Synthesis and Characterization of Double Metal Hexacyanoferrates

Manganese Hexacyanoferrate (MnHCF) and nickel doped manganese hexacyanoferrate were synthesized by simple co-precipitation method. The water content and chemical formula was obtained by TGA and MP-AES measurements, functional groups by FT-IR analysis, the crystal structure by PXRD and a local geometry by XAS. Elemental species of cycled samples were further investigated by TXM and 2D XRF. Electrochemical tests were performed in the glass cell. With addition of nickel, vacancies and water content increased in the sample. Crystal structure changed from monoclinic to cubic. Ni disturbed the local structure of Mn, site, however, almost no change was observed in Fe site. After charge/discharge cycling of MnHCF intercalation was already found in the peripheries of charged species after 20 cycle in 2D XRF analysis and randomly distributed intercalated regions after 50 cycles in TXM analysis. Cyclic voltammetry showed that peak-to-peak separation is increasing in case of the addition of Ni to MnHCF.

Synthesis and characterization of defective PBAs electrode material

Sodium manganese hexacyanoferrate (NaMnHCF) and its derivatives have been synthesized by simple co-precipitation method with addition of the citric and ascorbic acids respectively. The correspondent crystal structure, water content, chemical formula and a deep structural investigation of prepared samples have been performed by means of the combination of the laboratory and synchrotron techniques (PXRD, FT-IR, TGA, MP-AES and XAS). Electrochemical tests have been done using three-electrode system in sodium nitrate solution at different concentration. From cyclic voltammetry curves, Fe3+/2+ redox peak has been observed, whereas Mn3+/2+ peak was not always evident. Structural stability of the cycled samples has then been tested using 2D XRF imaging and Transmission X-ray microscopy (TXM) techniques. The intercalation of NaMnHCF after 20 cycles has been found by micro-XANES analysis of the highlighted spots which have been found in the XRF images. TXM has also confirmed the appearance of the intercalated particles after 50 cycles comparing the spectra between charged and discharged materials at three different edges (Mn, Fe and N). However, by comparison with lithium samples, it seems obvious that sodium samples are more homogeneous and intercalation is at the very beginning indicating the relative structural stability of sodium manganese hexacyanoferrate electrode material.

Synthesis, Characterization, and Applications of a Novel Cu(II)-MOF Based on a Propargylcarbamate-Functionalized Isophthalate Ligand

This work describes the synthesis of a propargylcarbamate-functionalized isophthalate ligand and its use in the solvothermal preparation of a new copper(II)-based metal organic framework named [Cu(1,3-YBDC)]ˑxH2O (also abbreviated as Cu-MOF. The characterization of this compound was performed using several complementary techniques such as infrared (ATR-FTIR) and Raman spectroscopy, X-ray powder diffraction spectroscopy (PXRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), atomic absorption spectroscopy (AAS) as well as thermal and surface area measurements. Synchrotron X-ray diffraction analysis revealed that this MOF contains a complex network of 5-substituted isophthalate anions bound to Cu(II) centers, arranged in pairs within paddlewheel (or “Chinese lantern”) structure with a short Cu…Cu distance of 2.633 Å. Quite unexpectedly, the apical atom in the paddlewheel structure belongs to the carbamate carbonyl oxygen atom. Such extra coordination by the propargylcarbamate groups drastically reduces the MOF porosity, a feature that was also confirmed by BET measurements. Indeed, its surface area was determined to be low (14.5 ± 0.8 m2/g) as its total pore volume (46 mm3/g). Successively the Cu-MOF was treated with HAuCl4 with the aim of studying the ability of the propargylcarbamate functionality to capture the Au(III) ion and reduce it to Au(0) to give gold nanoparticles (AuNPs). The overall amount of gold retained by the Cu-MOF/Au was determined by AAS while the amount of gold and its oxidation state on the surface of the MOF was studied by XPS. A glassy carbon (GC) electrode was drop-casted with a Cu-MOF suspension to electrochemically characterize the material through cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The performance of the modified electrodes towards nitrite oxidation was tested by CV and chronoamperometry.

Development and Detailed Characterization of Innovative, High-Performance Membrane Materials for CO2 Capture Processes

The scope of this dissertation is to study the transport phenomena of small molecules in polymers and membranes for gas separation applications, with particular attention to energy efficiency and environmental sustainability. This work seeks to contribute to the development of new competitive selective materials through the characterization of novel organic polymers such as CANALs and ROMPs, as well as through the combination of selective materials obtaining mixed matrix membranes (MMMs), to make membrane technologies competitive with the traditional ones. Kinetic and thermodynamic aspects of the transport properties were investigated in ideal and non-ideal scenarios, such as mixed-gas experiments. The information we gathered contributed to the development of the fundamental understanding related to phenomenon like CO2-induced plasticization and physical aging. Among the most significant results, ZIF-8/PPO MMMs provided materials whose permeability and selectivity were higher than those of the pure materials for He/CO2 separation. The CANALs featured norbornyl benzocyclobutene backbone and thereby introduced a third typology of ladder polymers in the gas separation field, expanding the structural diversity of microporous materials. CANALs have a completely hydrocarbon-based and non-polar rigid backbone, which makes them an ideal model system to investigate structure-property correlations. ROMPs were synthesized by means of the ring opening metathesis living polymerization, which allowed the formation of bottlebrush polymers. CF3-ROMP reveled to be ultrapermeable to CO2, with unprecedented plasticization resistance properties. Mixed-gas experiments in glassy polymer showed that solubility-selectivity controls the separation efficiency of materials in multicomponent conditions. Finally, it was determined that plasticization pressure in not an intrinsic property of a material and does not represent a state of the system, but rather comes from the contribution of solubility coefficient and diffusivity coefficient in the framework of the solution-diffusion model.

Comprehensive characterization of snowfall in terms of microphysical features, quantitative precipitation estimation and scavenging properties by in situ and remote sensing observations at an Antarctic coastal site

Snow plays a crucial role in the Earth's hydrological cycle and energy budget, making its monitoring necessary. In this context, ground-based radars and in situ instruments are essential thanks to their spatial coverage, resolution, and temporal sampling. Deep understanding and reliable measurements of snow properties are crucial over Antarctica to assess potential future changes of the surface mass balance (SMB) and define the contribution of the Antarctic ice sheet on sea-level rise. However, despite its key role, Antarctic precipitation is poorly investigated due to the continent's inaccessibility and extreme environment. In this framework, this Thesis aims to contribute to filling this gap by in-depth characterization of Antarctic precipitation at the Mario Zucchelli station from different points of view: microphysical features, quantitative precipitation estimation (QPE), vertical structure of precipitation, and scavenging properties. For this purpose, a K-band vertically pointing radar collocated with a laser disdrometer and an optical particle counter (OPC) were used. The radar probed the lowest atmospheric layers with high vertical resolution, allowing the first trusted measurement at only 105 m height. Disdrometer and OPC provided information on the particle size distribution and aerosol concentrations. An innovative snow classification methodology was designed by comparing the radar reflectivity (Ze) and disdrometer-derived reflectivity by means of DDA simulations. Results of classification were exploited in QPE through appropriate Ze-snow rate relationships. The accuracy of the resulting QPE was benchmarked against a collocated weighing gauge. Vertical radar profiles were also investigated to highlight hydrometeors' sublimation and growth processes. Finally, OPC and disdrometer data allowed providing the first-ever estimates of scavenging properties of Antarctic snowfall. Results presented in this Thesis give rise to advances in knowledge of the characteristics of snowfall in Antarctica, contributing to a better assessment of the SMB of the Antarctic ice sheet, the major player in the global sea-level rise.

Non-ambient solid-state characterization of crystalline molecular organic semiconductors

The research project is focused on the investigation of the polymorphism of crystalline molecular material for organic semiconductor applications under non-ambient conditions, and the solid-state characterization and crystal structure determination of the different polymorphic forms. In particular, this research project has tackled the investigation and characterization of the polymorphism of perylene diimides (PDIs) derivatives at high temperatures and pressures, in particular N,N’-dialkyl-3,4,9,10-perylendiimide (PDI-Cn, with n = 5, 6, 7, 8). These molecules are characterized by excellent chemical, thermal, and photostability, high electron affinity, strong absorption in the visible region, low LUMO energies, good air stability, and good charge transport properties, which can be tuned via functionalization; these features make them promising n-type organic semiconductor materials for several applications such as OFETs, OPV cells, laser dye, sensors, bioimaging, etc. The thermal characterization of PDI-Cn was carried out by a combination of differential scanning calorimetry, variable temperature X-ray diffraction, hot-stage microscopy, and in the case of PDI-C5 also variable temperature Raman spectroscopy. Whereas crystal structure determination was carried out by both Single Crystal and Powder X-ray diffraction. Moreover, high-pressure polymorphism via pressure-dependent UV-Vis absorption spectroscopy and high-pressure Single Crystal X-ray diffraction was carried out in this project. A data-driven approach based on a combination of self-organizing maps (SOM) and principal component analysis (PCA) is also reported was used to classify different π-stacking arrangements of PDI derivatives into families of similar crystal packing. Besides the main project, in the framework of structure-property analysis under non-ambient conditions, the structural investigation of the water loss in Pt- and Pd- based vapochromic potassium/lithium salts upon temperature, and the investigation of structure-mechanical property relationships in polymorphs of a thienopyrrolyldione endcapped oligothiophene (C4-NT3N) are reported.

Characterization of first sorption cycle of white Portland cement by 1H NMR

The work carried out is focused on the exploration of processes occurring in cement materials during sorption cycles by using Nuclear Magnetic Resonance (NMR) relaxometry. Long (months) and short (days-weeks) sorption cycles of cement materials were explored. The long cycle consists of around 6 months of drying and re-wetting cement samples of different sizes and water-to-cement (w/c) ratios in a homemade relative humidity (RH) chamber. Short cycles were performed by drying samples of different sizes and w/c ratios in the oven at 60 ˚C and re-wetting underwater. Different NMR techniques, such as one- and two-dimensional relaxometry and solid-signal analyses, were used to study the samples. Firstly, by the interpretation of quasi-continuous distributions of T2 relaxation time, we demonstrated that some reversible and irreversible changes concerning smaller porosity happened during the first sorption cycle. Secondly, using 2D NMR and a new 2D NMR inversion algorithm we showed preliminary results on the cement T1-T2 maps. Data obtained during sorption processes indicated possible water exchange between different pore populations inside the cement samples. Thirdly, the solid structure of cement samples was qualitatively investigated with T1 measurements and, as far as we know, for the first time interpreted with the Pake-Doublet theory. Changes in the solid structure were observed. Precisely variations of the amount of Ettringite during drying/wetting were proposed to take place. Finally, a work on NMR single-sided equipment design for in situ cement investigation was shown. The multi-cubic-blocks magnet structure design was performed using different specific CAD software, and the magnetic fields generated by RF coils of different geometries were investigated using a customized Matlab script. The single-sided NMR instrument equipped with the designed single-sided magnet and coil was built by the ERICA partner company MR Solutions (Abingdon, UK), and the preliminary results resultsated the correctness of the developed design.

Design, expression, and characterization of FimH antigen as single recombinant protein or exposed on nanoparticles

Uropathogenic Escherichia coli (UPEC) accounts for approximately 85% of all urinary tract infections (UTIs), causing a global economic burden. E. coli is one of the pathogens mentioned in the ESKAPEE list drafted by OMS, meaning that the increasing antibiotic resistance acquired by UPEC is and will be a serious health problem in the future. Amongst the immunogenic antigens exposed on the surface of UPEC, FimH represent a potential target for vaccine development, since it is involved in the early stages of infection. As already demonstrated, immunizations with FimH elicit functional antibodies that prevent UPEC infections even though the number of doses required to elicit a strong immune response is not optimal. In this work, we aimed to stabilize FimH as a soluble recombinant antigen exploiting the donor strand complementation mechanism by generating different chimeric constructs constituted by FimH and FimG donor strand. To explore the potential of self-assembling nanoparticles to display FimH through genetic fusion, different constructs have been computationally designed and produced. In this work a structure-based design, using available crystal structures of FimH and three different NPs was performed to generate different constructs with optimized properties. Despite the different conditions tested, all the constructs designed (single antigen or chimeric NPs), resulted to be un-soluble proteins in E. coli. To overcome this issue a mammalian expression system has been tested. Soluble antigen expression was achieved for all constructs tested in the culture supernatants. Three novel chimeric NPs have been characterized by transmission electron microscopy (TEM) confirming the presence of correctly assembled NPs displaying UPEC antigen. In vivo study has shown a higher immunogenicity of the E. coli antigen when displayed on NPs surface compared to the single recombinant antigen. The antibodies elicited by chimeric NPs showed a higher functionality in the inhibition of bacterial adhesion.

Design and characterization of polymorphs and co-crystals of organic molecular semiconductors

In the last decades, organic semiconductors have attracted attention due to their possible employment in solution-processed optoelectronic and electronic devices. One of the advantages of solution processing is the possibility to process into flexible substrates at low cost. Organic molecular materials tend to form polymorphs, which can exhibit very different properties. In most cases, the control of the crystal structure is decisive to maximize the performance of the final device. Although organic electronics have progressed a lot, n-type organic semiconductors still lag behind p-type, presenting challenges such as air instability and poor solubility. NDI derivatives are promising candidates for applications in organic electronics due to their characteristics. Recently, the structure-properties relationship and the polymorphism of these molecules have gained attention. In the first part of this thesis, NDI-C6 thermal behavior was extensively explored which revealed two different behaviors depending on the annealing process. This study allowed to define the stability ranking of the NDI-C6 bulk forms and to determine the crystal structure of Form γ at 54°C. Additionally, the polymorphic and thermal behavior of thin films of NDI-C6 was also explored. It was possible to isolate pure Form α, Form β, Form γ and a new metastable Form ε. It was also possible to determine the stability ranking of the phases in thin films. OFETs were fabricated having different polymorphs as active layer, unfortunately the performance was not ideal. During the second part of this thesis, core-chlorinated NDIs with fluoroalkyl chains were studied. Initially, the focus was on the polymorphism of CF3-NDI that revealed a solvate form with a very interesting molecular arrangement suggesting the possibility to form charge transfer co-crystals. In the last part of the thesis, the synthesis and characterization of CT co-crystal with different NDI derivatives, and acceptor and as donor BTBT and ditBu-BTBT were explored.

Study and characterization of polymorphs of BTBT derivatives and their application in organic electronics

The perquisites of organic semiconductors (OSCs) in the field of organic electronics have attracted much attention due to the advantages like cost-effectiveness, solution processibility, etc. A key property in OSCs is charge carrier mobility, which depends on molecular packing, as even the slightest changes in the packing of OSC can significantly impact the mobility. Organic molecules are constructed by weak interactions, which makes the OSCs prone to adopt multiple packing arrangements, thus giving rise to polymorphism. Therefore, polymorph screening in bulk and thin films is crucial for material development. This thesis aims to present a systematic study of polymorphism of [1]benzothieno[3,2-b]benzothiophene (BTBT) derivatives functionalized with different side chains. The role of peripheral side chains has been studied since they can promote different packing arrangements. The bulk polymorph screening of OSCs was approached with conventional solution mediated recrystallization experiments like evaporation, slurry maturation, anti-solvent precipitation, etc. Each of the polymorphs were inspected for their relative stability and the kinetics of transformation was evaluated. Polymorphism in thin films was also investigated for selected OSCs. Non-equilibrium methods like, thermal gradient and solution shearing were employed to examine the nucleation, crystal growth and morphology in controlled crystallization conditions. After careful analysis of crystal phases in bulk and thin films, OFETs have been fabricated by optimizing the manufacturing conditions and the hole mobility values were extracted. The charge transport property of the OSCs tested for OFETs was supported by the ionization potential and transfer integrals calculation. An attempt to correlate the solid-state structure to electronic properties was carried out. For some of the molecules, mechanical properties have been also investigated, as the response to mechanical stress is highly susceptible to packing arrangements and the intermolecular interaction energy contributions. Additionally, collaborative research was carried out by solving and analysing the crystal structures of six oligorylene molecules.