Study on the structure change and oxygen vacation shift for Ce1-xSmxO2-y solid solution

A series of solid electrolytes Ce1-xSmxO2-y (x=0similar to0.6) were prepared by sol-gel method. XRD measurement showed that single-phase solid solution was formed in all investigated ranges at 160 degreesC, which is a significantly lower synthesis temperature compared to traditional solid state reaction. High temperature X-ray, ESR, and Raman scattering were used to characterize the samples. ESR measurement showed that ESR with sample irradiated by high-energy particle is an effective way to study the defect structure. These changes in the Raman spectrum are attributed to O vacancies, which are introduced into the lattice when tetravalent Ce4+ is substituted by trivalent Sm3+.

Isothermal and nonisothermal melt-crystallization kinetics of syndiotactic polystyrene

Analyses of the isothermal and nonisothermal melt kinetics for syndiotactic polystyrene have been performed with differential scanning calorimetry, and several kinetic analyses have been used to describe the crystallization process. The regime II-->III transition, at a crystallization temperature of 239degrees, is found. The values of the nucleation parameter K-g for regimes II and III are estimated. The lateral-surface free energy, sigma = 3.24 erg cm(-2), the fold-surface free energy, sigma(e) = 52.3 +/- 4.2 erg cm(-2), and the average work of chain folding, q = 4.49 +/- 0.38 kcal/mol, are determined with the (040) plane assumed to be the growth plane. The observed crystallization characteristics of syndiotactic polystyrene are compared with those of isotactic polystyrene. The activation energies of isothermal and nonisothermal melt crystallization are determined to be DeltaE = -830.7 kJ/mol and DeltaE = -315.9 kJ/mol, respectively.