Enhancement of the electrooxidation of ethanol on Pt-Sn-P/C catalysts prepared by chemical deposition process

In this paper, five Pt3Sn1/C catalysts have been prepared using three different methods. It was found that phosphorus deposited on the surface of carbon with Pt and Sn when sodium hypophosphite was used as reducing agent by optimization of synthetic conditions such as pH in the synthetic solution and temperature. The deposition of phosphorus should be effective on the size reduction and markedly reduces PtSn nanoparticle size, and raise electrochemical active surface (EAS) area of catalyst and improve the catalytic performance. TEM images show PtSnP nanoparticles are highly dispersed on the carbon surface with average diameters of 2 nm. The optimum composition is Pt3Sn1P2/C (note PtSn/C-3) catalyst in my work. With this composition, it shows very high activity for the electrooxidation of ethanol and exhibit enhanced performance compared with other two Pt3Sn1/C catalysts that prepared using ethylene glycol reduction method (note PtSn/C-EG) and borohydride reduction method (note PtSn/-B). The maximum power densities of direct ethanol fuel cell (DEFC) were 61 mW cm(-2) that is 150 and 170% higher than that of the PtSn/C-EG and PtSn/C-B catalyst.

Thermal and crystallization behaviors of polyethylene blends synthesized by binary late transition metal catalysts combinations

A series of reactor blends of linear and branched polyethylenes have been prepared, in the presence of modified methylaluminoxane, using a combination of 2,6-bis[1(2,6-dimethyphenylimino) pyridyl]-cobalt(II) dichloride (1), known as an active catalyst for producing linear polyethylene, and [1,4-bis(2,6-diidopropylphenyl)] acenaphthene diimine nickel(II) dibromide (2), which is active for the production of branched polyethylene. The polymerizations were performed at various levels of catalyst feed ratio at 10 bar. The linear correlation between catalyst activity and concentration of catalyst 2 suggested that the catalysts performed independently from each other. The weight-average molecular weights ((M) over bar (w)), crystalline structures, and phase structures of the blends were investigated, using a combination of gel permeation chromatography, differential scanning calorimetry, wide-angle X-ray diffraction, and small angle X-ray scattering techniques. It was found that the polymerization activities and MWs and crystallization rate of the polymers took decreasing tendency with the increase of the catalyst 2 ratios, while melting temperatures (T-m), crystalline temperatures (T,), and crystalline degrees took decreasing tendency. Long period was distinctly influenced by the amorphous component concentration.

One-pot synthesis of polyimides via Ni-catalyzed coupling of bis(chlorophthalimide)s

A one-pot synthesis method for the preparation of polyimides containing biphenyl units was developed via nickel-catalyzed coupling reaction of bis(chlorophthalimide)s which were prepared from chloroplithalic anhydrides and diamines in xylene. The resulting polyimides had inherent viscosities of above 0.60dL g(-1). In the meantime, the copolymerizations from a mixture of three isomeric bis(chlorophthalimide)s gave the polymers with inherent viscosities of 0.36-0.55 gdL(-1). The solubility and film formability of the copolymers were better than those of homopolymers from bis(4-chlorophthalimide). The 10% weight loss of these polyimides was between 470 and 531 degrees C.

Effect of La3+ on structure and electrochemical reaction of microperoxidase-11 in imitated physiological solution

In this paper, the interaction mechanism between La3+ and microperoxidase-11 (MP-11) in the imitated physiological solution was investigated with the electrochemical and spectroscopic methods. It was found that when the molar ratio of La3+, and MP-11 is low, such as 2, La3+ can coordinate with oxygen in the propionic acid group of the heme group in the MP-11 molecule, forming the La-MP-11 complexes and leading to the increase in the non-planarity of the porphyrin cycle in the heme group and then the increase in the extent of exposure of the electrochemically active center, Fe(I I I) in the porphyrin cycle of the heme group. The increase in the extent of exposure of the electrochemically active center, Fe(III) in the porphyrin cycle of the heme group would increase the reversibility of the electrochemical reaction of the La-MP-11 complexes and its electrocatalytic activity for the reduction of H2O2. The results of the chromatographic analysis demonstrated that the average molar ratio of La3+ and MP-11 in the La-MP-11 complexes is 1.62.When the molar ratio of La3+ and MP-11 is high, such as 3, La3+ would shear some amino acid residues of the peptide of MP-11. Therefore, many La3+ ions can bind to the oxygen- and/or nitrogen-containing groups in the sheared amino acid residues except coordinating with the sheared and non-sheared MP-11 molecules.

Interaction between La3+ and MP-11 in the physiological solution

In this paper, the interaction between La3+ and microperoxidase-11 (MP-11) in the imitated physiological solution was investigated with the electrochemical method, circular dichroism (CD) and ultraviolet-visible (UV-vis) absorption spectroscopy. It was found that the interaction ways between La3+ and MP-11 are different with increasing the molar ratio of La3+ and MP-11. When the molar ratio of La3+ and MP-11 is less than 2, La3+ mainly interacts with the metacetonic acid group of the heme group in the MP-11 molecules, causing the increase in the non-planarity of the porphyrin cycle in the heme group and the decrease in the content of the random coil conformation of MP-11. These structural changes would increase the exposure extent of the electrochemical active center of MP-11 and thus, La3+ can promote the electrochemical reaction of MP-11 and its electrocatalytic activity for the reduction of H2O2 at the glassy carbon (GC) electrode. However, when the molar ratio of La3+ and MP-11 is larger than 3, except binding to the carbonyl oxygen of the metacetonic acid group in the heme group, La3+ interacts also with the oxygen-containing groups of the amides in the polypeptide chains of the MP-11 molecules, leading to the increase in the contents of the random coil conformation in the peptide of the MP-11 molecule, comparing with that for the molar ratio of less than 2.

Polypropylene as a carbon source for the synthesis of multi-walled carbon nanotubes via catalytic combustion

Multi-walled carbon nanotubes (MWCNTs) were efficiently synthesized by catalytic combustion of polypropylene (PP) using nickel compounds (such as Ni2O3, NiO, Ni(OH)(2) and NiCO3 (.) 2Ni(OH)(2)) as catalysts in the presence of organic-modified montmorillonite (OMMT) at 630-830 degrees C. Morphologies of the sample undergoing different combustion times were observed to investigate actual process producing MWCNTs by this method. The obtained MWCNTs were characterized by X-ray diffraction (XRD), transmission electron microscope and Raman spectroscopy. The yield of MWCNTs was affected by the composition of PP mixtures with OMMT and nickel compounds and the combustion temperature. The proton acidic sites from the degraded OMMT layers due to the Hoffman reaction of the modifiers at high temperature played an important role in the catalytic degradation of PP to supply carbon sources that are easy to be catalyzed by nickel catalyst for the growth of MWCNTs. The XRD measurements demonstrated that the nickel compounds were in situ reduced into the Ni(0) state with the aid of hydrogen gas and/or hydrocarbons in the degradation products of PP, and the Ni(O) was really the active site for the growth of MWCNTs. The combination of nickel compounds with OMMT was a key factor to efficiently synthesize MWCNTs via catalytic combustion of PP.

Synthesis and characterization of SiO2/Gd2O3 : Eu core-shell luminescent materials

Europium-doped Gd2O3 with an average size of similar to15 nm was coated on the surface of preformed silica nanospheres by the wet chemical method. SEM and TEM photographs showed that SiO2/Gd2O3:Eu core-shell submicrospheres are obtained. XRD patterns indicated that the Gd2O3:Eu shell is crystalline after heat treatment. FTIR and XPS spectra showed that the Gd2O3:Eu shell is linked to the silica surface by forming a Si-O-Gd bond. Photoluminescence studies showed that the luminescent properties are still retained after coating on an inert silica core; additionally, we noted that the emitting peaks are broadened, which results from size effects and interface effects of nanocrystal.

A facile synthetic method for biphenyltetracarhoxylic dianhydrides

We report a facile and high-yielding procedure for preparing biphenyltetracarboxylic dianhydrides (BPDAs). This method relies on a nickel-catalyzed electroreductive coupling reaction of dimethyl 3-chorophthalate (3-DMCP) and/or dimethyl 4-chorophthalate (4-DMCP) with subsequent hydrolysis of tetra-ester and dehydration of tetra-acid.

Syntheses and properties of soluble biphenyl-based polyimides from asymmetric bis(chlorophthalimide)s

A novel synthesis of asymmetric bis(chlorophthalimide)s (3,4-BCPIs) has been established. The polymerizations of them produced higher molecular weight (0.38-0.51 dL/g) polyimides containing biphenyl units than those of isomeric polymers derived from symmetric bis(chlorophthalimide)s (4,4'-BCPIs) and 3,3'-BCPIs. The distribution of the formed biphenyl units of head to tail, head to head, and tail to tail in the chain of the polymers was about 58.0:21.0:21.0, determined by C-13 NMR spectra of the polymers. The composition of model compounds, determined by HPLC, was well consistent with the 13C NMR spectrum result. Comparing with polymers derived from 4,4'-BCPIs and 3,3'-BCPIs, the polymers derived from 3,4-BCPIs showed better solubilities in N,N-dimethylacetamide (DMAc), N,N-dimethyl-formamide (DMF), and N-methylpyrrolinone (NMP). Flexible films could be cast from the polymer solution with the inherent viscosities of above 0.35 dL/g. The polymer derived from asymmetric bis(chlorophthimide)s gave the highest T-g among the isomeric polymers.

Synthesis, structure and norbornene polymerization behavior of neutral palladium complexes

A series of neutral palladium(II) complexes bearing non-symmetric bidentate pyrrole-iminato or salicylaldiminato chelate ligands have been synthesized, and the structure of representative complexes (3a, 4a, and 5a) have been confirmed by X-ray crystallographic analysis. These palladium complexes have been investigated as catalysts for the polymerization of norbornene. Using modified methylaluminoxane (MMAO) as a cocatalyst, these complexes display high activities and produce vinyl-addition polynorborenes. Catalytic activity of up to 8.52 x 10(3) kg/mol(Pd) h has been observed. Wide-angle X-ray diffraction (WAXD) has been used to investigate the polymer microstructure and it has been found that they are non-crystalline.

Copolymerization of dichlorodiphenylsulfone with bis(chlorophthalimide) catalyzed by NiBr2/PPh3/Zn

A new high-performance material, poly(sulfone-imide) was prepared by Ni(0)-catalyzed coupling of aromatic dichlorides containing imide structure and 4,4'-dichlorodiphenylsulfone. The copolymers were produced with high yield and moderate to high inherent viscosities of 0.52-1.13 dL/g. Wide-angle X-ray diffractograms revealed that the polymers were amorphous. Most of the polymers exhibited good solubility and could be readily dissolved in various solvents such as N-methyl-2-pyrrolidinone(NMP) and N,N-dimethylacetamide (DMAc). These polysulfone-imides had glass-transition temperatures between 317 and 345 degreesC and 10% weight loss temperatures in the range of 450476 degreesC in nitrogen atmosphere. The tough polymer films, obtained by casting from cresol solution, had a tensile strength range of 21 158 MPa and a tensile modulus range of 2.1-3.3 GPa.

Synthesis of a novel structural triblock copolymer of poly(gamma-benzyl-L-glutamic acid)-b-poly(ethylene oxide)-b-poly(epsilon-caprolactone)

A novel structural triblock copolymer of poly(gamma-benzyl-L-glutamic acid)-b-poly(ethylene oxide)-b-poly(epsilon-caprolactone) (PBLG-PEO-PCL) was synthesized by a new approach in the following three steps: (1) sequential anionic ring opening polymerization (ROP) of ethylene oxide and epsilon-caprolactone with an acetonitrile/potassium naphthalene initiator system to obtain a diblock copolymer CN-PEO-PCL with a cyano end-group; (2) conversion of the CN end-group into NH2 end-group by hydrogenation to obtain NH2-PEO-PCL; (3) ROP of gamma-benzyl-L-glutamate-N-carboxyanhydrides (Bz-L-GluNCA) with NH2-PEO-PCL as macroinitiator to obtain the target triblock copolymer. The structures from CN-PEO precursor to the triblock copolymers were confirmed by FT-IR and H-1 NMR spectroscopy, and their molecular weights were measured by gel permeation chromatography. The monomer of Bz-L-GluNCA can react almost quantitatively with the amino end-groups of NH2-PEO-PCL macroinitiator by ROP.

Kinetics of extraction and stripping of y(III) by Cyanex 272 as an acidic extractant using a constant interfacial cell with laminar flow

The extraction and stripping kinetics of yttrium(III) with bis(2,4,4-trimethylpentyl) phosphinic acid (Cyanex 272, HA) dissolved in heptane as an acid extractant have been investigated by constant interfacial cell with laminar flow. The experimental hydrodynamic conditions have been chosen so that the contribution of diffusion to the measured rate of reaction is minimized. The plot of interfacial area on the rate has shown a linear relationship, which makes the interface the most probable local for the chemical reactions. At the same time, the extraction thermodynamic and kinetic methods are compared to determine the equilibrium extraction constant. A rate equation and the rate-determining step of the extraction and stripping of yttrium(III) have also been obtained, respectively.

Effects of a surfactant on the electrocatalytic activity of cobalt hexacyanoferrate modified glassy carbon electrode towards the oxidation of dopamine

The cobalt hexacyanoferrate film (CoHCF) was deposited on the surface of a glassy carbon (GC) electrode with a potential cycling procedure in the presence and absence of the cationic surfactant, cetyl trimethylammonium bromide (CTAB), to form CoHCF modified GC (CoHCF/GC) electrode. It was found that CTAB would affect the growth of the CoHCF film, the electrochemical behavior of the CoHCF film and the electrocatalytic activity of the CoHCF/GC electrode towards the electrochemical oxidation of dopamine (DA). The reasons of the electrochemical behavior of CoHCF/GC electrode influenced by CTAB were investigated using FTIR and scanning electron microscope (SEM) techniques. The apparent rate constant of electrocatalytic oxidation of DA catalyzed by CoHCF was determined using the rotating disk electrode measurements.