Design of microstructure of zirconia foams from the emulsion template properties

In this work, we investigate the correlations between structural and rheological properties of emulsified aqueous sol and the porous microstructure of monolithic zirconia foams, manufactured by the integrative combination of the sol-gel and emulsification processes. Macroporous zirconia ceramics prepared using different amounts of decahydronaphthalene, as oil phase, are compared in terms of the emulsion microstructure and ceramic porosity. A combination of electrical conductivity, oil droplet diameter, and rheological measurements was used to highlight the key effect of the dynamic structural properties of the emulsion on the porosity of the ceramic zirconia foam. The minimization of drying shrinkage by appropriate sol-gel mineralization of the oil droplet wall enabled versatile and easy tuning of the ceramic foam microstructure, by fine adjustment of the emulsion characteristics. The foam with the highest porosity (90%) and the lowest bulk density (0.40 g cm-3) was prepared from emulsion with 80 wt% of decahydronaphthalene, which also showed a bicontinuous structure and elevated flow consistency. © The Royal Society of Chemistry 2013.

Effect of controlled conductivity on thermal sensing property of 0-3 pyroelectric composite

Composite films made of lead zirconate titanate ceramic particles coated with polyaniline and poly(vinylidene fluoride) - PZT-PAni/PVDF were produced by hot pressing the powder mixtures in the desired ceramic volume fraction. The ceramic particles were coated during the polyaniline synthesis and the conductivity of the conductor polymer was controlled by different degrees of protonation. Composites were characterized by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), ac and dc electrical measurements, the longitudinal d33 piezo coefficient and the photopyroelectric response. Results showed that the presence of PAni increased the dielectric permittivity of the composite and allowed better efficiency in the poling process, which increased the piezo- and pyroelectric activities of the composite film and reduced both the poling time and the poling electric field. The thermal sensing of the material was also analyzed, showing that this composite can be used as pyroelectric sensor. © 2013 IOP Publishing Ltd.

Effect of ceramic shade on the degree of conversion of a dual-cure resin cement analyzed by FTIR

Objectives: The aim of this research was to evaluate the degree of monomer conversion of different resin cement shades when photocured under different feldspathic ceramic shades. The photocuring time was also evaluated as well as the translucency of each ceramic shade. Methods: Three VITA VM7 ceramic shades (Base Dentin 0M1, Base Dentin 2M2 and Base Dentin 5M3) were used to determine the translucency percentage. A spectrophotometer MiniScan was used to measure the opacity percentage of each specimen (2-mm-thick) and then the translucency was calculated. To measure the degree of conversion (DC), the resin cement (Variolink II; A3 Yellow and transparent) specimens (thickness: 100 μm) were photocured under a ceramic block (2-mm-thick) for 20 or 40 s. Specimens photocured without the ceramic block were used as control. Sixteen groups (n = 3) were evaluated. Micro-ATR/FTIR spectrometry was used to evaluate the extent of polymerization of all specimens after 24 h. The %DC was calculated of experimentally polymerized versus maximally polymerized composite. Results: The translucency percentages of 0M1, 2M2 and 5M3 ceramics were 12.41 (1.02)%, 5.75 (1.91)% and 1.07 (0.03)%, respectively. The %DC of both resin cement shades cured under ceramic 5M3 was significantly lower than the other groups (p < 0.05). The %DC of 0M1 groups exhibited no significant difference from 2M2 groups (p > 0.05), with the exception of the transparent cement photocured for 40 s. Conclusion: Photocuring under 2 mm ceramic showed that the increase in chroma saturation significantly decreased Variolink II resin cement %DC (100-μm-thick). © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of convergence angle of tooth preparation on the fracture resistance of Y-TZP-based all-ceramic restorations

Objective: To investigate the influence of the convergence angle of tooth preparation on the fracture load of Y-TZP-based ceramic (YZ-Vita YZ) substructure (SB) veneered with a feldspathic porcelain (VM9-Vita VM9). Methods: Finite element stress analysis (FEA) was performed to examine the stress distribution of the system. Eighty YZ SB were fabricated using a CAD-CAM system and divided into four groups (n = 20), according to the total occlusal convergence (TOC) angle: G6-6° TOC; G12-12° TOC; G20-20° TOC; and G20MOD-20° TOC with modified SB. All SB were veneered with VM9, cemented in a fiber reinforced epoxy resin die, and loaded to failure. Half of the specimens from each group (n = 10) were cyclic fatigued (106 cycles) before testing. Failure analysis was performed to determine the fracture origin. Data were statistically analyzed using Anova and Tukey's tests (α = 0.05). Results: The greatest mean load to fracture value was found for the G20MOD, which was predicted by the FEA. Cyclic fatigue did not significantly affect the load of fracture. Catastrophic failure originating from the internal occlusal surface of the SB was the predominant failure mode, except for G20MOD. Significance: The YZ-VM9 restorations resisted greater compression load than the usual physiological occlusal load, regardless of the TOC angle of preparations. Yet, the G20MOD design produced the best performance among the experimental conditions evaluated. © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effects of cement-curing mode and light-curing unit on the bond durability of ceramic cemented to dentin

The aim of this study was to evaluate the effects of different light-curing units and resin cement curing types on the bond durability of a feldspathic ceramic bonded to dentin. The crowns of 40 human molars were sectioned, exposing the dentin. Forty ceramic blocks of VITA VM7 were produced according to the manufacturer's recommendations. The ceramic surface was etched with 10% hydrofluoric acid/60s and silanized. The dentin was treated with37% phosphoric acid/15s, and the adhesive was applied. The ceramic blocks were divided and cemented to dentin according to resin cement/RC curing type(dual-and photocured), light-curing unit (halogen light/QTH and LED), and storage conditions (dry and storage/150 days + 12,000 cycles/thermocycling). All blocks were stored in distilled water (37°C/24h) and sectioned (n = 10): G1-QTH + RC Photo, G2-QTH + RC Dual, G3-LED + RC Photo, G4-LED + RC Dual. Groups G5, G6, G7, and G8 were obtained exactly as G1 through G4, respectively, and then stored and thermocycled. Microtensile bond strength tests were performed (EMIC), and data were statistically analyzed by ANOVA and Tukey's test (5%). The bond strength values (MPa) were: G1-12.95 (6.40)ab; G2-12.02 (4.59)ab; G3-13.09 (5.62)ab; G4-15.96 (6.32)a; G5-6.22 (5.90)c; G6-9.48 (5.99)bc; G7-12.78 (11.30)ab; and G8-8.34 (5.98)bc. The same superscript letters indicate no significant differences. Different light-curing units affected the bond strength betweenceramic cemented to dentin when the photocured cement was used, and only after aging (LED>QTH). There was no difference between the effects of dual-and photo-cured resin-luting agents on the microtensile bond strength of the cement used in this study.

Mechanochemical synthesis of yttrium manganite

Yttrium manganite (YMnO3) is a multiferroic material, which means that it exhibits both ferromagnetic and ferroelectric properties, so making it interesting for a variety of technological applications. In this work, single-phase YMnO3 was prepared for the first time by mechanochemical synthesis in a planetary ball mill. The YMnO3 was formed directly from the highly activated constituent oxides, Y 2O3 and Mn2O3, after 60 min of milling time. During prolonged milling, the growth of the particles occurred. The cumulative energy introduced into the system during milling for 60 min was 86 kJ/g. The X-ray powder-diffraction analysis indicates that the as-prepared samples crystallize with an orthorhombic (Pnma) YMnO3 structure. The morphology and chemical composition of the powder were investigated by SEM and FESEM. The magnetic properties of the obtained YMnO3 powders were found to change as a function of the milling time in a manner consistent with the variation in the nanocomposite microstructure. © 2012 Elsevier B.V. All rights reserved.

Glass foam of macroporosity using glass waste and sodium hydroxide as the foaming agent

Glass foams using float glass waste and sodium hydroxide were produced. The influence of the sodium hydroxide amount in the foam formulation was studied. Titanium dioxide was used as a strengthening agent. The variations of temperature, heating rate and sintering time were investigated during the synthesis process. Open porosity was estimated using mercury porosimetry. The morphology of the glass foams was evaluated using scanning electron microscopy, phase formation was studied using X-ray diffraction, and chemical composition was estimated using X-ray fluorescence. As a result, glass foams with macroporosity were obtained. Since the glass foams used glass waste as reactant, the results suggest the development of an alternative route for glass recycling. © 2012 Elsevier Ltd and Techna Group S.r.l.

Enhanced stability in CO2 of Ta doped BaCe0.9Y 0.1O3-δ electrolyte for intermediate temperature SOFCs

The influence of Ta concentration on the stability of BaCe 0.9-xTaxY0.1O3-δ (where x=0.01, 0.03 and 0.05) powders and sintered samples in CO2, their microstructure and electrical properties were investigated. The ceramic powders were synthesized by the method of solid state reaction, uniaxially pressed and sintered at 1550 °C to form dense electrolyte pellets. A significant stability in CO2 indicated by the X-ray analysis performed was observed for the samples with x≥0.03. The electrical conductivities determined by impedance measurements in the temperature range of 550-750 °C and in various atmospheres (dry argon, wet argon and wet hydrogen) increased with temperature but decreased with Ta concentration. The highest conductivities were observed in the wet hydrogen atmosphere, followed by those in wet argon, while the lowest were obtained in the dry argon atmosphere for each dopant concentration. The composition with Ta content of 3 mol% showed satisfactory characteristics: good resistance to CO2 in extreme testing conditions, while a somewhat reduced electrical conductivity is still comparable with that of BaCe0.9Y0.1O3-δ. © 2012 Elsevier Ltd and Techna Group S.r.l.

Clinical Satisfaction and Quality of Ceramic Fixed Dentures

It is known that several factors can affect the clinical success and durability of fixed partial dentures. Therefore, the aim of the present study was to present a literature review about the longevity, clinical success, and quality, as well as, patients' and dental surgeons' satisfaction of ceramic fixed dentures. High rate of patients' satisfaction has been observed in relation to the esthetic of ceramic crowns. In addition, the literature has shown that dental ceramics can be used in several clinical situations with high success rate and longevity. Despite of failures and complications of ceramic restorations, nowadays, with the improvement of mechanical properties of such materials, ceramic crowns present a favorable prognosis and can be used in several clinical situations with high success rate, clinical quality, and great patients' satisfaction. © 2013 The American Ceramic Society.

Intense photoluminescence emission at room temperature in calcium copper titanate powders

A study was undertaken about the structural and photoluminescent properties at room temperature of CaCu3Ti4O12 (CCTO) powders synthesized by a soft chemical method and heat treated between 300 and 800 °C. The decomposition of precursor powder was followed by thermogravimetric analysis (TG-DTA), X-ray diffraction (XRD), Fourier transform infrared (FT-IR), Fourier transform Raman (FT-Raman) and photoluminescence (PL) measurements. XRD analyses revealed that the powders annealed at 800 °C are becoming ordered and crystallize in the cubic structure. The most intense PL emission was obtained for the sample calcined at 700 °C, which is not highly disordered (300-500 °C) and neither completely ordered (800 °C). From the spectrum it is clearly visible that the lowest wavelength peak is placed around 480 nm and the highest wavelength peak at about 590 nm. The UV/vis absorption spectroscopy measurements showed the presence of intermediate energy levels in the band gap of structurally disordered powders. © 2012 Elsevier Ltd and Techna Group S.r.l.