c) 2004 Elsevier B.V. All rights reserved.

Theoretical and experimental study of the relation between photoluminescence and structural disorder in barium and strontium titanate thin films

Thin films of barium and strontium titanate (BST), synthesized by the polymeric precursor solution and spin coated on [Pt (140nm)/Ti (10 nM)/SiO2(1000 nm)/Si] substrates were found to be photoluminescent at room temperature when heat treated below 973 K, i.e. before their crystallization. First principles quantum mechanical techniques, based on density functional theory (DFT) were employed to study the electronic structure of two periodic models: one is standing for the crystalline BST thin film and the other one for the structurally disordered thin film. The aim is to compare the photoluminescence (PL) spectra of the crystalline and disordered thin films with their UV-vis spectra and with their computed electronic structures. The calculations show that new localized states are created inside the band gap of the crystalline model, as predicted by the UV-vis spectra. The study of the charge repartition in the structure before and after deformation of the periodic model shows that a charge gradient appears among the titanate clusters. This charge gradient, together with the new localized levels, gives favorable conditions for the trapping of holes and electrons in the structure, and thus to a radiative recombination process. Our models are not only consistent with the experimental data, they also allow to explain the relations between structural disorder and photoluminescence at room temperature. (c) 2005 Elsevier Ltd. All rights reserved.

Contribution of structural order-disorder to the green photoluminescence of PbWO4

An intense and broad visible photoluminescence (PL) band was observed at room temperature in structurally disordered PbWO4 thin films. The scheelite lead tungstate (PbWO4) films prepared by the polymeric precursor method and annealed at different temperatures were structurally characterized by means of x-ray diffraction and atomic force microscopy analysis. Quantum-mechanical calculations showed that the local disorder of the network modifier (Pb) has a very important role in the charge transfer involved in the green PL emission. The experimental and theoretical results are in good agreement, both indicating that the generation of the intense visible PL band is related to simultaneous structural order and disorder in the scheelite PbWO4 lattice.

Auditory processing disorder in patients with language-learning impairment and correlation with malformation of cortical development

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Gaze pursuit and arm control of adolescent males diagnosed with attention deficit hyperactivity disorder (ADHD) and normal controls: evidence of a dissociation in processing visual information of short and long duration

Three-dimensional kinematic analysis of line of gaze, arm and ball was used to describe the visual and motor behaviour of male adolescents diagnosed with attention deficit hyperactivity disorder (ADHD). The ADHD participants were tested when both on (ADHD-On) and off (ADHD-Off) their medication and compared to age-matched normal controls in a modified table tennis task that required tracking the ball and hitting to cued right and left targets. Long-duration information was provided by a pre-cue, in which the target was illuminated approximately 2 s before the serve, and short-duration information by an early-cue illuminated about 350 ms after the serve, leaving -500 ms to select the target and perform the action. The ADHD groups differed significantly from the control group in both the pre-cue and early-cue conditions in being less accurate, in having a later onset and duration of pursuit tracking, and a higher frequency of gaze on and off the ball. The use of medication significantly reduced the gaze frequency of the ADHD participants, but surprisingly this did not lead to an increase in pursuit tracking, suggesting a barrier was reached beyond which ball flight information could not be processed. The control and ADHD groups did not differ in arm movement onset, duration and velocity in the short-duration early-cue condition; in the long-duration pre-cue condition, however, the ADHD group's movement time onset and arm velocity differed significantly from controls. The results show that the ADHD groups were able to process short-duration information without experiencing adverse effects on their motor behaviour; however, long-duration information contributed to irregular movement control.

Auditory processing disorder in perisylvian syndrome

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of the order and disorder of BaMoO4 powders in photoluminescent properties

The study of the photoluminescent properties affected by order and disorder of the BaMoO4 powders is the principal objective in this work. BaMoO4 compounds were prepared using soft chemical process called Complex Polymerization Method. In this work, different deagglomeration types and different heating rates were used to promote different disorder degrees. Scheelite type phase (BaMoO4) was determined by X-ray Diffraction (XRD), Fourier Transformed Infra-Red (FTIR) and Raman spectroscopy after heat treating the sample at 400 degrees C. The room temperature luminescence spectra revealed an intense single-emission band in the visible region. Based on XRD and Raman data it was observed that the transition between the completely disordered structure to completely ordered structure is a good condition for photoluminescence (PL) emission. The best PL emission is obtained when the material possesses short range disorder, i.e., is periodically ordered (XRD), but some disorder as measured by Raman spectroscopy. The excellent optical properties observed for disordered BaMoO4 suggested that this material is a highly promising candidate for optical applications.

Influence of structural disorder on the photoluminescence emission of PZT powders

Intense and broad visible photoluminescent (PL) band was observed at room temperature in disordered Pb(Zr(0.53)Ti(0.47))O(3) powders. Structural order-disorder was evaluated by different methods. XANES results pointed to the presence of different coordination modes of disordered Ti powders, and in the ordered sample the local structure around titanium atoms is characteristic of the structurally ordered PZT with only TiO(6) units. Only samples containing simultaneous structural order and disorder in their network present the intense visible PL emission at room temperature.

Disorder-dependent photoluminescence in Ba0.8Ca0.2TiO3 at room temperature

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of the modifier on the short and long range disorder of stannate perovskites

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)