Microsphere Bouquets of Bismuth Telluride Nanoplates: Room-Temperature Synthesis and Thermoelectric Properties

We report the synthesis and properties of sphere-shaped microscale aggregates of bismuth telluride nanoplates. We obtain porous microspheres by reducing bismuth chloride and orthotelluric acid with hydrazine in the presence of thioglycolic acid-which serves as the shape-and size-directing agent-followed by room-temperature aging-which promotes nanoplate aggregation. Thin film assemblies of the nanoplate microspheres exhibit n-type behavior due to sulfur doping and a Seebeck coefficient higher than that reported for assemblies of chalcogenide nanostructures. Adaptation of our scalable approach to synthesize and hierarchically assemble nanostructures with controlled doping could be attractive for tailoring novel thermoelectric materials for applications in high-efficiency refrigeration and harvesting electricity from heat.

3D hierarchical rutile TiO2 and metal-free organic sensitizer producing dye-sensitized solar cells 8.6% conversion efficiency

Three-dimensional (3D) hierarchical nanoscale architectures comprised of building blocks, with specifically engineered morphologies, are expected to play important roles in the fabrication of 'next generation' microelectronic and optoelectronic devices due to their high surface-to-volume ratio as well as opto-electronic properties. Herein, a series of well-defined 3D hierarchical rutile TiO2 architectures (HRT) were successfully prepared using a facile hydrothermal method without any surfactant or template, simply by changing the concentration of hydrochloric acid used in the synthesis. The production of these materials provides, to the best of our knowledge, the first identified example of a ledgewise growth mechanism in a rutile TiO2 structure. Also for the first time, a Dye-sensitized Solar Cell (DSC) combining a HRT is reported in conjunction with a high-extinction-coefficient metal-free organic sensitizer (D149), achieving a conversion efficiency of 5.5%, which is superior to ones employing P25 (4.5%), comparable to state-of-the-art commercial transparent titania anatase paste (5.8%). Further to this, an overall conversion efficiency 8.6% was achieved when HRT was used as the light scattering layer, a considerable improvement over the commercial transparent/reflector titania anatase paste (7.6%), a significantly smaller gap in performance than has been seen previously.