Part I. Kinetics of coarsening of the gamma-prime precipitate in nickel-silicon alloys. Part II. Rate of crystallization of an amorphous Fe-P-C alloy

The coarsening kinetics of Ni₃ Si(γ') precipitate in a binary Ni-Si alloy containing 6.5 wt. % silicon was studied by magnetic techniques and transmission electronmicroscopy. A calibration curve was established to determine the concentration of silicon in the matrix. The variation of the Si content of the Ni-rich matrix as a function of time follows Lifshitz and Wagner theory for diffusion controlled coarsening phenomena. The estimated values of equilibrium solubility of silicon in the matrix represent the true coherent equilibrium solubilities.

The experimental particle-size distributions and average particle size were determined from dark field electron micrographs. The average particle size varies linearly with t^-1/3 as suggested by Lifshitz and Wagner. The experimental distributions of particle sizes differ slightly from the theoretical curve at the early stages of aging, but the agreement is satisfactory at the later stages. The values of diffusion coefficient of silicon, interfacial free energy and activation energy were calculated from the results of coarsening kinetics. The experimental value of effective diffusion coefficient is in satisfactory agreement with the value predicted by the application of irreversible the rmodynamics to the process of volume constrained growth of coherent precipitate during coarsening. The coherent γ' particles in Ni-Sialloy unlike those in Ni-Al and Ni-Ti seem to lose coherency at high temperature. A mechanism for the formation of semi-coherent precipitate is suggested.

Discontinuous yielding and fracture initiation near a notch in mild steel

This thesis presents the results of an experimental investigation of the initiation of brittle fracture and the nature of discontinuous yielding in small plastic enclaves in an annealed mild steel. Upper and lower yield stress data have been obtained from unnotched specimens and nominal fracture stress data have been obtained from specimens of two scale factors and two grain sizes over a range of nominal stress rates from 10^2 to 10^7 lb/in.^2 sec at -111°F and -200°F. The size and shape of plastic enclaves near the notches were revealed by an etch technique.

A stress analysis utilizing slip-line field theory in the plastic region has been developed for the notched specimen geometry employed in this investigation. The yield stress of the material in the plastic enclaves near the notch root has been correlated with the lower yield stress measured on unnotched specimens through a consideration of the plastic boundary velocity under dynamic loading. A maximum tensile stress of about 122,000 lb/in.^2 at the instant of fracture initiation was calculated with the aid of the stress analysis for the large scale specimens of ASTM grain size 8 1/4.

The plastic strain state adjacent to a plastic-elastic interface has been shown to cause the maximum shear stress to have a larger value on the elastic than the plastic side of the interface. This characteristic of dis continuous yielding is instrumental in causing the plastic boundaries to be nearly parallel to the slip-line field where the plastic strain is of the order of the Lüder's strain.

The tensile fracture of mild steel

The fibrous and cleavage tensile fracture of an annealed mild steel was investigated. Round tensile specimens of two geometries, one straight and one with a circumferential notch, were pulled at temperatures between room temperature and liquid nitrogen temperature. Tensile fractures occurred at average strains from 0.02 to 0.87. The mechanism of fibrous fracture at room temperature was investigated metallographically. The stress-strain values at which fibrous and cleavage fractures are initiated were determined.

Many fine microcracks, which are associated with pearlite colonies and inclusion stringers, develop prior to fibrous fracture. The macrofracture, which leads to final separation of the tensile specimen, is initiated by the propagation of a microcrack beyond the microstructural feature with which it is associated. Thus, the fibrous fracture of mild steel does not develop by the gradual growth and coalescence of voids that are large enough to be visible in the optical microscope. When the microcracks begin to open and propagate, final fracture quickly follows. Axial cracks are a prominent feature of the macrofracture that forms in the interior of the specimen immediately before final fracture.

The Bridgman distribution of stresses is not valid in a notched tensile specimen. Fibrous and cleavage fractures occur at approximately the same value of maximum tensile stress. When the maximum tensile stress that is necessary for cleavage fracture is plotted against the corresponding maximum tensile strain, the result is an unique locus.

Rate and Microstructure Effects on the Dynamics of Carbon Nanotube Foams

Soft hierarchical materials often present unique functional properties that are sensitive to the geometry and organization of their micro- and nano-structural features across different lengthscales. Carbon Nanotube (CNT) foams are hierarchical materials with fibrous morphology that are known for their remarkable physical, chemical and electrical properties. Their complex microstructure has led them to exhibit intriguing mechanical responses at different length-scales and in different loading regimes. Even though these materials have been studied for mechanical behavior over the past few years, their response at high-rate finite deformations and the influence of their microstructure on bulk mechanical behavior and energy dissipative characteristics remain elusive.

In this dissertation, we study the response of aligned CNT foams at the high strain-rate regime of 10² - 10⁴ s^-1. We investigate their bulk dynamic response and the fundamental deformation mechanisms at different lengthscales, and correlate them to the microstructural characteristics of the foams. We develop an experimental platform, with which to study the mechanics of CNT foams in high-rate deformations, that includes direct measurements of the strain and transmitted forces, and allows for a full field visualization of the sample’s deformation through high-speed microscopy.

We synthesize various CNT foams (e.g., vertically aligned CNT (VACNT) foams, helical CNT foams, micro-architectured VACNT foams and VACNT foams with microscale heterogeneities) and show that the bulk functional properties of these materials are highly tunable either by tailoring their microstructure during synthesis or by designing micro-architectures that exploit the principles of structural mechanics. We also develop numerical models to describe the bulk dynamic response using multiscale mass-spring models and identify the mechanical properties at length scales that are smaller than the sample height.

The ability to control the geometry of microstructural features, and their local interactions, allows the creation of novel hierarchical materials with desired functional properties. The fundamental understanding provided by this work on the key structure-function relations that govern the bulk response of CNT foams can be extended to other fibrous, soft and hierarchical materials. The findings can be used to design materials with tailored properties for different engineering applications, like vibration damping, impact mitigation and packaging.

Strength, Deformation and Fracture in Metallic Nanostructures

An understanding of the mechanics of nanoscale metals and semiconductors is necessary for the safe and prolonged operation of nanostructured devices from transistors to nanowire- based solar cells to miniaturized electrodes. This is a fascinating but challenging pursuit because mechanical properties that are size-invariant in conventional materials, such as strength, ductility and fracture behavior, can depend critically on sample size when materials are reduced to sub- micron dimensions. In this thesis, the effect of nanoscale sample size, microstructure and structural geometry on mechanical strength, deformation and fracture are explored for several classes of solid materials. Nanocrystalline platinum nano-cylinders with diameters of 60 nm to 1 μm and 12 nm sized grains are fabricated and tested in compression. We find that nano-sized metals containing few grains weaken as sample diameter is reduced relative to grain size due to a change from deformation governed by internal grains to surface grain governed deformation. Fracture at the nanoscale is explored by performing in-situ SEM tension tests on nanocrystalline platinum and amorphous, metallic glass nano-cylinders containing purposely introduced structural flaws. It is found that failure location, mechanism and strength are determined by the stress concentration with the highest local stress whether this is at the structural flaw or a microstructural feature. Principles of nano-mechanics are used to design and test mechanically robust hierarchical nanostructures with structural and electrochemical applications. 2-photon lithography and electroplating are used to fabricate 3D solid Cu octet meso-lattices with micron- scale features that exhibit strength higher than that of bulk Cu. An in-situ SEM lithiation stage is developed and used to simultaneously examine morphological and electrochemical changes in Si-coated Cu meso-lattices that are of interest as high energy capacity electrodes for Li-ion batteries.

Mortality, growth and growth rate variability of striped bass larvae in Chesapeake Subestuaries

In this report we develop age-length keys and derive age-frequency data. We estimate striped bass and white perch mortality and growth rates, based on the otolith-aging analysis. We also report on hatch-date frequencies of striped bass and white perch larvae, and we discuss environmental effects on recruitment potential.

Reference-growth rate – a simple and handy parameter summarizing the influence of environmental conditions

Abstract Environmental changes may have an impact on life conditions of the fish, e.g. food supply for the fish. The prevailing environmental conditions apply evenly to all age groups of one stock. Small fish have high growth rates, whereas large fish grow with low rates. But, it can be shown on the basis of the von Bertalanffy-growth model that it is sufficient to know only the growth rate of one single age group to compute the growth rates of all other age groups. The growth rate of a reference fish GRF (e.g. a fish with a body mass of 1 kg) was introduced as a reference growth describing the current food condition of all age groups of the stock. As an example a time series of the reference-growth rate of the northern cod stock (NAFO, 3K) was computed for the time span 1979 to 1999. For the northern cod stock it can be observed that environmental conditions caused growth rates below the long-term mean for seven years in a row. After a prolonged hunger period the fish stock collapsed in 1992 also by the impact of fisheries - and this was probably not a coincidence. Now, with the reference-growth rate GRF a simple and handy parameter was found to summarize the influence of the environmental conditions on growth and other derived models and therefore makes it easier to compute the influence of environmental changes within stock assessment. Zusammenfassung Veränderungen der Umwelt können Auswirkungen auf die Lebensbedingungen der Fische haben, z. B. auf das Nahrungsangebot der Fische. Die vorherrschenden Umgebungsbedingungen wirken gleichmäßig auf alle Altersgruppen eines Bestandes, wobei typischer Weise kleineFische hohe Wachstumsraten haben, während die großen Fische mit niedrigen Raten wachsen. Auf der Grundlage des von Bertalanffy-Wachstumsmodells kann gezeigt werden, dass es ausreicht, nur die Wachstumsrate von einer einzigen Altersgruppe zu kennen, um die Wachstumsraten von allen anderen Altersgruppen berechnen zu können. Die Wachstumsrate eines Referenz-Fisches (z.B. eines Fisches mit einer Körpermasse von 1 kg) wurde als Referenz-Wachstum GRF eingeführt, die den aktuellen Zustand des Nahrungsangebots füralle Altersgruppen des Bestandes beschreibt. Als Beispiel wurde einer Zeitreihe der Referenz-Wachstumsraten des nördlichen Kabeljaubestandes (NAFO, 3K) für die Zeitsraum 1979 bis 1999 berechnet. Für diesen Kabeljaubestand war zu beobachten, dass Umgebungsbedingungen für sieben Jahre in Folge Wachstumsraten unter dem langjährigen Mittelwert verursachten. Nach einer längeren Hungerperiode kollabierte dieser Fischbestand im Jahr 1992 auch durch den Einfluß der Fischerei - und dies war sicher kein Zufall. Jetzt, mit der Referenz-Wachstumsrate GRF, ist ein einfacher und handlicher Parameter gefunden, der es gestattet den Einfluss der Umweltbedingungen auf die Wachstumsbedingungen und andere davon abgeleitete Modelle zusammenzufassen. Dies macht es einfach, den Einfluss von Umweltveränderungen innerhalb der Bestandsabschätzungen zu berechnen.

I. The rate and mechanism of the vapor-phase reaction between water and parts-per-million concentrations of nitrogen dioxide. II. The rate and mechanism of the air oxidation of parts-per-million concentrations of nitric oxide in the presence of water vapor.

Part I

A study of the thermal reaction of water vapor and parts-per-million concentrations of nitrogen dioxide was carried out at ambient temperature and at atmospheric pressure. Nitric oxide and nitric acid vapor were the principal products. The initial rate of disappearance of nitrogen dioxide was first order with respect to water vapor and second order with respect to nitrogen dioxide. An initial third-order rate constant of 5.5 (± 0.29) x 10⁴ liter² mole^-2 sec^-1 was found at 25˚C. The rate of reaction decreased with increasing temperature. In the temperature range of 25˚C to 50˚C, an activation energy of -978 (± 20) calories was found.

The reaction did not go to completion. From measurements as the reaction approached equilibrium, the free energy of nitric acid vapor was calculated. This value was -18.58 (± 0.04) kilocalories at 25˚C.

The initial rate of reaction was unaffected by the presence of oxygen and was retarded by the presence of nitric oxide. There were no appreciable effects due to the surface of the reactor. Nitric oxide and nitrogen dioxide were monitored by gas chromatography during the reaction.

Part II

The air oxidation of nitric oxide, and the oxidation of nitric oxide in the presence of water vapor, were studied in a glass reactor at ambient temperatures and at atmospheric pressure. The concentration of nitric oxide was less than 100 parts-per-million. The concentration of nitrogen dioxide was monitored by gas chromatography during the reaction.

For the dry oxidation, the third-order rate constant was 1.46 (± 0.03) x 10⁴ liter² mole^-2 sec^-1 at 25˚C. The activation energy, obtained from measurements between 25˚C and 50˚C, was -1.197 (±0.02) kilocalories.

The presence of water vapor during the oxidation caused the formation of nitrous acid vapor when nitric oxide, nitrogen dioxide and water vapor combined. By measuring the difference between the concentrations of nitrogen dioxide during the wet and dry oxidations, the rate of formation of nitrous acid vapor was found. The third-order rate constant for the formation of nitrous acid vapor was equal to 1.5 (± 0.5) x 10⁵ liter² mole^-2 sec^-1 at 40˚C. The reaction rate did not change measurably when the temperature was increased to 50˚C. The formation of nitric acid vapor was prevented by keeping the concentration of nitrogen dioxide low.

Surface effects were appreciable for the wet tests. Below 35˚C, the rate of appearance of nitrogen dioxide increased with increasing surface. Above 40˚C, the effect of surface was small.