Luminescent CdSe and CdSe/CdS core-shell nanocrystals synthesized via a combination of solvothermal and two-phase thermal routes

A new solvothermal route has been developed for synthesizing the size-controlled CdSe nanocrystals with relatively narrow size distribution, and the photoluminescence (PL) quantum yields (QYs) of the nanocrystals can reach 5-10%. Then the obtained CdSe nanocrystals served as cores to prepare the core/shell CdSe/CdS nanocrystals via a two-phase thermal approach, which exhibited much higher PL QYs (up to 18-40%) than the CdSe core nanocrystals. The nanocrystal samples were characterized by ultraviolet-visible (UV-vis) absorption spectra, PL spectra, wide-angle Xray diffraction (WAXD), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM).

Up-conversion spectrum properties of the oxy-fluoride glass co-doped with Er3+ and Yb3+

Up-conversion of 45PbF(2)-45GeO(2)-10WO(3) oxy-fluoride glasses co-doped with Yb3+ and Er3+ ions were prepared by fusion method through melting at 1223 K and then annealing at 653 K for 4 h. Transmittance of the undoped host glass was beyond 73% in a range of 0.6-2.5 mu m and the co-doped glasses still provided good transmittance beyond 50%. Refractive indices of the host and co-doped glasses were 1.517 and 1.650, respectively. Blue, green and red fluorescence spectra were observed in a range of 400-700 nm under 980 nm diode laser excitation. Up-conversion spectra at about 410, 518, 530and 650 nm were assigned to the 4f electron transitions of H-2(9/2) -> I-4(15)/(2), H-2(15/2) -> I-4(15/2) S-4(3/2) -> I-4(15/2) and F-4(9/2) -> I-4(15/2) of Er3+ ion, respectively. The mechanism of energy transfer between Yb3+ and Er3+ ions in the glass was analyzed. Raman shift shows the non-radiative relaxation of the glass sample is low.

Highly efficient red electroluminescence induced by efficient electron injection and exciton confinement

HigWy efficient DCJTB-doped device was realized by enhanced electron injection and exciton confinement. A fluorine end-capped linear phenylene/oxadiazole oligomer 2,5-bis(4-fluorobiphenyl-4'-yl)-1,3,4-oxadiazole (1) and a trifluoromethyl end-capped oligomer 2,5-bis(4-trifluoromethylbiphenyl-4'-yl)-1,3,4-oxadiazole (2) were designed and incorporated as an electron transporting/hole blocking material in the device structure ITO/NPB (60 mn)/DCJTB:Alq(3) (0.5%, 10 nm)/1 or 2 (20 nm)/Alq(3) (30 mn)/LiF (1 nm)/Al (100 nm). The devices showed highly efficient red luminescence. In particular, the device based on 1 achieved pure red luminescence at 620 run originating from DCJTB, with a narrow FWHI of 65 nm, maximal brightness of 13,300 cd/m(2) at voltage of 20.8 V and current density of ca. 355 mA/cm(2). High current and power efficiencies (> 3.6 cd/A. 1.01m/W) were retained within a wide range of current densities. Our results show efficient and stable DCJTB-doped red electroluminescence could be anticipated for practical applications by taking advantage of the present approaches. The control experiments using BCP were also studied.

Synthesis, crystal structure, spectroscopy and electroluminescence of zinc(II) complexes containing bidentate 2-(2-pyridyl)quinoline derivative ligands

Three bidentate ligands, 4-phenyl-2-(2-pyridyl)-quinoline (ppq), 6-(carbazol-9-yl)-4-phenyl-2-(2-pyridyl)-quinoline (cpq) and 6-diphenylamino-4-phenyl-2-(2-pyridyl)-quinoline (dpq) and their zinc(II) complexes, have been designed and synthesized. The crystal structure of [Zn(ppq)(2)Cl]PF6 shows that the central zinc atom is coordinated with one chloride and four nitrogen atoms from two ligands. The introduction of an electron-donating substituent such as carbazole or an aromatic amine group at the 6-position of the quinoline moiety can generate colored tunable Zn complexes, and the photoluminescence (PL) wavelength was modulated from 418 nm for [Zn(ppq)(2)Cl]PF6 to 591 nm for [Zn(cpq)(2)Cl]PF6 and 638 nm for [Zn(dpq)(2)Cl]PF6 in CH2Cl2 solution. The electroluminescence spectrum of [Zn(dpq)(2)Cl]PF6 exhibits pure red light emission with the Commission Internationale de L'Eclairage (CIE) coordinates (0.63, 0.36) and a maximum at 648 nm.

Sol-gel fabrication, patterning and photoluminescent properties of LaPO4 : Ce3+, Tb3+ nanocrystalline thin films

Ce3+ and/or Tb3+-doped LaPO4 nanocrystalline thin films and their patterning were fabricated by a sol-gel process combined with soft lithography on silicon and quartz glass substrates. The results of XRD indicated that the films began to crystallize at 700 degreesC. The 1000 degreesC annealed single layer films are transparent by eyes, uniform and crack-free with a thickness of about 200 nm and an average grain size of 100 nm. Patterned thin film with different band widths (5-50 mum) were obtained by micro-molding in capillaries technique. The luminescence and energy transfer properties of Ce3+ and Tb3+ were studied in LaPO4 films.

Luminescence properties of RP1-xVxO4: A (R=Y, Gd, La; A=Sm3+Er3+ x=0, 0.5, 1) thin films prepared by pechini sol-gel process

Thin film phosphors with compositions of RP1-xVxO4: A (R = Y, Gd, La; A = Sm3+, Et3+; x = 0, 0.5, 1) have been prepared by a Pechini sol-gel process. X-Ray diffraction, atomic force microscopy (AFM), photoluminescence excitation and emission spectra were utilized to characterize the thin film phosphors. The results of XRD showed that a solid solution formed in YVxP1-xO4: A film series from x = 0 to x = 1 with zircon structure, which also held for GdVO4: A film. However, LaVO4: A film crystallized with a different structure, monazite. AFM study revealed that the phosphor films consisted of homogeneous particles ranging from 90 to 400 nm depending on the compositions. Upon short ultraviolet excitation, the films exhibit the characteristic Sm(3+ 4)G(5/2)-H-6(J) (J=5/2, 7/2, 9/2) emission in the red region and Er3+ H-2(11/2), S-4(3/2)-I-4(15/2) emission in the green region, respectively With the increase of x values in YVxP1-xO4: SM3+ (Er3+) films, the emission intensity Of SM3+ (Er3+) increases due to the increase of energy transfer probability from VO43- to Sm3+ (Er3+). Due to the structural effects, the Sm3+ (Er3+) shows similar spectral properties in YVO4 and GdVO4 films, which are much different from those in LaVO4 film.

Lanthanide complex/polymer composite optical resin with intense narrow band emission, high transparency and good mechanical performance

Novel composite resins possessing good luminescent properties have been synthesized through a free radical copolymerization of styrene, alpha-methylacrylic acid and the binary or ternary complexes of lanthanide ions (Eu3+ and Tb3+). These polymer-based composite resins not only possess good transparency and mechanical performance but also exhibit an intense narrow band emission of lanthanide complexes under UV excitation. We characterized the molecular structure, physical and mechanical performance, and luminescent properties of the composite resins. Spectra investigations indicate that alpha-methyl-acrylic acid act as both solubilizer and ligand. Photoluminescence measurements indicate that the lanthanide complexes show superior emission lines and higher intensities in the resin matrix than in the corresponding pure complex powders, which can be attributed to the restriction of molecular motion of complexes by the polymer chain networks and the exclusion of water molecules from the complex. We also found that the luminescence intensity decreased with increasing content of alpha-methylacrylic acid in the copolymer system. The lifetime of the lanthanide complexes also lengthened when they were incorporated in the polymer matrix. In addition, we found that the relationships between emission intensity and Tb (Eu) content exhibit some extent of concentration quenching.

Preparation and characterization of luminescent cubic MCM-48 impregnated with an Eu3+ beta-diketonate complex

We report on the preparation of luminescent silica mesoporous molecular sieves (MCM-48) activated by the europium complex Eu(DBM)(3) . 2H(2)O (where DBM = dibenzoylmethane), using a simple wet impregnation method. Different concentrations of Eu(DBM)(3) . 2H(2)O were introduced into the MCM-48 cubic structure, and the resulting samples were washed with ethanol for different times. UV-Vis absorption measurements and thermogravimetric analysis were used to estimate the amount of Eu complex that has been incorporated within the pores of the MCM-48 host. The various samples were characterized by X-ray powder diffraction (XRD), infrared spectroscopy, diffuse reflectance (DR) and fluorescence measurements. The results reveal that Eu complexes have been successfully introduced into the pores of MCM-48 without disrupting the structure. All the impregnated MCM-48 materials show the typical red luminescence of Eu3+ when excited with a UV lamp. Shifts of the absorption maxima were observed in the DR and fluorescence excitation spectra and will be discussed in relation with guest-host interactions between the organic complex and the silica matrix. The decay profiles of the europium luminescence in the different samples were also measured and discussed.

Luminescence of the compounds Y0.5-xLi1.5VO4 :(Dy3+,Eu3+)

In this paper for the first time the compounds Y0.5-xLi1.5VO4:(Dy3+, Eu3+),(YLV:Dy,Eu) (0.01and 400 degreesC lower than that to synthesize rare earth vanadates. Their structures were analyzed by X-ray powder diffraction experiment. The excitation and emission spectra were measured at room temperature. The blue, the yellow and the red emission from the F-4(9/2)-H-6(15/2) (474.2-484.2 nm) transitions and F-4(9/2)-H-6(13/2) (568-576.4 nm) transitions of Dy3+ and the D-5(0)-F-7(2) (608-619.2 nm) transitions of Eu3+, respectively, are very strong in multiwavelength.

The relationship between chemical bond properties and Stokes shift of Eu2+ in some silicate host lattices

The covalency of each bond in divalent europium doped hosts CaSiO3, SrSiO3, BaSiO3, Sr2LiSiO4F, Ba5SiO4Cl6 and Ba5SiO4Br6 were calculated by using the complicate crystal chemical bond theory. The relationship between the Stokes shift and the bond properties of Eu2+ in these crystals was discussed. The result demonstrates that, in the isostructural crystals that being doped with Eu2+, there is a more precise connection between the magnitude of Stokes shift and the mean covalency of the dopant site.

Synthesis, structure and luminescent properties of a new praseodymium(III) complex with beta-diketone

A new tetrakis praseodymium(tu) complex Pr(TFNB)(3)Phen has been synthesized, in which TFNB is 4,4,4-trifluoro-1-(2-naphthyl)-1,3-butanedione and Phen is 1,10-phenanthroline. Its crystal structure and luminescent spectra were successfully determined and investigated. The typical antenna effect existing in the luminescence of Pr(TFNB)(3)Phen was revealed by the study of the UV-Vis absorption spectra of ligands and the excitation spectrum of Pr(TFNB)(3)Phen.

Luminescence properties of LB films based on heteropolytungstate of rare earth

In this work, the LB films based on heteropolytungstate of Dy and Sm have been prepared. The X-ray diffraction shows the LB films have a highly ordered lamella structure. The luminescence characteristics of the LB films were studied. The charge transfer bands of LB films are in higher energies than those of the corresponding solids. It is noticed that the yellow to blue intensity ratio (Y:B) of Dy3+ in the LB films is different from that of the solid. The differences in the spectra show that the Dy3+ site symmetry in LB film was changed due to the interaction between the surfactant and the polyanions. The differences could also be found in the luminescence spectra of the LB films of Sm complex.

Preparation and characterization of a layered transparent luminescent thin film of silica-CTAB-Tb(acac)(3) composite with mesostructure

A layered luminescent mesostructured thin film of silica-CTAB-Tb(acac)(3) composite has been synthesized by a dip-coating process through an in situ sol-gel method. The terbium (Tb3+) ion and beta-diketone organic ligand acetylacetone (acac) were introduced into the precursor solution, respectively. The as-synthesized composite film was transparent, colorless and possessed a layered structure. After the composite film was dried at 50 degreesC for a few minutes Tb(acac)(3) complex was synthesized in the mesostructured thin film, which can be indicated by the luminescence of the composite film under the UV lamp. The properties of the samples were characterized by XRD, absorption, Fourier transform infrared spectroscopy, and luminescent spectra.

Local structure and valences of samariurn in SrB4O7 : Sm and SrB6O10 : Sm prepared in-air

The coordination numbers for the samarium atoms and the Sm-O bond distances in SrB4O7:Sm and SrB6O10:Sm prepared in air were determined by means of Sm-L-3 edge EXAFS. The coordination. was found to be nine-folded for both these hosts and the bond distance was 2.40-2.42 Angstrom in SrB4O7:Sm and 2.42-2.44 Angstrom in SrB6O10:Sm. For SrB4O7:Sm the coordination number is coincident with that of the strontium. atoms suggesting the substitution of the samarium atoms at the strontium sites. The coordination number of the strontium atoms in SrB6O10 was also suggested to be nine assuming the same type of substitution. The valences of samarium were determined from the luminescent spectra. Both divalent and trivalent ions were present in both SrB4O7:Sm and SrB6O10:Sm, while the fraction of Sm2+ was higher in the former than in the latter. This difference has been assigned to the difference in rigidity between the B-O networks in these structures.

Synthesis-dependent luminescence properties of Y3Al5O12 : Re3+ (Re=Ce, Sm, Tb) phosphors

By using metal nitrates and oxides as the starting materials, Y2Al5O12 (YAG) and YAG:Re3+ (Re = Ce, Sm, Th) powder phosphors were prepared by solid-state (SS), coprecipitation (CP) and citrate gel (CG) methods. The resulting YAG and YAG-based phosphors were characterized by XRD, FT-IR, SEM and photoluminescent excitation and emission spectra. The purified crystalline phases of YAG were obtained at 800 degreesC (CG) and 900 degreesC (CP, SS). At an identical annealing temperature and doping concentration, the doped rare-earth ions showed the stronger emission intensity in the CP- and SS-derived phosphors than the CG-derived YAG phosphors. The poor emission intensity for the CG-derived phosphors is mainly caused by the contamination of carbon impurities from citric acid in the starting materials.