High-temperature hysteresis and magnetization reversal in nanocomposite FeCo plus MnO

The hysteretic behavior of mechanically alloyed nanocomposites FeCo + MnO was studied at high temperatures. These composites present an unusual high and thermally stable coercivity, compared to FeCo milled at equal conditions. Coercivity enhancement was observed in hysteresis loops obtained between room temperature and 750 K. It is attributed to the isolation of the FeCo ferromagnetic particles by the paramagnetic MnO (T(N) = 120 K). The M(rev)(M(irr))(H) curves are clearly linear for the composite, indicating that coherent rotation is the reversal mechanism in these materials. (C) 2008 Elsevier B.V. All rights reserved.

Magnetic and structural properties of NiFe(2)O(4) ferrite nanopowder doped with Zn(2+)

This work involved an investigation to ascertain how the substitution of nickel ions for zinc ions affects the structural, morphological and magnetic properties of NiFe(2)O(4) ferrite samples. Ni(1-x)Zn(x)Fe(2)O(4) (x = 0.0, 0.3 0.5, 0.7) powders were prepared by combustion reaction and characterized structurally by X-ray diffraction. The specific surface area of the powders was determined by the nitrogen adsorption method (BET). Magnetization measurements were taken using an alternative gradient magnetometer (AGM), which revealed that the powders prepared by combustion reaction resulted in nanosized particles with a particle size of 18-27 nm. The crystallite size and lattice parameter increased as the concentration of Zn increased. Moreover, augmenting the Zn content in the NiFe(2)O(4) ferrite increased the saturation magnetization and coercive field. (C) 2008 Elsevier B.V. All rights reserved.

Ni-Zn-Sm nanopowder ferrites: Morphological aspects and magnetic properties

Ni-Zn ferrites have been widely used in components for high-frequency range applications due to their high electrical resistivity, mechanical strength and chemical stability. Ni-Zn ferrite nanopowders doped with samarium with a nominal composition of Ni0.5Zn0.5Fe2-xSmxO4 (x = 0.0, 0.05, and 0.1 mol) were obtained by combustion synthesis using nitrates and urea as fuel. The morphological aspects of Ni-Zn-Sm ferrite nanopowders were investigated by X-ray diffraction, nitrogen adsorption by BET, sedimentation, scanning electron microscopy and magnetic properties. The results indicated that the Ni-Zn-Sm ferrite nanopowders were composed of soft agglomerates of nanoparticles with a high surface area (55.8-64.8 m(2)/g), smaller particles (18-20 nm) and nanocrystallite size particles. The addition of samarium resulted in a reduction of all the magnetic parameters evaluated, namely saturation magnetization (24-40 emu/g), remanent magnetization (2.2-3.5 emu/g) and coercive force (99.3-83.3 Oe). (c) 2007 Elsevier B. V. All rights reserved.

Magnetic interaction in exchange-biased bilayers: a first-order reversal curve analysis

The distributions of coercivities and magnetic interactions in a set of polycrystalline Ni(0.8)Fe(0.2)/FeMn bilayers have been determined using the first-order reversal curve (FORC) formalism. The thickness of the permalloy (Py) film was fixed at 10 nm (nominal), while that of the FeMn film varied within the range 0-20 nm. The FORC diagrams of each bilayer displayed two clearly distinguishable regions. The main region was generated by Py particles whose coercivities were enhanced in comparison with those in which the FeMn film was absent (sample O). The minor region was produced by Py particles with coercivities similar to or slightly higher than those of particles in the Py film of sample O. Each sample presented two distributions of interaction fields, one for each region, and both were centred slightly below the exchange-bias field, thus indicating a prevalence of magnetizing interactions. These results are consistent with a grain size distribution in the Py layer and the presence of uncompensated antiferromagnetic moments.

Synthesis and characterization of glass-ceramic microspheres for thermotherapy

Glass microspheres containing radionuclides are used to treat liver cancer. A promising alternative therapy is being developed based on the magnetic hyperthermia which is related to the heat supplied by a magnetic material under an alternating current magnetic field. The advantage of this option is that most of killed cells are cancer cells which are more susceptible to the temperature raise. In the present work aluminum iron silicate glasses containing minor glass modifiers and nucleating agents were synthesized as irregular shape particles which were further transformed in microspheres by using a petrol liquefied gas-oxygen torch. The optimized processing parameters which lead to microspheres that give a response to the magnetic field were determined. The dissolution rate in water at 90 degrees C was determined to be 3 x 10(-8) g cm(-2) min(-1). The microsphere size distribution was determined by laser scattering. The crystalline phase responsible for the ferromagnetic response was identified as magnetite. Since this phase has a high saturation magnetization and high Curie temperature, it is potentially useful for biomedical applications. The hysteresis magnetic loop was measured for materials produced in different conditions, and some of them showed to be appropriated for thermotherapy. The ratio Fe(3+)/Fe(total) was determined by Mossbauer spectroscopy. (C) 2010 Elsevier B.V. All rights reserved.

First-order-reversal-curve analysis of Pr-Fe-B-based exchange spring magnets

Ribbons of nominal composition (Pr(9.5)Fe(84.5)B(6))(0.96)Cr(0.01)(TiC)(0.03) were produced by arc-melting and melt-spinning the alloys on a Cu wheel. X-ray diffraction (XRD) reveals two main phases, one based upon alpha-Fe and the other upon Pr(2)Fe(14)B. The ribbons show exchange spring behavior with H (c) = 12.5 kOe and (BH)(max) = 13.6 MGOe when these two phases are well coupled. Transmission electron microscopy revealed the coupled behavior is observed when the microstructure consists predominantly of alpha-Fe grains (diameter similar to 100 nm.) surrounded by hard material containing Pr(2)Fe(14)B. The microstructure is discussed in terms of a calculation by Skomski and Coey. A first-order-reversal-curve (FORC) analysis was performed for both a well-coupled sample and a poorly coupled sample. The FORC diagrams show two strong peaks for both the poorly coupled sample and for the well-coupled material. In both cases, the localization of the FORC probability suggests magnetizing interactions between particles. Switching field distributions were calculated and are consistent with the sample microstructure.

Effect of urea and glycine fuels on the combustion reaction synthesis of Mn-Zn ferrites: Evaluation of morphology and magnetic properties

The goal of this study is to evaluate the influence of the urea and glycine fuels on the synthesis of Mn-Zn ferrite by combustion reaction The morphology and magnetic properties of the resulting powders were investigated. The powders were characterized by X-ray diffraction (XRD), nitrogen adsorption (BET), scanning and transmission electron microscopy (SEM and TEM), and magnetic measurement of M x H curves. The X-lay diffraction patterns indicated that the samples containing urea resulted in the formation of crystalline powders and the presence of hematite as a secondary phase The samples containing glycine presented only the formation of crystalline and monophases (Mn,Zn)Fe(2)O(4). The average crystallite size was 18 and 35 nm and saturation magnetization was 3.6 and 75 emu/g, respectively, for the samples containing urea and glycine. The samples synthesized with glycine fuel showed better magnetic properties for application as soft magnetic devices. (C) 2009 Elsevier B.V All rights reserved

First-order-reversal-curve analysis of Pr-Fe-B-based nanocomposites

Ribbons of nominal composition (Pr(9.5)Fe(84.5)B(6))(0.96)Cr(0.01)(TiC)(0.03) were produced by arc-melting and melt-spinning the alloys on a Cu wheel. X-ray diffraction reveals two main phases, one based upon alpha-Fe and the other upon Pr(2)Fe(14)B. The ribbons show exchange spring behavior with H(c)=12.5 kOe and (BH)(max)= 13.6 MGOe when these two phases are well coupled. Transmission electron microscopy revealed that the coupled behavior is observed when the microstructure consists predominantly of alpha-Fe grains(diameter similar to 100 nm.) surrounded by hard material containing Pr(2)Fe(14)B. A first-order-reversal-curve (FORC) analysis was performed for both a well-coupled sample and a partially-coupled sample. The FORC diagrams show two strong peaks for both the partially-coupled sample and for the well coupled material. In both cases, the localization of the FORC probability suggests demagnetizing interactions between particles. Switching field distributions were calculated and are consistent with the sample microstructure. (C) 2009 Elsevier B.V. All rights reserved.

Influence of calcination temperature on the morphology and magnetic properties of Ni-Zn ferrite applied as an electromagnetic energy absorber

An evaluation was made of the influence of calcination temperatures on the structure, morphology and eletromagnetic properties of Ni-Zn ferrite powders. To this end, Ni(0.5)Zn(0.5)Fe(2)O(4) ferrite powders were prepared by combustion reaction and calcined at temperatures of 800, 1000 and 1200 degrees C/2 h. The resulting powders were characterized by XRD, SEM and reflectivity measurements in the frequency bands of 8-12 GHz. The results demonstrated that raising the calcination temperature increased the particle sizes of the powders of all the systems in question, improving the reflectivity of the materials. (C) 2008 Elsevier B.V. All rights reserved.

Structural and magnetic properties of chromium-doped ferrite nanopowders

This paper reports on a study of Cr(3+)-doped nanosized Ni-Zn ferrites produced by combustion reaction, and evaluates their morphological and magnetic properties. The powders were characterized by X-ray diffraction (XRD) and SEM and magnetic properties. All the compositions showed the formation of the inverse spinel phase of Ni-Zn ferrite. The average crystallite size ranged from 21 to 26 nm. The saturation magnetization was found to be in the range of 53-43 emu/g. The increase in Cr(3+) concentration in the Ni-Zn ferrite caused a reduction in hysteresis losses and a slight reduction in the saturation magnetization. (C) 2008 Elsevier B.V. All rights reserved.

First order reversal curve analysis of nanocrystalline Pd(80)Co(20) alloy films

Films of isotropic nanocrystalline Pd(80)Co(20) alloys were obtained by electrodeposition onto brass substrate in plating baths maintained at different pH values. Increasing the pH of the plating bath led to an increase in mean grain size without inducing significant changes in the composition of the alloy. The magnetocrystalline anisotropy constant was estimated and the value was of the same order of magnitude as that reported for samples with perpendicular magnetic anisotropy. First order reversal curve (FORC) analysis revealed the presence of an important component of reversible magnetization. Also, FORC diagrams obtained at different sweep rate of the applied magnetic field, revealed that this reversible component is strongly affected by kinetic effect. The slight bias observed in the irreversible part of the FORC distribution suggested the dominance of magnetizing intergrain exchange coupling over demagnetizing dipolar interactions and microstructural disorder. (c) 2009 Elsevier B.V. All rights reserved.

Mechanisms of TL for production of the 230 degrees C peak in natural sodalite

The thermoluminescence (TL) peak in natural sodalite near 230 degrees C which appears only after submitted to thermal treatments and to gamma irradiation has been studied in parallel with electron paramagnetic resonance (EPR) spectrum appearing under the same procedure This study revealed a full correlation between the 230 degrees C TL peak and the eleven hyperfine lines from EPR spectrum In both case the centers disappear at the same temperature and are restored after gamma irradiation A complete model for the 230 C TL peak is presented and discussed In addition to the correlation and TL model specific characteristics of the TL peaks are described (C) 2010 Elsevier B V All rights reserved

Dating archeological ceramics from the Valley of Vitor, Arequipa by the TL method

The age of some ancient pottery from the Valley of Vitor in the region of Arequipa, Peru, is determined by the thermoluminescence (TL) method. For dating, a 325 degrees C TL peak was used and irradiation with -dose from 5 to 50Gy was carried out for the additive method, and from 0.4 to 5Gy for the regeneration method. For these dose values, the TL intensity is observed to grow linearly, obtaining an accumulated dose of 1.62 +/- 0.09Gy and 1.36 +/- 0.03Gy for the additive and regeneration methods, respectively. The age (A) of the sample was calculated by the two methods, being A=867 +/- 195 years after Christ (AC) for the additive method and A=1050 +/- 157 years AC for the regeneration method. Both results are within 800-1200 years AC, which is the period of the Wari culture.

Cyclocreatine, an anticancer and neuroprotective agent. Spectroscopic, structural and theoretical study

The structural, spectroscopic and theoretical study of cyclocreatine (1-carboxymethyl-2-iminoimidazolidine, CyCre) has been performed prompted by the biological relevance of the molecule and its potential role as a ligand in biometalic compounds. The crystal structure of CyCre has been determined by X-ray diffraction methods. The compound crystallizes as a zwitterion in the monoclinic system, space group P2(1)/c. The crystal is further stabilized by a network of N-H center dot center dot center dot O bonds. Infrared and Raman spectra of the solid, electronic spectra of aqueous solutions at different pH values and (1)H and (13)C NMR spectra have been recorded and analyzed. Band assignments were accomplished with the help of theoretical calculations. Optimized molecular geometries, harmonic vibrational frequencies and molecular electrostatic potentials were calculated using methods based on the density functional theory. (C) 2010 Elsevier B.V. All rights reserved.

A multivariate ultrastructural errors-in-variables model with equation error

This paper deals with asymptotic results on a multivariate ultrastructural errors-in-variables regression model with equation errors Sufficient conditions for attaining consistent estimators for model parameters are presented Asymptotic distributions for the line regression estimators are derived Applications to the elliptical class of distributions with two error assumptions are presented The model generalizes previous results aimed at univariate scenarios (C) 2010 Elsevier Inc All rights reserved