On post-instability processes in adiabatic shear in hot rolled steel

EXPERIMENTS carried out using a split Hopkinson torsional bar have shown that only one shear band develops in specimens of hot rolled steel which break during testing. We observed, however, that in specimens which were not deformed to failure, several fine shear bands appeared. We believe that these formed during the loading cycle before the appearance of the final shear band and were not due to the effect of unloading. So we developed a numerical model to study the evolution of shear banding from several finite amplitude disturbances (FADs) in both temperature and strain rate. This numerical model reveals the detailed processes by which the FADs evolve into a fully developed shear band and suggests that beyond instability, the so-called shear banding process consists of two stages: inhomogeneous shearing and true shear-banding. The latter is characterized by the collapse of the stress and an abrupt increase of the local shear strain rate.

A study of the mechanism of consolidating metal-powder under explosive-implosive shock-waves

A study of the two-dimensional flow pattern of particles in consolidation process under explosive-implosive shock waves has been performed to further understand the mechanism of shock-wave consolidation of metal powder, in which bunched low-carbon steel wires were used instead of powder. Pressure in the compact ranges from 6 to 30 GPa. Some wires were electroplated with brass, some pickled. By this means, the flow pattern at particle surfaces was observed. The interparticle bonding and microstructure have been investigated systematically for the consolidated specimens by means of optical and electron microscopy, as well as by microhardness. The experimental results presented here are qualitatively consistent with Williamson's numerical simulation result when particle arrangement is close packed, but yield more extensive information. The effect of surface condition of particle on consolidation quality was also studied in order to explore ways of increasing the strength of the compacts. Based on these experiments, a physical model for metal powder shock consolidation has been established.

Orthotropy rescaling and implications for fracture in composites

For most practically important plane elasticity problems of orthotropic materials, stresses depend on elastic constants through two nondimensional combinations. A spatial rescaling has been found to reduce the orthotropic problems to equivalent problems in materials with cubic symmetry. The latter, under favorable conditions, may be approximated by isotropic materials. Consequently, solutions for orthotropic materials can be constructed approximately from isotropic material solutions or rigorously from cubic ones. The concept is developed to gain insight into the interplay between anisotropy and finite geometry. The inherent simplicity of the solutions allows a variety of technical problems to be addressed efficiently. Included are stress concentration related cracking, effective contraction of orthotropic material specimens, crack deflection onto easy fracture planes, and surface flaw induced delamination.

Orientation preference and fractal character of short fatigue cracks in a weld metal

Short fatigue crack behaviour in a weld metal has been further investigated. The Schmid factor and the fractal dimension of short cracks on iso-stress specimens subjected to reversed bending have been determined and then applied to account for the distribution and orientation characteristics of short fatigue cracks. The result indicates that the orientation preference of short cracks is attributed to the large values of Schmid factor at relevant grains. The Schmid factors of most slip systems, which produced short cracks, are less than or equal to 0.4. Crack length measurements reveal that short crack path, compared to that of long crack, possesses a more stable and relatively larger value of fractal dimension. This is regarded as one of the typical features of short cracks.

Ballistic impact of ceramics

The impact behaviour of a range of glass and ceramic materials has been studied using high-speed photography. A gas gun was used to project hardened spheres at plate specimens in the velocity range 30 to 1000m s-1. The target materials included soda-lime glass, boron carbide and various glass ceramics and aluminas. The performance of a particular ceramic was found to depend on a combination of parameters but of key importance was the relative hardness of the projectile and target materials. The fracture toughness, K(IC), had only a secondary effect.

Creep behavior of woven roving grp beam in three-point bending

The creep and relaxation behaviour of laminated glass fibre reinforced plastics (GRP) in three-point bending were studied both experimentally and analytically. Creep and relaxation experiments were carried out on eight types of specimens, consisting of glass fibre fabric reinforced epoxy beams. While the bending deflexion and creep strains were measured in the creep tests, the load and relaxation strain were recorded in the relaxation tests. Marked creep effects were seen in the tests, where the environment temperature was 50°C and the period of the measurement was 60 min. An attempt to predict the creep deflexion and relaxation behaviour was made. The transverse shear effect on creep deflexion was taken into account. The predicted results were compared with experimental ones. They were found to be in reasonable agreement, but the linearization assumption, upon which the relaxation behaviour analysis was based, appears to lead to larger inaccuracies in the results.

Thermophoretic deposition of particles in gas flowing over cold surfaces

Some of the calculated parameters show a maximum value for specimens heat-treated at about 100°C. The tensile strength is, for instance, substantially higher for specimens shock-heated at 100°C than for non-heated ones. Another striking feature is the initial decrease of the diameter observed in specimens heat-treated at 600°C when loaded in uniaxial compression. Both optical microscopy and DSA experiments reveal a large increase in microcracking when the heat-treatment temperature exceeds 300°C.

Static and fatigue failure behavior of carbon-fiber reinforced epoxy composite-materials with edge notch

A study of carbon fiber reinforced epoxy composite material with 0° ply or ±45°ply(unnotched or with edge notch) was carried out under static tensile and tension-tensioncyclic loading testing. Static and fatigue behaviour and damage failure modes in unnotched/notched specimens plied in different manners were analysed and compared with each other.A variety of techniques (acoustic emission, two types of strain extensometer, high speed pho-tography, optical microscopy, scanning electron microscope, etc.) were used to examine thedamage of the laminates. Experimental results show that when these carbon/epoxy laminateswith edge notch normal to the direction of the load are axially loaded in static or fatiguetension, the crack does not propagate along the length of notch but is in the interface (fiberdirection). The notch has no substantial effect on the stresses at the unnotched portion. Thedamage failure mechanism is discussed.

Elastic-plastic finite element analyses of short cracks

Stress and strain distributions and crack opening displacement characteristics of short cracks have been studied in single edge notch bend and centre cracked panel specimens using elastic–plastic finite element analyses incorporating both a non strain hardening and a power law hardening behaviour. J contour integral solutions to describe stress strain conditions at crack tips for short cracks differ from those for long cracks. The analyses show that (i) short cracks can propagate at stress levels lower than those required for long cracks and (ii) a two-parameter description of crack tip fields is necessary for crack propagation.

高压扭转铜试样的微观组织与压缩性能

通过高压扭转对铜试样施加不同程度的变形，研究了样品扭转面（ND面）和纵截面（TD面）上微观组织特征．对ND面，在较小的剪应变下，原始晶粒形貌模糊，晶粒内部形成等轴状的位错胞及亚晶结构；随变形量的增大，亚晶间取向差及亚晶内部的位错密度增大，最后形成亚微米尺度的等轴晶粒．对TD面，变形初期原始晶粒被拉长，晶粒内部为位错墙分割成的层状结构，层内为拉长的位错胞；随变形程度的增大，拉长晶粒的宽度减小，与剪切方向的夹角减小，晶内层状组织间距减小，并逐渐演化成拉长的亚晶组织；进一步增大变形，晶粒拉长痕迹消失，变形组织与ND面相似，为等轴状亚微米晶粒．压缩实验表明，经16圈扭转后，整个试样上的压缩性能基本均匀，σ0．2达到385MPa，应变率敏感性指数增大至0．021．

Descriptions of new fishes from Panama

The following preliminary descriptions are of new fishes obtained by the authors during their first season's work on the Biological Survey of the Canal Zone, the ichthyological work of which is being conducted cooperatively by the Field Museum of Natural History and the Smithsonian Institution. (2 page document)

Two new subspecies of birds from Panama

While working on the Smithsonian Biological Survey of the Canal Zone, Mr. E. A. Goldman of the Biological Survey, United States Department of Agriculture, collected specimens of two undescribed subspecies of birds which are characterized below. (Document contains 3 pages)

New species of fishes from Panama

The fishes described in the following pages were collected by the authors in the fresh waters of Panama, while engaged in field work on the Biological Survey of the Canal Zone; the ichthyological work of which is being conducted cooperatively by the Smithsonian Institution, the Field Museum of Natural History and the Bureau of Fisheries. A complete account of all the fishes collected during the past two years on this survey is in the course of preparation. (Document contains 16 pages)

PICES Press, Vol. 13, No. 2, July 2005

PICES in transition: The 3rd inter-sessional Science Board and Governing Council meeting (pdf 0.3 MB) New and upcoming PICES publications (pdf 0.3 MB) PICES hosts GLOBEC Symposium on “Climate Variability and Sub-Arctic Marine Ecosystems” in Victoria (pdf 0.4 MB) First CREAMS/PICES Workshop on East Asian Seas Time-series (pdf 0.4 MB) PICES workshop discusses Oceanic Ecodynamics COmparison in the Subarctic Pacific (OECOS) - a project proposal (pdf 0.3 MB) The state of the western North Pacific in the second half of 2004 (pdf 0.4 MB) The Bering Sea: Current status and recent events (pdf 0.3 MB) Recent trends in waters of the subarctic NE Pacific (pdf 0.3 MB) CFAME workshop on “Developing a working plan for CCCC synthesis” (pdf 0.5 MB) What is winter? (pdf 0.5 MB) The first specimens of Humboldt squid in British Columbia (pdf 0.4 MB) Obituary - Dr. Daniel M. Ware (pdf 0.3 MB) PICES Calendar (pdf 0.3 MB)

Thermal Residual Stresses in SiCw/Al Composite

<正> The SiCw/6061Al composites were fabricated by squeeze casting method. Varia-tions of thermal residual stresses with quenching temperature, cooling manner, aging time and thethermal-cold cycle process in thin specimens,and the distributions of thermal residual stresses alongthe distances from the surface and changes with heating temperatnres in thick specimens were stud-ied by means of X-ray diffraction (XRD). The effects of residual stresses on the mierostructure, di-mensional stability and age-hardening behavior were studied by SEM, TEM observations, and tensiletest. The results showed that there existed macrostress, microstress and thermal mismatch stress inSiCw/Al compo-site,and the presence of microstress and thermal mismatch stress has no influenceon the measurement of macrostress, but the macrostress can affect the measured value of thermalmismatch stress. Thermal res dual stress induced during the composite fabrication process, will be further in-creased when the composite were subjected to the e