Concentration dependence of the Er3+ visible and infrared luminescence in Y2-x Erx O3 thin films on Si

Y2-x Erx O3 thin films, with x varying between 0 and 0.72, have been successfully grown on crystalline silicon (c-Si) substrates by radio-frequency magnetron cosputtering of Y2 O 3 and Er2 O3 targets. As-deposited films are polycrystalline, showing the body-centered cubic structure of Y2 O3, and show only a slight lattice parameter contraction when x is increased, owing to the insertion of Er ions. All the films exhibit intense Er-related optical emission at room temperature both in the visible and infrared regions. By studying the optical properties for different excitation conditions and for different Er contents, all the mechanisms (i.e., cross relaxations, up-conversions, and energy transfers to impurities) responsible for the photoluminescence (PL) emission have been identified, and the existence of two different well-defined Er concentration regimes has been demonstrated. In the low concentration regime (x up to 0.05, Er-doped regime), the visible PL emission reaches its highest intensity, owing to the influence of up-conversions, thus giving the possibility of using Y2-x Er x O3 films as an up-converting layer in the rear of silicon solar cells. However, most of the excited Er ions populate the first two excited levels 4I11/2 and 4I13/2, and above a certain excitation flux a population inversion condition between the former and the latter is achieved, opening the route for the realization of amplifiers at 2.75 μm. Instead, in the high concentration regime (Er-compound regime), an increase in the nonradiative decay rates is observed, owing to the occurrence of cross relaxations or energy transfers to impurities. As a consequence, the PL emission at 1.54 μm becomes the most intense, thus determining possible applications for Y2-x Erx O 3 as an infrared emitting material. © 2009 American Institute of Physics.

The influence of substrate on the properties of Er2O3 films grown by magnetron sputtering

The structural properties and the room temperature luminescence of Er2O3 thin films deposited by RF magnetron sputtering have been studied. Films characterized by good morphological properties have been obtained by using a SiO2 interlayer between the film and the Si substrate. The evolution of the properties of the Er2O3 films due to rapid thermal annealing processes in O2 ambient performed at temperatures in the range 800-1200 °C has been investigated in details. The existence of well-defined annealing conditions (temperature of 1100 °C or higher) allowing to avoid the occurrence of extensive chemical reactions with the oxidized substrate has been demonstrated and an increase of the photoluminescence (PL) intensity by about a factor of 40 with respect to the as deposited material has been observed. The enhanced efficiency of the photon emission process has been correlated with the longer lifetime of the PL signal. The same annealing processes are less effective when Er2O3 is deposited on Si. In this latter case interfacial reactions and pit formation occur, leading to a material characterized by stronger non-radiative phenomena that limit the PL efficiency. © 2006 Elsevier B.V. All rights reserved.