Acid-base, electron-donating and magnetic properties of Nd2O3 and its mixed oxides with alumina catalysts

The electron donor properties of Nd2O3 activated at 300, 500 and 800°C were investigated through studies on the adsorption of electron acceptors of various electron affinities - 7, 7, 8,8-tetracyanoquinodimethane (2.84 eV). 2, 3, 5, 6-tetrachloro-l , 4-benzoquinone (2.40 eV). p-dinitrobenzene (1.77 eV), and m-dinitrobenzene (1.26 eV) in solvents acetonitrile and 1, 4-dioxan. The extent of electron transfer during adsorption has been found from magnetic measurements and electronic spectral data. The corresponding data on mixed oxides of neodymium and aluminium are reported for various. compositions. The acid-base properties of catalysts were also determined using a set of Hammett indicators.

Surface acidity/basicity of yttria and its mixed oxides with alumina catalysts

Acid/base strength distribution of Y2O3 and its mixed oxides with alumina catalysts are measured on Hammett acidity function scale and expressed in terms of H0max value. Basicity of Y2O3 increases with increase in activation temperature and for mixed oxides the basicity increases with increase in concentration of Y2O3, in the catalyst.

Electron Donating Property and Catalytic Activity of Perovskite-type Mixed Oxides (ABO3 ) Consisting of Rare Earth and 3d Transition Metals

The catalytic activity of Perovskite-type mixed oxides (LaCo03 . PrCo03 and SmCo03 ) for the reduction of cyclohexanone to cyclohexanol with 2-propanol (Meerwein-Ponndorf-Verley reduction) has been studied. The data have been correlated with the surface electron donor properties of these mixed oxides.

Wet peroxide oxidation of phenol over mixed pillared montmorillonites

Wet peroxide oxidation (WPO) of phenol is an effective means for the production of diphenols, which are of great industrial importance. An added advantage of this method is the removal of phenol from wastewater effluents. Hydroxylation of phenol occurs efficiently over mixed iron aluminium pillared montmorillonites. An initial induction period is noticed in all cases. A thorough study on the reaction variables suggests free radical mechanism for the reaction.

Surface Electron Donor Properties of Dy2O3,Y2O3 and Their Mixed Oxides with Alumina Catalyst

The limit of electron transfer in electron affinity from the oxide surface to the electron acceptor (EA) are reported from the adsorption of EA on DY203, mixed oxides of DY203 with alumina and mixed oxides of Y203 with y-alumina. The extent of electron transfer is understood from magnetic measurements.

Catalytic activity of some of the perovskite-type mixed oxides (ABO3) consisting of rare earth and 3d transition metals

The catalytic activity of some of the ABO3 (A = La, Pr and Sm, B= Cr, Mn, Fe, Co and Ni) perovskite-type oxides for the liquid phase reduction of ketone and oxidation of alcohol in 2-propanol medium has been studied. The data have been correlated with the surface electron donor properties of these oxides. The surface electron donor properties have been determined from the adsorption of electron acceptors of varying electron affinities on the oxide surface.

Surface acidity/basicity and catalytic activity of mixed oxides of Zr, La and Al

The surface acidity/basicity of binary oxides of Zr and La and the ternary oxides of Zr, La and Al are reported. The data have been correlated with their catalytic activity towards liquid phase reduction of cyclohexanone.

Acidity, basicity and catalytic activity of La−Zn mixed oxides

Surface acidity/Basicity of mixed oxides of La and Zn activated at three different temperatures were determined. The data have been correlated with the catalytic activity for liquid phase reduction of cyclohexanone in isopropanol.

Catalysis by Transition Metal Modified Ceria and Ceria-Zirconia Mixed Oxides Prepared via Sol-Gel Route

The aim of catalysis research is to apply the catalyst successfully in economically important reactions in an environmentally friendly way. The present work focuses on the modification of structural and surface properties of ceria and ceria-zirconia catalysts by the incorporation of transition metals. The applications of these catalysts in industrially important reactions like ethylbenzene oxidation, alkylation of aromatics are also investigated.Sol-gel method is effective for the preparation of transition metal modified ceria and ceria-zirconia mixed oxide since it produces catalyst with highly dispersed incorporated metal. Unlike that of impregnation method plugging of pores is not prominent for sol-gel derived catalyst materials. This prevents loss of surface area on metal modification as evident for BET surface area measurements.The powder X-ray diffraction analysis confirms the cubic structure of transition metal modified ceria and ceria-zirconia catalysts. The thermal stability is evident from TGA/DTA analysis. DR UV-vis spectra provide information on the coordination environment of the incorporated metal. EPR analysis ofCr, Mn and Cu modified ceria and a ceria-zirconia catalyst reveals the presence of different oxidation states of incorporated metal.Temperature programmed desorption of ammonia and thermogravimetric desorption of 2,6-dimethyl pyridine confirms the enhancement of acidity on metal incorporation. High a-methyl styrene selectivity in cumene cracking reaction implies the presence of comparatively more number of Lewis acid sites with some amount of Bronsted acid sites. The formation of cyclohexanone during cyclohexanol decomposition confirms the presence of basic sites on the catalyst surface.Mn and Cr modified catalysts show better activity towards ethylbenzene oxidation. A redox mechanism through oxometal pathway is suggested.All the catalysts were found to be active towards benzylation of toluene and a-xylene. The selectivity towards monoalkylated products remains almost 100%. The catalytic activity is correlated with the Lewis acidity of the prepared systems.The activity of the catalysts towards methylation of phenols depends on the strength acid sites as well as the redox properties of the catalysts. A strong dependence of methylation activity on the total acidity is illustrated.

Impact of zinc substitution on the structural and magnetic properties of chemically derived nanosized manganese zinc mixed ferrites

Mn1-xZnxFe2O4 nanoparticles (x=0-1) were synthesized by wet chemical co-precipitation techniques. X-ray diffraction, transmission electron microscopy and high-resolution transmission electron microscopy were effectively utilized to investigate the different structural parameters. The elemental analysis was conducted using energy-dispersive spectrum and inductively coupled plasma analysis. The magnetic properties such as magnetization and coercivity were measured using vibrating sample magnetometer. The observed magnetization values of the nanoparticles were found to be lower compared to the bulk counterpart. The magnetization showed a gradual decrease with zinc substitution except for a small increase from x=0.2 to 0.3. The Curie temperature was found to be enhanced in the case of ferrites in the nanoregime. The variation in lattice constant, reduced magnetization values, variation of magnetization with zinc substitution, the presence of a net magnetic moment for the zinc ferrite and the enhancement in Curie temperature in Mn1-xZnxFe2O4 all provide evidence to the existence of a metastable cation distribution together with possible surface effects at the nanoregime.

Thermal transport properties of selected ferroelectrics, mixed valance perovskites and dielectric ceramics using photopyroelectric technique

Photothermal spectroscopy is a group of high sensitivity methods used to measure optical absorption and thermal characteristics of a sample.The basis of photothermal spectroscopy is a photo-induced change in the thermal state of the sample.Light energy absorbed and not lost by subsequent emission results in sample heating.This heating results in a temperature change as well as changes in thermodynamic parameters of the sample which are related to temperature.Measurements of the temperature,pressure,or density changes that occur due to optical absorption are ultimately the basis for the photothermal spectroscopic methods.This is a more direct measure of optical absorption than optical transmission based spectroscopies.Sample heating is a direct consequence of optical absorption and so photothermal spectroscopy signals are directly dependent on light absorption.Scattering and reflection losses do not produce photothermal signals.Subsequently,photothermal spectroscopy more accurately measures optical absorption in scattering solutions,in solids,and at interfaces.This aspect makes it particularly attractive for application to surface and solid absorption studies,and studies in scattering media.

Structure and energetics of mixed 4He-3He drops

Using a finite-range density functional, we have investigated the energetics and structural features of mixed helium clusters. The possibility of doping the cluster with a molecule of sulfur hexafluoride is also considered. It is seen that the repulsion introduced by the impurity strongly modifies the properties of the smallest drops. Although only a qualitative comparison is possible, the gross features displayed by our calculations are in agreement with recent experimental findings.

Fabrication And Parametric Measurements Of N2 Laser Pumped Dye Laser And Its Application To Energy Transfer Studies In Mixed Dyes

Eventhough a large number of schemes have been proposed and develoned for N9 laser ouined dye lasers the relatively low efficiency compelled the scientists to device new methods to improve the system efficiencs. Energy transfer mechanism has been shown to he a convenien tool for the enhancement of efficiency of dye lasers. Th p resent work covers a detailed study of the performance characteristics of a N2 laser pumped dye laser in the con— ventional mode and also, when pumped by the energy transfer mechanism. For .th.e present investigations a dye laser pumped by a'N2 laser (A4200 kw peak power) was fabricated. The grating at grazing incidence was used as the beam expanding device; A t its best performance the system was giving an output peak power of l5 kW for a 5 X lC"3H/l Rh—€ solution in methanol. T he conversion efficiency was 7.5; The output beam was having 3 divergence of 2 mrad and bandwidth o.9 A. Suitable modifications were suggested for obtaining better conversion efficiency and bandwidth.

Studies on the catalysis by sulfated mixed oxides of tin with some rare earth elements

A comparative study of acid-base properties and catalytic activity of Sn-La and Sn-Sm mixed oxides and their corresponding sulfate modified analogues are reported in this thesis. The catalytic activity and product selectivity in the decomposition of alcohols are correlated with the acid-base and redox properties of the catalyst systems under study The effect of catalyst preparation, pretreatment and various reaction parameters on the catalytic activity of sulfate modified oxides is investigated in the oxidative dehydrogenation reactions The experimental conditions are optimised to synthesise industrially important organic chemicals viz. 2,6 xylenol, o-cresol, N-methylanilne and N,N-dimethylaniline employing the mixed oxide systems. The effect of sulfate treatment on the catalytic activity of these systems in the alkylation reactions of phenol, anisole and aniline is also investigated and the merits and demerits of sulfate treatment are highlighted.

Crystal Structures and Spectral Investigation of Aroylhydrazones and their Mixed Ligand Metal Chelates

Supra molecular architectures of coordination complexes of liydrazones through non covalent interactions have been explored. Molecular self—assernbly driven by weak interactions such as hydrogen— bonding, K '”T[, C-1-I‘ "TE, van der Waals interactions, and so forth are currently of tremendous research interest in the fields of molecule based materials. The directional properties of the hydrogembonding interaction associate discrete molecules into aggregate structures that are sufficiently stable to be considered as independent chemical species. Chemistry can borrow nature’s strategy to utilize hydrogen-bonding as Well as other noncovalent interactions as found in secondary and tertiary structures of proteins such as the double helix folding of DNA, hydrophobic selflorganization of phospholipids in cell membrane etc. In supramolecular chemistry hydrogen bonding plays an important role in forming a variety of architectures. Thus, the wise modulation and tuning of the complementary sites responsible for hydrogen—bond formation have led to its application in supramolecular electronics, host-guest chemistry, self-assembly of molecular capsules, nanotubes etc. The work presented in this thesis describes the synthesis and characterization of metal complexes derived from some substituted aroylhydrazones. The thesis is divided into seven chapters.