Structural and optical properties of Al1-xInxN epilayers on GaN template grown by metalorganic chemical vapor deposition

This paper reports that Al1-xInxN epilayers were grown on GaN template by metalorganic chemical vapor deposition with an In content of 7%-20%. X-ray diffraction results indicate that all these Al1-xInxN epilayers have a relatively low density of threading dislocations. Rutherford backscattering/channeling measurements provide the exact compositional information and show that a gradual variation in composition of the Al1-xInxN epilayer happens along the growth direction. The experimental results of optical reflection clearly show the bandgap energies of Al1-xInxN epilayers. A bowing parameter of 6.5 eV is obtained from the compositional dependence of the energy gap. The cathodoluminescence peak energy of the Al1-xInxN epilayer is much lower than its bandgap, indicating a relatively large Stokes shift in the Al1-xInxN sample.

Fabrication and Characterization of High Power InGaN Blue-Violet Lasers with an Array Structure

InGaN/GaN multi-quantum-well-structure laser diodes with an array structure are successfully fabricated on sapphire substrates. The laser diode consists of four emitter stripes which share common electrodes on one laser chip. An 800-mu m-long cavity is formed by cleaving the substrate along the < 1 (1) over bar 00 >. orientation using laser scriber. The threshold current and voltage of the laser array diode are 2A and 10.5 V, respectively. A light output peak power of 12W under pulsed current injection at room temperature is achieved. We simulate the electric properties of GaN based laser diode in a co-planar structure and the results show that minimizing the difference of distances between the different ridges and the n-electrode and increasing the electrical conductivity of the n-type GaN are two effective ways to improve the uniformity of carrier distribution in emitter stripes. Two pairs of emitters on a chip are arranged to be located near the two n-electrode pads on the left and right sides, and the four stripe emitters can laser together. The laser diode shows two sharp peaks of light output at 408 and 409 nm above the threshold current. The full widths at half maximum for the parallel and perpendicular far field patterns are 8 degrees and 32 degrees, respectively.

Role of Ga vacancies in enhancing the leakage current of GaN Schottky barrier ultraviolet photodetectors

The leakage current of GaN Schottky barrier ultraviolet photodetectors is investigated. It is found that the photodetectors adopting undoped GaN instead of lightly Si-doped GaN as an active layer show a much lower leakage current even when they have a higher dislocation density. It is also found that the density of Ga vacancies in undoped GaN is much lower than in Si-doped GaN. The Ga vacancies may enhance tunneling and reduce effective Schottky barrier height, leading to an increase of leakage current. It suggests that when undoped GaN is used as the active layer, it is necessary to reduce the leakage current of GaN Schottky barrier ultraviolet photodetector.

Cathodoluminescence study on in composition inhomogeneity of thick InGaN layer

We have investigated the optical properties of thick InGaN film grown on GaN by cathodeluminescence (CL) spectroscopy. It is found that there is obvious In composition variation in both growth and lateral direction of InGaN film. The depth distribution of In composition is closely related to the strain relaxation process of InGaN film. Accompanied with the relaxation of compressive strain, the In composition of InGaN layer increases and the CL peak energy shifts towards red. Moreover, a rather apparent In composition fluctuation is found in the relaxed upper part of InGaN layer as confirmed by CL imaging.

Microstructure and strain analysis of GaN epitaxial films using in-plane grazing incidence x-ray diffraction

This paper investigates the major structural parameters, such as crystal quality and strain state of (001)-oriented GaN thin films grown on sapphire substrates by metalorganic chemical vapour deposition, using an in-plane grazing incidence x-ray diffraction technique. The results are analysed and compared with a complementary out-of-plane x-ray diffraction technique. The twist of the GaN mosaic structure is determined through the direct grazing incidence measurement of (100) reflection which agrees well with the result obtained by extrapolation method. The method for directly determining the in-plane lattice parameters of the GaN layers is also presented. Combined with the biaxial strain model, it derives the lattice parameters corresponding to fully relaxed GaN films. The GaN epilayers show an increasing residual compressive stress with increasing layer thickness when the two dimensional growth stage is established, reaching to a maximum level of -0.89 GPa.

Effects of GaN Capping on the Structural and the Optical Properties of InN Nanostructures Grown by Using MOCVD

InN nanostructures with and without GaN capping layers were grown by using metal-organic chemical vapor deposition. Morphological, structural, and optical properties were systematically studied by using atomic force microscopy, X-ray diffraction (XRD) and temperature-dependent photoluminescence (PL). XRD results show that an InGaN structure is formed for the sample with a GaN capping layer, which will reduce the quality and the IR PL emission of the InN. The lower emission peak at similar to 0.7 eV was theoretically fitted and assigned as the band edge emission of InN. Temperature-dependent PL shows a good quantum efficiency for the sample without a GaN capping layers; this corresponds to a lower density of dislocations and a small activation energy.

Effect of Interface Roughness and Dislocation Density on Electroluminescence Intensity of InGaN Multiple Quantum Wells

Effects of interface roughness and dislocation density on the electroluminescence (EL) intensity of InGaN multiple quantum wells (MQWs) are investigated. It is found that the EL intensity increases with the number of satellite peaks in the x-ray diffraction experiments of InGaN MQW samples. It is indicated that the rough interface will lead the reduction of EL intensity of InGaN MQW samples. It is also found that the EL intensity increases with the decrease of dislocation density which is characterized by the x-ray diffraction measurements. It is suggested that the EL intensity of InGaN MQWs can be improved by decreasing the interface roughness and dislocation density.

Cathodoluminescence study of GaN-based film structures

GaN films grown on sapphire substrate with an emphasis on epitaxial lateral overgrown (ELOG) layers with an array of rhombic shaped mask area as well as InGaN/GaN MQW laser diode layer structures were investigated by cathodoluminescence (CL) spectroscopy and CL imaging at room and low temperatures. The microscopic imaging with a high-spatial resolution clearly reveals the distribution of threading dislocations and point defects in ELOG GaN films. The secondary electron and CL data measured on cleaved faces of laser diodes are analyzed in consideration with luminescence mechanisms in semiconductor heterostructures and around the p - n junction, providing important information on the defects and carrier dynamics in laser diode devices.

Investigation of responsivity decreasing with rising bias voltage in a GaN Schottky barrier photodetector

The unexpected decrease in measured responsivity observed in a specific GaN Schottky barrier photodetector (PD) at high reverse bias voltage was investigated and explained. Device equivalent transforms and small signal analysis were performed to analyse the test circuit. On this basis, a model was built which explained the responsivity decrease quantitatively. After being revised by this model, responsivity curves varying with bias voltage turned out to be reasonable. It is proved that the decrease is related to the dynamic parallel resistance of the photodiode. The results indicate that with a GaN Schottky PD, the choice of load resistance is restricted according to the dynamic parallel resistance of the device to avoid responsivity decay at high bias voltage.

Photoelectric characteristics of metal/InGaN/GaN heterojunction structure

A heterojunction structure photodetector was fabricated by evaporating a semitransparent Ni/Au metal film oil the InGaN/GaN structure. The photocurrent (PC) spectra show that both the Schottky junction (NiAu/InGaN) and the InGaN/GaN isotype heterojunction contribute to the PC signal which suggests that two junctions are connected in series and result in a broader spectral response of the device. Secondary electron, cathodoluminescence and electron-beam-induced current images measured from the same area of the edge surface clearly reveal the profile of the layer structure and distribution of the built-in electric field around the two junctions. A band diagram of the device is drawn based oil the consideration of the polarization effect at the InGaN/GaN interface. The analysis is consistent with the physical mechanism of a tandem structure of two junctions connected in series.

Fabrication and optical characterization of GaN-based nanopillar light emitting diodes

InGaN/GaN-multiple-quantum-well-based light emitting diode ( LED) nanopillar arrays with a diameter of approximately 200nm and a height of 700nm are fabricated by inductively coupled plasma etching using Ni self-assembled nanodots as etching mask. In comparison to the as-grown LED sample an enhancement by a factor of four of photoluminescence ( PL) intensity is achieved after the fabrication of nanopillars, and a blue shift and a decrease of full width at half maximum of the PL peak are observed. The method of additional wet etching with different chemical solutions is used to remove the etch-induced damage. The result shows that the dilute HCl ( HCl:H2O=1:1) treatment is the most effective. The PL intensity of nanopillar LEDs after such a treatment is about 3.5 times stronger than that before treatment.

A GaN photodetector integrated structure for wavelength characterization of ultraviolet light

An interesting GaN photodetector structure, which can be used for characterizing the wavelength of incident ultraviolet light, is proposed. It is composed of two back-to-back integrated diodes, i.e. p-n and p-i-n GaN ultraviolet photodiodes with different spectral response. The wavelength of monochromatic ultraviolet light could be identified by measuring the photocurrent ratio value through a simple electronic circuit.

Investigation on the structural origin of n-type conductivity in InN films

This work presents a study of the correlation between the electrical properties and the structural defects in nominally undoped InN films. It is found that the density of edge-type threading dislocations (TDs) considerably affects the electron concentration and mobility in InN films. The Hall-effect measured electron concentration increases, while the Hall mobility decreases with the increase in the edge-type TD density. With the combination of secondary ion mass spectrometry and positron annihilation analysis, we suggest that donor-type point defects at the edge-type TD lines may serve as dominant donors in InN films and affect the carrier mobility.

Polymerization of ionic liquid-based microemulsions: A versatile method for the synthesis of polymer electrolytes

电子邮箱fyan@suda.edu.cn

The effect of growth temperature on structural quality of GaN/AlN quantum wells by metal-organic chemical vapour deposition

The effect of the growth temperature on the surface and interface quality for the GaN/AlN multiquantum well (MQW) layer grown by metal-organic vapour chemical deposition is investigated. The obtained GaN/AlN MQW structure is almost coherent to the underlying AlGaN layer at improved growth conditions. With a relatively low growth temperature, the GaN/AlN MQW growth rate increases, the surface roughness reduces considerably and no macro steps are observed, resulting in a better periodicity of MQW.