Planar and UV written channel optical waveguides prepared with siloxane poly(oxyethylene)-zirconia organic-inorganic hybrids. Structure and optical properties

Organic-inorganic hybrids were prepared using ureapropyltriethoxysilane, methacryloxypropyltrimethoxysilane and acrylic acid modified zirconium(IV) n-propoxide precursors and were characterized by small angle X-ray scattering, X-ray diffraction and photoluminescence spectroscopy. The results indicate an effective interaction between the zirconium-based nanoparticles and the siliceous nanodomains that induces changes in the hybrids' emission features. Planar waveguides were obtained by spin-coating of the prepared sols on sodalime and silica substrates. Refractive index, thickness, number of propagating modes, and attenuation coefficient were measured at 543.5, 632.8 and 1550 nm by the prism coupling technique. The synergism between the two hybrid precursors resulted in monomode planar waveguides with low losses in the infrared ( from 0.6-1.1 dB cm(-1)) which also support a number of propagating modes in the visible ( losses from 0.4-1.5 dB cm(-1)). Channel waveguides were also obtained by UV photopatterning using amplitude or phase masks and propagating modes were observed at 1550 nm.

Relation between photoluminescence emission and local order-disorder in the CaTiO3 lattice modifier

In this letter, the authors propose that photoluminescence emission in CaTiO3 is affected not only by disorder in the lattice former but also by structural disorder in the lattice modifier. Structural disorder was evaluated by Ti, Ca K-edge x-ray absorption near-edge structure experiments and by photoluminescence emission. The preedge feature of the Ca K edge was related to the intensity of photoluminescence emission. The results of the preedge feature of the Ca K-edge x-ray absorption near-edge structure confirm the presence of different Ca coordination numbers, namely, Ca-O-11 and Ca-O-12. (c) 2007 American Institute of Physics.

Photoluminescence in amorphous zirconium titanate

Photoluminescence at room temperature was observed in amorphous zirconium titanate obtained from the polymeric precursor method. This was the first time in which PL was noticed in an amorphous compound made of two network formers. The PL spectra could be deconvoluted into two bands, whose center 1 was located from 540 nm to 552 nm and center 2 from 625 nm to 641 nm. The co-existence of fivefold and sixfold oxygen coordination of titanium and/or zirconium could be the origin of the radiative recombination of electron-hole pairs in amorphous ZT, which may be responsible for the emission of the photoluminescence.

Reversible holographic glasses using visible lasers

Antimony based glasses have been investigated for the first time regarding the possibility of holographic data storage using visible lasers sources. Changes in both refractive index and the absorption coefficient were measured using a holographic setup. The modulation of the optical constants is reversible by heat treatment. Bragg gratings were written under visible light of an Ar laser and erased thermally.

Photoluminescence at room temperature in disordered Ba(0.50)Sr(0.)5(0)(Ti0.80Sn0.20)O-3 thin films

Photoluminescence (PL) properties at room temperature of disordered Ba0.50Sr0.50(Ti0.80Sn0.20)O-3 (BST:Sn) thin films were obtained by the polymeric precursor method. X-ray diffraction data and corresponding PL properties have been measured using the 488 nm line of an argon ion laser. The PL spectra of the film annealed at 350 degrees C for 21 h are stronger than those of the film annealed at 350 degrees C for 28 h, indicating a disorganized structure. The energy band gaps of the crystalline and amorphous BST:Sn thin films were 3.35 and 2.25 eV, respectively. The doped BST thin films also tend to a cubic structure, resulting from TiO6 deformations. (c) 2006 American Institute of Physics.